H3O Radical in Proton-Exchange Membrane Fuel Cells and Its Role in Membrane Degradation
Based on previous experimental evidence on isotopic substitution, we postulate that the hydronium radical (H3O·) might be present in PEMFCs. Our ab initio modeling indicates that this radical can be stabilized by the sulfonic anion on the polymer sidechain, leading to a greatly reduced reaction barrier in the t-F degradation reaction with the assistance of explicit water by undergoing a sidechain conformational change. To our knowledge, this is the first evidence that H3O· could be present in electrochemical devices with both experimental and theoretical support.
fuel cell membrane degradation↗
Editors’ Choice—Necessity to Avoid Titanium Oxide as Electrocatalyst Support in PEM Fuel Cells: A Membrane Durability Study
Pt/TiO 2 as electrocatalyst was found to significantly increase the rate of the membrane chemical degradation in a polymer electrolyte membrane (PEM) fuel cell. The increased degradation was proved to be due to TiO x (TiO 2 or Ti 4 O 7 ), which is widely recognized as a promising corrosion-resistant electrocatalyst support. The membrane degradation (thinning) appears to be preferentially in the side facing anode electrode. Migrated Ti species as a result of TiO x dissolution during fuel cell operation in an acidic environment was quantified by electron probe microanalysis (EPMA). Total fluorine inventory loss of the membrane strongly depends on the quantity of migrated Ti species (likely Ti 3+ and/or Ti 4+ ). The membrane chemical degradation induced by TiO x is proposed to be due to dissolved ionic Ti species reacting with H 2 O 2 through a Fenton reaction. TiO x is determined to be inviable as electrocatalyst support for PEM fuel cells, and future research is suggested to be directed toward alternative oxides with similar corrosion-resistance.