DOE OSTI2020

Latent Tracks in Ion-Irradiated LiTaO 3 Crystals: Damage Morphology Characterization and Thermal Spike Analysis

Systematic research on the response of crystal materials to the deposition of irradiation energy to electrons and atomic nuclei has attracted considerable attention since it is fundamental to understanding the behavior of various materials in natural and manmade radiation environments. This work examines and compares track formation in LiTaO3 induced by separate and combined effects of electronic excitation and nuclear collision. Under 0.71–6.17 MeV/u ion irradiation with electronic energy loss ranging from 6.0 to 13.8 keV/nm, the track damage morphologies evolve from discontinuous to continuous cylindrical zone. Based on the irradiation energy deposited via electronic energy loss, the subsequently induced energy exchange and temperature evolution processes in electron and lattice subsystems are calculated through the inelastic thermal spike model, demonstrating the formation of track damage and relevant thresholds of lattice energy and temperature. Combined with a disorder accumulation model, the damage accumulation in LiTaO3 produced by nuclear energy loss is also experimentally determined. The damage characterizations and inelastic thermal spike calculations further demonstrate that compared to damage-free LiTaO3, nuclear-collision-damaged LiTaO3 presents a more intense thermal spike response to electronic energy loss owing to the decrease in thermal conductivity and increase in electron–phonon coupling, which further enhance track damage.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Irradiation-Induced Extremes Create Hierarchical Face-/Body-Centered-Cubic Phases in Nanostructured High Entropy Alloys

A nanoscale hierarchical dual-phase structure is reported to form in a nanocrystalline NiFeCoCrCu high-entropy-alloy (HEA) film via ion irradiation. Under the extreme energy deposition and consequent thermal energy dissipation induced by energetic particles, a fundamentally new phenomenon is revealed, in which the original single-phase face-centered-cubic (FCC) structure partially transforms into alternating nanometer layers of a body-centered-cubic (BCC) structure. The orientation relationship follows the Nishiyama–Wasser-man relationship, that is, (011) BCC || (1¯1¯1) FCC and [100] BCC || [11¯0] FCC . Simulation results indicate that Cr, as a BCC stabilizing element, exhibits a tendency to segregate to the stacking faults (SFs). Furthermore, the high densities of SFs and twin boundaries in each nanocrystalline grain serve to accelerate the nucleation and growth of the BCC phase during irradiation. By adjusting the irradiation parameters, desired thicknesses of the FCC and BCC phases in the laminates can be achieved. Finally, this work demonstrates the controlled formation of an attractive dual-phase nanolaminate structure under ion irradiation and provides a strategy for designing new derivate structures of HEAs.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Coupled effects of electronic and nuclear energy deposition on damage accumulation in ion-irradiated SiC

Coupling between electronic and nuclear energy dissipation in ion-irradiated, single crystal 4H-SiC has been investigated using Si, Ti, and Ni ions over a range of energies at 300 K, and irradiation damage accumulation is characterized using Rutherford backscattering spectroscopy in channeling geometry. The damage production rate from nuclear energy loss (S n ) is observed to decrease with increasing electronic energy loss (S e ) of the incident ions. A dynamic threshold (S e,th ) in electronic energy loss is determined for each ion species, which defines two regions: i) S e > S e,th , where electronic energy dissipation fully suppresses damage production due to nuclear energy loss along incident ion paths, and ii) S e < S e,th , where simultaneous damage recovery due to Se competes with damage production processes. Here, the electronic energy loss threshold (S e,th ) increases sublinearly with incident ion atomic number. Here, the assessment of S e,th and how it affects damage accumulation is important to advance the understanding of complex processes occurring under ion-solid interactions, as well as in the design of functional materials for opto-electronics and novel structural materials and devices tolerant to harsh thermal and radiation environments.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Indirectly probing the structural change in ion-irradiated Zr-Based metallic glasses from small scale mechanical tests

Ion irradiation was applied to tailor the structural heterogeneities in Zr-based metallic glasses at room temperature. Experimental methods of X-ray diffraction, nanoindentation, and micropillar compression were conducted to examine the irradiation effects on their structural and mechanical property changes. It is found that the irradiated materials retained amorphous structure after room-temperature Ni ion irradiation. The reduction of elastic modulus and hardness measured by nanoindentation indicated the irradiation-induced mechanical degradation. A unified statistic model was employed to quantitatively predict the density and strength of irradiation defects, although their specific structural and physical nature is not explicitly included in this model. The transition of non-intersecting shear bands to multiple intersecting shear bands was observed on compression tests of irradiated micropillars with the increase of irradiation dose. Furthermore, the analysis of the displacement excursion of micropillar compression tests indicated a different deformation mode from the unirradiated state. These results from nanoindentation pop-in and micro-pillar compression tests suggested that irradiation eventually leads to a new state with different types and characteristics of structural heterogeneities from violent displacement cascades and non-equilibrium energy deposition/dissipation processes, which also proves ion irradiation as an effective method to tune the structure and mechanical properties of metallic glasses.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Structural damage and phase stability of Al 0.3 CoCrFeNi high entropy alloy under high temperature ion irradiation

In this study, an initially single phase high entropy alloy (HEA) Al 0.3 CoCrFeNi was irradiated by 3 MeV Au ions to a fluence of 6 × 10 15 cm –2 (~31 dpa at damage peak) at four different temperatures ranging from 250 °C to 650 °C. Transmission electron microscopy (TEM) and Atom probe tomography (APT) were employed to study the evolution of structural damage and phase stability with irradiation temperature. Al 0.3 CoCrFeNi exhibited a similar evolution of irradiation-induced defects with temperature as compared with conventional FCC alloys. At 250 °C and 350 °C, most of the visible irradiation-induced defects were faulted 1/3$\langle{111}\rangle$ dislocation loops. As the irradiation temperature increased to 500 °C, perfect 1/2$\langle{110}\rangle$ dislocation loops were observed along with the faulted loops. At the highest irradiation temperature 650 °C, only dislocation lines and networks could be observed. Regarding phase stability, the 3 MeV Au irradiation was observed to suppress the precipitation of (Ni, Al)-enriched nano clusters and the L12 ordered structure at irradiation temperatures 250 °C to 500 °C whereas precipitation of the B2 ordered structure was accelerated at 650 °C. This resulted in qualitatively opposite precipitation behavior between the ion irradiated damage region and unirradiated region at 500 °C and 650 °C. The opposite phase stability of the ion-irradiated damage region and unirradiated region at different temperatures is attributed to the competing effects of ballistic dissolution vs irradiation enhanced diffusion on precipitation.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Effects of irradiation spectrum on the microstructural and mechanical properties of bulk metallic glasses

Zr 52.5 Cu 17.9 Ni 14.6 Al 10 Ti 5 (BAM-11) and Cu60Zr 20 Hf 10 Ti 10 bulk metallic glass (BMG) specimens were ion irradiated to characterize and compare their irradiation induced microstructural and mechanical property evolution. For the ion irradiations, samples of each BMG were exposed to 9 MeV Ni 3+ and 5.5 MeV C + ions to a midrange (~1.5 μm depth) dose of 0.5 displacements per atom (dpa) at temperatures ranging from room temperature to 360 °C in order to examine potential effects associated with low (5.5 MeV C) and high (9 MeV Ni) average primary knock on energies. BAM-11 BMG samples were also irradiated by neutrons (E > 0.1 MeV) at ~70 °C to a fluence of 1.4 × 10 20 n/cm 2 (dose of 0.1 dpa). Importantly, no pronounced irradiation spectrum effects were observed for the nanoindentation mechanical properties of the two BMGs following ion irradiation. However, significant softening was observed in the BAM-11 BMG sample irradiated by neutrons, while annealing of the unirradiated samples led to a marked increase in hardening. Finally, results of the nanoindentation experiments indicate that softening is caused by irradiation induced creation of free volume defects, while the hardening is caused by their annihilation.

36 MATERIALS SCIENCE↗