DOE OSTI2022

Impacts of Solvent Washing on the Electrochemical Remediation of Commercial End-of-Life Cathodes

Changes to surface structure and chemistry occurring throughout the functional lifetime of lithium-ion batteries (LIBs) may impact the effectiveness of end-of-life rejuvenation methods. Solvent washing prior to electrochemical relithiation is shown to both increase relithiation efficacy and beneficially alter the interfacial chemistry of heavily degraded industrial cathode material. Four common solvents (acetone, diethyl carbonate, isopropyl alcohol, propylene carbonate) are employed to investigate the role of varying physicochemical solvent properties on the mechanism of capacity recovery. Electrochemical (dQ/dV, EIS), structural (XRD), and chemical (SPME-GC-MS) analysis techniques are employed to comprehensively analyze solvent-cathode interactions. Highly nucleophilic solvents (acetone, DEC) are found to reduce cathode charge-transfer impedance and enable stable impedance growth throughout subsequent cycling. The use of nucleophilic solvents under mechanically aggressive washing conditions may also enable the reintroduction of bulk lattice oxygen, thereby restoring anionic redox capacity. Further, the four solvents are found to selectively remove a subset of surface species from the aged cathode material, including residual electrolyte, additives, and electrolyte-additive reaction products, which are qualitatively analyzed. Surface species removal by each solvent is correlated with the electrochemical performance of the correspondingly washed cathode, highlighting the importance of an optimized washing protocol to effective remediation in the context of direct LIB recycling. For the material under study, the use of a simple acetone washing protocol prior to electrochemical relithiation enables up to 174% capacity recovery relative to unwashed/relithiated black mass.

ADVANCED PROPULSION SYSTEMS↗

DOE OSTI2021

Understanding why poly(acrylic acid) works: decarbonylation and cross-linking provide an ionically conductive passivation layer in silicon anodes

Poly(acrylic acid) (PAA) is commonly used as a binder for fabricating silicon (Si) anode active materials in lithium-ion batteries due to its useful properties including high polar solvent solubility, good rheology, and strong adhesive properties. However, the role and evolution of PAA during electrode fabrication, cycling, and calendar aging are not well understood. In this work, we reveal the evolution of PAA during electrode curing and relate its chemical change to the final electrode properties and performance. These studies are made possible using two types of in situ attenuated total reflectance-infrared Fourier transform (ATR-FTIR) spectroscopy: thermal ATR-FTIR to probe the cross-linking reaction, and ATR-FTIR spectroelectrochemistry of three-dimensional composite electrodes, a unique technique developed herein that probes the solvation dynamics of lithium ions at the silicon anode interface under electrochemical polarization. Specifically, we show that PAA undergoes a thermally-mediated, cross-linking decarbonylation reaction to form an ether-based network polymer. To show the importance of the polyether moieties, we synthesize partially esterified PAA analogues that do not undergo this cross-linking decarbonylation reaction and correlate the degree of cross-linking to half-cell performance metrics. Finally, we unveil the mechanism of the polyether binder performance through in situ ATR-FTIR spectroelectrochemistry and show that PAA acts as an interfacial material that conducts lithium-ions, limits solvent molecule access to the Si surface, and stabilizes the electrode against parasitic lithium inventory loss at high state of charge for an extended period of time.

25 ENERGY STORAGE↗

DOE OSTI2020

SiO 2 Is Wasted Space in Single-Nanometer-Scale Silicon Nanoparticle-Based Composite Anodes for Li-Ion Electrochemical Energy Storage

The electrode processing conditions of silicon-based composite anodes play a pivotal role in the resulting interfacial chemical speciation and, thus, the electrochemical cycling behavior of the electrode. Systematically investigating how small chemical changes to the surface of the silicon nanoparticle (NP) affect larger, electrode-level properties is a strategy that will inform design principles to maximize electrode energy density and extend electrode lifetime. Here, we incorporate silicon nanoparticles (NPs) with an average diameter of 5.5 nm synthesized from the gas phase through a nonthermal plasma method into composite anode half-cell coin cells. We perform chemistry to functionalize the native hydride-terminated silicon NP surface with N-methylpyrrolidone (NMP) to improve slurry properties and reduce the silicon reactivity prior to composite electrode fabrication. We construct composite electrodes from these silicon NPs and observe an 86% capacity retention over 100 cycles at a rate of C/5, with an initial silicon specific capacity of 2600 mAh/g. We expose the same Si NPs to water that completely oxidizes these small-diameter NPs to SiO 2 and find that the SiO 2 NPs in the same electrode configuration exhibit no obvious lithium alloying capacity in the electrochemical potential range of lithium silicide alloy formation. As this result stands in contrast to existing literature, we provide a discussion on the origin of the discrepancies.

25 ENERGY STORAGE↗

DOE OSTI2020

Investigating the Chemical Reactivity of Lithium Silicate Model SEI Layers

Silicon anodes suffer from an unstable solid electrolyte interphase (SEI) layer that contributes to undesirable capacity fade with cycling. A key part to addressing this unstable SEI formation is to examine how certain components of the SEI react with the electrolyte over time. One SEI component that has not been thoroughly studied in the context of the chemical reactivity against the electrolyte is lithiated silicate. Four model silicate thin films with increasing lithium content were deposited by radio frequency (RF) magnetron sputtering to study how the lithiation of the native oxide on a silicon anode affects the chemical stability of the anode surface. SiO2, Li2Si2O5, Li2SiO3, and Li3SiOx films were exposed to 1.2 M LiPF6 in the 3:7 wt% ethylene carbonate/ethyl methyl carbonate (EC/EMC) electrolyte for periods of time that are representative of the amount of time it takes to undergo cell formations. Soaked samples were rinsed, dried, and characterized by a combination of attenuated total reflectance-infrared spectroscopy (ATR-IR), focused ion beam-secondary electron microscopy (FIB-SEM), and X-ray photoelectron spectroscopy (XPS) depth profiling. It was found that the rate of the decrease in film thickness of the silicates exposed to the electrolyte over time increases as a function of the lithium content in the thin film. This reaction involves HF etching and LiPF6 salt degradation leading to silicate loss and fluorination throughout the bulk. Understanding this chemical instability is critical to determining the overall mechanism of SEI degradation over time.

ADVANCED PROPULSION SYSTEMS,ENERGY STORAGE↗

DOE OSTI2020

Intrinsic Chemical Reactivity of Silicon Electrode Materials: Gas Evolution

In this work, we explore how the chemical reactivity toward an aprotic battery electrolyte changes as a function of lithium salt and silicon surface termination chemistry. The reactions are highly correlated, where one decomposition reaction leads to a subsequent decomposition reaction. We report the data show that the presence of silicon hydrides (SiH$_x$) promotes the formation of CO gas, while surface oxides SiO$_x$ drive the formation of CO 2 . The extent and rate of oxidation depend on the surface basicity of the SiO 2 surface species. The most acidic surfaces seem to hinder CO 2 generation but not the decomposition of the salt. Indeed, the presence of F-containing salts (LiPF 6 and LiTFSI) promotes the reactions between carbonate electrolyte and silicon surfaces. Surfaces with high Li content seem to be the most passivating to gassing reactions, pointing to a pathway to stabilize the interfaces during cell formation and assembly.

25 ENERGY STORAGE↗