Cottle, David L.

Publications and source records attributed to Cottle, David L..

Determining the oxidation behavior of matrix graphite

This work presents the oxidation behavior of matrix graphite in air. Matrix graphite, graphite powder/flakes bonded by a small amount of non-graphitic carbon, surrounds coated fuel particles in order to form cylindrical fuel compacts (in prismatic core designs) or spheres (in pebble-bed reactor designs). This work focuses on oxidation tests conducted on two matrix graphite materials, one provided by Kairos Power and the other A3 matrix graphite. Some of the tests followed American Society for Testing and Materials (ASTM) oxidation testing standards using a vertical furnace system and others were performed in a thermogravimetric analyzer (TGA). It was determined that, at temperatures of 450 °C–700 °C, the oxidation rate of the Kairos matrix graphite follows the Arrhenius equation. In comparison with A3 matrix graphite, the Kairos matrix graphite shows better oxidation resistance at high temperatures (≥550 °C), but also a higher oxidation rate at low temperatures. Both the A3 matrix graphite and the Kairos matrix graphite materials may experience preferential oxidation of the partially graphitized binder. An oxygen penetration gradient was also observed when using the three characterization methods (i.e., optical microscope, x-ray tomography [XCT], and density profile by the lathe) enlisted in this research. In conclusion, the oxygen penetration depth increases with decreasing isothermal oxidation temperature, while the center of the oxidized samples (10% weight loss) remains almost untouched even at 500 °C.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

High temperature annealing of irradiated nuclear grade graphite

Previous work has shown that the material properties of nuclear grade graphite are substantially affected by the atomic and microstructural changes that occur during neutron-irradiation. The parameters that play a role in these changes are irradiation dose, temperature, graphite composition and the initial microstructure of the graphite. Understanding the details of how these material changes occur and exactly what the changes consists of will enable the prediction of the material property changes as a function of these variables. Other work has shown these atomic level and microstructural changes can be healed or annealed out by raising the irradiated graphite above its irradiation temperature. Here in this work, experiments were carried out to investigate how the properties of irradiated graphite recover when heated. By showing property recovery as a function of annealing temperature or energy, insight is provided into the type of damage that occurred during neutron-irradiation. The data presented here shows recovery of thermal diffusivity, coefficient of thermal expansion, Young's modulus and electrical resistivity between annealing temperatures of 500 °C and 2380 °C. Graphite grades NBG-18, IG-110 and PCEA are considered that were both stressed and unstressed during irradiation.

36 MATERIALS SCIENCE↗

Thermocouple Testing in Support of the AGR-5/6/7 Experiment

This report documents thermocouple testing performed in IRC Lab C-15 over a period of seven years. This testing supported selection and characterization of the thermocouple set used in the AGR-5/6/7 experiment. The following summary was taken directly from the report. Temperature measurement is a challenging aspect of very high temperature irradiation experiments because commonly used high-temperature commercial thermocouples such as platinum-rhodium (Types S, R, and B) and tungsten-rhenium (Type C), suffer dramatic drift because of neutron-induced transmutation. As a result, these types of thermocouples, which are used routinely for industrial temperature measurements outside of reactors, are used only in very special circumstances for reactor experiments. Conversely, because of their low neutron cross-sections, Type N thermocouples are affected to only a limited extent by neutron irradiation. However, the use of these nickel-based thermocouples is limited when the temperature exceeds 1050°C due to drift arising from minor alloying elements migrating from the thermocouple's metal sheath to the thermoelements. This change in the composition of the thermo-elements results in significant decalibration of the signal. The issues described above were recognized during the early planning stages of the final AGR experiment (designated AGR-5/6/7), and a thermocouple furnace testing program was performed over a seven-year period (2014-2019, 2021) to first select and then characterize the best thermocouple set for the high temperature regions of the AGR-5/6/7 irradiation experiment. The calculated temperature range of the AGR-5/6/7 experiment was 600–1500°C. For temperatures below 1000°C standard Type N thermocouples were deemed adequate. The furnace testing campaign identified two thermocouple types suitable for measuring temperatures above 1000°C, a Mo/Nb thermocouple developed at INL called HTIR-TC, and a Type N thermocouple developed by Cambridge University (called herein Cambridge Type N), which featured a custom high nickel alloy sheath. One of the original goals of the furnace testing program was to identify a thermocouple capable of low drift operation near the peak temperature expected in AGR-5/6/7, i.e., about 1400°C. The HTIR-TC design appeared promising in this regard, however a manufacturing difficulty proved to be a barrier and instead the furnace testing focused on drift performance at 1250°C. The manufacturing difficulty was that the Nb sheaths of the HTIR-TCs experienced extreme embrittlement when heat treated at 1600°C or greater. Heat treatment is needed to stabilize the emf output of this TC type, and the higher the heat treatment temperature the higher the peak temperature of stable operation. Because of the sheath embrittlement the heat treatment temperature had to be lowered to 1450°C resulting in a stable operating temperature of about 1250°C. One of the successes of the furnace testing program was identification of a shortcoming in the heat treatment procedure that had been traditionally used in the production of HTIR-TCs. The shortcoming was that the entire heated length of the HTIR-TC sensor was not being heat treated, but rather only the part of the sensor expected to experience temperatures above 1000°C. The problem manifested itself when the thermocouples were removed from the heat treat furnace and placed in another furnace with a different geometry, their indicated temperatures would be widely scattered, but mostly in the negative direction. The solution was to heat treat the entire heated length of the sensor. Since the deepest immersion depth in the AGR-5/6/7 experiment was about 40 inches, a heat treatment length of 48 inches was used. After this change was implemented, thermocouples which were moved into a new environment with a different temperature profile (i.e., a different furnace), produced accurate temperature measurements. Although assembly of the AGR-5/6/7 experiment was completed in September of 2017 (and irradiation begun in 2018), furnace testing of thermocouples continued in 2018 and 2019. The main purpose of this testing was to establish very long-term drift characteristics of the HTIR and Cambridge Type N thermocouples installed in the experiment. Representative thermocouples from the same lots as those installed in the AGR-5/6/7 experiment were used. Additionally, thermocouples of different designs, (particularly variations on the HTIR-TC design) were "piggy-backed" on this testing program to provide insights for instrumenting future very high temperature irradiation experiments. This two-year testing program demonstrated that HTIR-TCs and Cambridge Type N TCs could operate at 1250°C for up to 10,000 hrs (and in some cases longer) while experiencing negative drifts on the order of 2-4°C/1000 hrs. This performance was considered acceptable given the extreme operating environment the sensors faced.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗