Corrao, Adam A.

Publications and source records attributed to Corrao, Adam A..

12 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2023

Salt-Mediated Coarsening in Conversion-Reaction-Synthesized Nanoporous Metals and Nanocomposites Resolved through In Situ Synchrotron Diffraction Studies

High-energy synchrotron X-rays were used to probe the structural and microstructural evolution in Fe, Co, and Cu nanoporous metals (NPMs) and metal/salt nanocomposites (NCs) produced by recently developed conversion reaction synthesis (CRS) methods. Microstructure analysis of as-synthesized samples via whole pattern fitting showed that the NPMs exhibit domain sizes that increase as Co < Fe < Cu, with both Fe and Co having crystallite sizes below 3.0 nm. The as-synthesized metal/salt NCs had similar metal sizes, and additionally, the salt in the composite had unusually large lattice microstrain whose origin is attributed to chemical substitution of metal ions into the salt (e.g., Li $1–3x$ Fe $x$ Cl for Fe 3+ ). When thermal annealing is used to modify crystallite size, pore collapse often occurs in NPMs but NCs can be effectively tuned without this problem. While the NC coarsening occurs slowly at low temperatures, it was found that there is a drastic acceleration of the reaction rate at a specific onset temperature that results in the crystallite size increasing by an order of magnitude in about a minute. Curiously, there was no evidence in the diffraction data for salt melting at this onset temperature. However, there was a sharp reduction in the salt chemical lattice strain at the onset temperature, indicating that rapid metal coarsening is facilitated by the salt. Importantly, this behavior indicates an unexpectedly coupled reaction mechanism by which the metal ions needed for grain growth are supplied by the salt in a rate-limiting fashion.

77 NANOSCIENCE AND NANOTECHNOLOGY↗
DOE OSTI2023

Thermodynamic and Kinetic Barriers Limiting Solid-State Reactions Resolved through In Situ Synchrotron Studies of Lithium Halide Salts

Although halide salts such as LiCl and LiBr are routinely used as a source of Li ions during ion exchange reactions, a detailed understanding of the processes controlling the rates of these reactions is presently lacking. Recently, it has been discovered that the rate limiting barriers for ion exchange are commonly associated with these salts rather than the ceramic target of ion exchange, making it important to quantitatively understand of salt processes. Here it is demonstrated that in situ synchrotron studies of ion exchange reactions can be used to precisely quantify the thermodynamic activation energies associated with these solid state reactions in a manner that can be directly compared with predictions from density functional theory (DFT). While the temperature dependence of the LiCl reaction rate is found to be set by a barrier associated with ion hopping, it was discovered that for LiBr it is also affected by the defect formation energy – an energy found to be substantially lower than predicted by DFT. Furthermore, it is shown that when reaction rates for different relative amounts of reactants are varied, it is possible to identify the rate-limiting reagent and to elucidate an overall scaling relationship that controls the concentration-dependence of the reaction rate. Also, it is demonstrated that global fits across doped and undoped salts can be used to probe both intrinsic and extrinsic vacancy concentrations. This improved understanding of ion exchange mechanisms can be used to accelerate ion exchange reaction rates by orders of magnitude. In conclusion, the techniques demonstrated here can be broadly applied to probe the kinetics and thermodynamics of solid state reactions.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Selectivity in Yttrium Manganese Oxide Synthesis via Local Chemical Potentials in Hyperdimensional Phase Space

In sharp contrast to molecular synthesis, materials synthesis is generally presumed to lack selectivity. The few known methods of designing selectivity in solid-state reactions have limited scope, such as topotactic reactions or strain stabilization. This contribution describes a general approach for searching large chemical spaces to identify selective reactions. This novel approach explains the ability of a nominally “innocent” Na 2 CO 3 precursor to enable the metathesis synthesis of single-phase Y 2 Mn 2 O 7 : an outcome that was previously only accomplished at extreme pressures and which cannot be achieved with closely related precursors of Li 2 CO 3 and K 2 CO 3 under identical conditions. By calculating the required change in chemical potential across all possible reactant-product interfaces in an expanded chemical space including Y, Mn, O, alkali metals, and halogens, using thermodynamic parameters obtained from density functional theory calculations, we identify reactions that minimize the thermodynamic competition from intermediates. In this manner, only the Na-based intermediates minimize the distance in the hyperdimensional chemical potential space to Y 2 Mn 2 O 7 , thus providing selective access to a phase which was previously thought to be metastable. Experimental evidence validating this mechanism for pathway-dependent selectivity is provided by intermediates identified from in situ synchrotron-based crystallographic analysis. Finally, this approach of calculating chemical potential distances in hyperdimensional compositional spaces provides a general method for designing selective solid-state syntheses that will be useful for gaining access to metastable phases and for identifying reaction pathways that can reduce the synthesis temperature, and cost, of technological materials.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Sample environment effects on synchrotron-measured temperature profiles in an approximant of optical floating zone crystal growth

Even though the growth of crystals using optical floating zone furnaces has had an immense scientific impact, the implementation of this method remains more of an art than a science due to the difficulty of obtaining quantitative information about the sample thermal profile during crystal growth. Building on recent work demonstrating that in situ synchrotron studies can be used to map sample rod temperatures during heating, investigations were carried out to better understand how the sample environment affects the sample temperature profile. Through a combination of experimental studies and modeling efforts, it is shown that the environment in the furnace can strongly influence the sample temperature at the lamp focus, the steepness of the vertical temperature gradient, and the timescale required for sample heating and cooling - effects which can combine to produce a strong history-dependence to sample temperature profiles. It is demonstrated that the furnace effects can be effectively captured in thermal models, allowing both the steady-state and time-dependent behavior of the sample to be accurately reproduced with predictive models, and providing a launching point for improved furnace designs that can more readily deliver desired thermal profiles.

36 MATERIALS SCIENCE↗
DOE OSTI2020

In situ temperature profile measurements with high-energy X-rays as a probe of optical floating zone crystal growth environment

The ability of optical floating zone (OFZ) furnaces to rapidly produce large single crystals of complex emerging materials has had a transformative effect on many scientific fields that require samples of this type. However, the crystal growth process within the OFZ furnace is not well understood owing to the challenges involved in monitoring the high-temperature crystal growth process. Novel beamline-compatible optical furnaces that approximate the inhomogeneous growth environment within an OFZ furnace have been fabricated and tested in high-energy synchrotron beamlines. In this paper, it is demonstrated that temperature profiles can be effectively extracted from powder diffraction data collected on polycrystalline ceramic rods heated at their tip. Furthermore, these measured temperature profiles can be accurately reproduced using a heat-transfer model that accounts for solid-state thermal conduction, partial sample lamp power absorption, convective air cooling and radiative cooling, allowing key thermal parameters such as thermal conductivity to be extracted from experimental data.

36 MATERIALS SCIENCE↗