Engineering topics
Publications and source records attributed to Cottle, David L.
Graphite Oxidation Activities to include introduction, rate determination, strength after oxidation, penetration depth analysis, strategic partnership projects, and summary and continuing work.
The purpose of this report is to present data collected in the Baseline Graphite Characterization Program, which is directly tasked with supporting the Idaho National Laboratory’s (INL’s) research and development efforts on the Advanced Reactor Technologies (ART) Program. This program populates a comprehensive database that reflects the baseline properties of nuclear-grade graphite regarding individual grade, billet, and position within individual billets. The physical- and mechanical-property information being collected will be transferred to the Nuclear Data Management and Analysis System (NDMAS), and that database will help populate the handbook of property data available to member nations of the Generation-IV International Forum. Transfer of these data from the applicable technical lead to the dissemination databases available to other end users requires a full review of the test procedures and data-collection efforts through an analysis of the multiple summary spreadsheets and values being collected. This report represents the analysis for NBG-17 Billet V104 and facilitates release of associated data to the NDMAS custodians. Millions of raw data points have been collected during testing and quantification analyses for these billets. The summary scalar property values and supplementary traceability data are collected into comprehensive spreadsheets. Data sets are composed of single billets of graphite for any given grade, organized by mechanical test-specimen type, and further subdivided into individual spreadsheet tabs according to the specific test or evaluation being performed. A direct analysis of properties was not conducted, and this report does not provide information on the validity or performance characteristics of the graphite itself. Rather, this report is intended as a verification of the completeness of actual data collected in accordance with PLN-3467, “Baseline Graphite Characterization Plan: Electromechanical Testing,” [1] and PLN-3348 “Graphite Mechanical Testing” [2] and their representation of the measurement and test results with sole regard to the graphite billets under evaluation.
This interim report documents preliminary results of the post-irradiation examination material property testing from the fourth advanced graphite creep (AGC), AGC 4, capsule specimens. This is the fourth of a series of six irradiation test trains planned as part of the AGC experiment to fully characterize the neutron irradiation effects and radiation creep behavior of current nuclear graphite grades to moderate dose levels (=7 dpa). The AGC 4 capsule was irradiated in the Idaho National Laboratory Advanced Test Reactor at a nominal temperature of 800°C and to a peak dose of 8 dpa. Half of the AGC-4 specimens were subjected to compressive stresses to induce irradiation creep. Post-irradiation testing and measurement results are reported with the exception of thermal testing, which is still in progress, and irradiation mechanical strength testing. Additionally, some specimens initially deemed too hot to be examined in the ART Graphite laboratory may still be measured. The data reported includes specimen dimensions for both stressed and unstressed specimens to establish the irradiation creep rates, mass and dimensional data necessary to derive density, elastic constants (Young?s modulus, shear modulus, and Poisson?s ratio) from ultrasonic time of flight velocity measurements, Young?s modulus from the fundamental frequency of vibration, and electrical resistivity. A more complete evaluation of trends in the material property changes, as well as irradiation-induced creep due to the irradiation environment and applied load on the specimens, will be discussed later in AGC 4 post-irradiation examination analysis reports.
This report documents results of the post-irradiation examination material property testing of the creep, control, and piggyback specimens from the irradiation creep capsule Advanced Graphite Creep (AGC)-2 are reported. This is the second of a series of six irradiation test trains planned as part of the AGC experiment to fully characterize the neutron irradiation effects and radiation creep behavior of current nuclear graphite grades. The AGC-2 capsule was irradiated in the Idaho National Laboratory Advanced Test Reactor at a nominal temperature of 600°C and to a peak dose of 5 dpa (displacements per atom). One half of the creep specimens were subjected to mechanical stresses (an applied stress of either 13.8, 17.2, or 20.7 MPa) to induce irradiation creep. All post-irradiation testing and measurement results are reported with the exception of the irradiation mechanical strength testing, which is the last destructive testing stage of the irradiation testing program. Material property tests were conducted on specimens from 15 nuclear graphite grades using a similar loading configuration as the first AGC capsule (AGC-1) to provide easy comparison between the two capsules. However, AGC-2 contained an increased number of specimens (i.e., 487 total specimens irradiated) and replaced specimens of the minor grade 2020 with the newer grade 2114. The data reported include specimen dimensions for both stressed and unstressed specimens to establish the irradiation creep rates, mass and volume data necessary to derive density, elastic constants (Young’s modulus, shear modulus, and Poisson’s ratio) from ultrasonic time of flight velocity measurements, Young’s modulus from the fundamental frequency of vibration, electrical resistivity, and thermal diffusivity and thermal expansion data from 100–500°C. No data outliers were determined after all measurements were completed. A brief statistical analysis was performed on the irradiated data and a limited comparison between pre- and post-irradiation properties is presented. A more complete evaluation of trends in the material property changes, as well as irradiation-induced creep due to irradiation, temperature, and applied load on specimens will be discussed in later AGC-2 post-irradiation examination analysis reports.
During their long service in commercial light water reactors, zirconium alloy cladding tubes are subject to oxidation and subsequent hydrogen pickup which can degrade the materials mechanical properties [1]. These degradations can lead to premature cladding ruptures during reactor power transients [2] as well as negatively impact the claddings post quench ductility following high temperature steam oxidation in thermal hydraulic transients [3]. Hydrogen has low solid solubility in zirconium and usually precipitates as brittle zirconium hydride platelets in the cladding metal matrix. Due to temperature driven diffusion (Soret effect) and the grain texture of stress relieved zirconium metal tubes, these hydrides precipitate with a circumferential orientation near the outer surface of the cladding tubes forming a hydride rim which can serve as a site for crack initiation during circumferential ‘hoop’ loading of the cladding [4rim formation][5]. In order to better understand the effect of hydride rims on the fracture behavior of stress relieved zirconium alloy cladding tubes a procedure to produce these rim-like structures is being developed at Idaho National Laboratory (INL).