A Mechanism for Carbon Depletion at Bondline of High-Frequency Electric-Resistance-Welded X70 Pipeline Steel
The bondline of electric-resistance-welded (ERW) linepipe steel, often etched white (i.e., ferrite) in optical microscopy, is generally believed to be carbon depleted. The mechanism for the carbon depletion, however, is not fully understood by researchers. To this end, here we used atom probe tomography (APT) to measure elemental segregation of the as-welded and post-weld heat-treated bondline regions of X70 linepipe welds. The thin vertical features at the bondline in the as-welded condition were identified as carbon-rich martensite-austenite (M-A) constituents, and the majority ferrite phase in the bondline was identified as carbon-depleted ferrite. Following the post-weld normalization, all alloying elements, except Nb and Mo, are homogenized across the bondline and heat-affected zone. The carbon depletion in the ERW bondline was accurately measured. A new mechanism for carbon depletion has been proposed using Scheil calculations of elemental partitioning during weld formation. Segregation of elements in the heat-affected zone was shown to follow the negligible partitioning local equilibrium (NPLE) kinetics for bainite transformation.