DOE OSTI2020

Imaging hole-density inhomogeneity in arsenic-doped CdTe thin films by scanning capacitance microscopy

We report nanometer-scale hole-density imaging in As-doped CdTe films by scanning capacitance microscopy (SCM). The hole-density profiling is validated by contrasting a CdTe cross-section sample made by molecular-beam epitaxy with systematically increased As doping in a staircase pattern over the range of 10 15 -10 18 /cm 3 within a single film. In polycrystalline films, the carrier distribution is significantly nonuniform, with inhomogeneity ranging from several hundred nm to several um and hole density varying by one order of magnitude (low 10^16 to low 10 17 /cm 3 ). This nonuniformity is distributed randomly, independent of the grain structure and grain boundaries (GBs). Kelvin probe force microscopy (KPFM) maps the surface potential and is correlated to cathodoluminescence (CL) and SCM by imaging over identical areas. Higher potential and lower CL intensity are found on GBs but not by SCM contrast; this indicates positive GB charging and recombination, but not GB-specific hole-density changes. The overall KPFM potential image is in rough agreement with the SCM carrier distribution and indicates band-edge potential fluctuations. Nonuniform carrier concentration, potential fluctuations, and defect recombination can all cause voltage and performance loss in As-doped CdTe solar technology.

14 SOLAR ENERGY↗

DOE OSTI2020

Thin-Film Solar Cells with 19% Efficiency by Thermal Evaporation of CdSe and CdTe

CdTe-based solar cells exhibiting 19% power conversion efficiency were produced using widely available thermal evaporation deposition of the absorber layers on SnO2-coated glass with or without a transparent MgZnO buffer layer. Evaporating CdSe and CdTe sequentially by thermal evaporation and subsequent CdCl2 annealing establishes efffective CdSeTe band grading as well as dense, large-grain films. These results show that high-performance II-VI photovoltaics can be made by inexpensive, commercially available evaporation systems without the need to build customized equipment, enabling CdTe photovoltaics research and manufacturing to be more accessible to the broader photovoltaics community.

14 SOLAR ENERGY↗

DOE OSTI2018

Interface Engineering for 25% CdTe Solar Cells

Buffer layers, such as CdS and Mg x Zn 1-x O (MZO), are critical for CdTe and other thin film polycrystalline solar cells. A ternary compound, such as MZO, allows for interface engineering by adjusting composition, bandgap, and doping to manipulate barriers and recombination to enhance thin film efficiencies toward 25%. Here, theoretical studies demonstrate the enormous impact of front interface offset and emitter doping have on device performance. The results reveal it is possible to achieve 25% device efficiency with open-circuit voltage >1 V, even for 10 5 cm/s recombination velocity, provided the interface offsets and doping are properly engineered.

14 SOLAR ENERGY↗