Electrical Conductivity, Relaxation and the Glass Transition: A New Look at a Familiar Phenomenon

Annealed samples from a single melt of a 10 mol% K2O-90SiO2 glass were reheated to temperatures ranging from 450 to 800 C, held isothermally for 20 min, and then quenched in either air or a silicon oil bath. The complex impedance of both the annealed and quenched samples was measured as a function of temperature from 120 to 250 C using ac impedance spectroscopy from 1 Hz to 1 MHz. The dc conductivity, sigma(sub dc), was measured from the low frequency intercept of depressed semicircle fits to the complex impedance data. When the sigma(sub dc) at 150 C was plotted against soak temperature, the results fell into three separate regions that are explained in terms of the glass structural relaxation time, tau(sub S). This sigma(sub dc) plot provides a new way to look the glass transition range, Delta T(sub r). In addition, sigma(sub dc) was measured for different soak times at 550 C, from which an average relaxation time of 7.3 min was calculated. It was found that the size and position of the Delta T(sub r) is controlled by both the soak time and cooling rate.

Angel, Paul W.↗

NASA NTRS1993

Thermal history effects on electrical relaxation and conductivity for potassium silicate glass with low alkali concentrations

Electrical response measurements from 10 Hz to 100 kHz between 120 and 540 C were made on potassium-silicate glasses with alkali oxide contents of 2, 3, 5 and 10 mol percent. Low alkali content glasses were chosen in order to try to reduce the Coulombic interactions between alkali ions to the point that frozen structural effects from the glass could be observed. Conductivity and electrical relaxation responses for both annealed and quenched glasses of the same composition were compared. Lower DC conductivity (sigma(sub DC)) activation energies were measured for the quenched compared to the annealed glasses. The two glasses with the lowest alkali contents exhibited a non-Arrhenius concave up curvature in the log(sigma(sub DC)) against 1/T plots, which decreased upon quenching. A sharp decrease in sigma(sub DC) was observed for glasses containing K2O concentrations of 5 mol percent or less. The log modulus loss peak (M'') maximum frequency plots against 1/T all showed Arrhenius behavior for both annealed and quenched samples. The activation energies for these plots closely agreed with the sigma(sub DC) activation energies. A sharp increase in activation energy was observed for both series as the potassium oxide concentration decreased. Changes in the electrical response are attributed to structural effects due to different alkali concentrations. Differences between the annealed and quenched response are linked to a change in the distribution of activation energies (DAE).

Angel, Paul W.↗

NASA NTRS1991

Oxygen tracer diffusion in single-crystal alumina

Oxygen tracer diffusion coefficients are determined in single-crystal alumina samples with differing dopant levels using the gas-exchange technique. The diffusion direction is parallel to the c-axis and the ambient PO2 is 1 atm (100,000 Pa) for all experiments except a single run with a low PO2, approximately 10 to the -15th atm (10 to the -10th Pa) produced by a CO/CO2 mixture. The diffusion is insensitive to both impurities and ambient PO2. The insensitivities are discussed in terms of point-defect clustering. Prior tracer studies are compared and discussed.

Cawley, James D.↗