A quasi three dimensional finite element analysis was used to analyze the edge stress problem in four-ply, composite laminates. Convergence studies were made to explore the existence of stress singularities near the free edge. The existence of stress singularities at the intersection of the interface and the free edge is confirmed.
An improved procedure for the three dimensional finite element analysis of an angle ply laminate with a circular hole is discussed. The procecure exploits polar symmetry and is the basis for a new finite element computer code. For the broad class of laminates that contain angle plies, this code requires only one half as much computing capacity as conventional codes.
Graphite/epoxy laminates were tested under bolt-bearing loads for a range of bolt clampup torques and for several test conditions involving water. High clampup torque improved both the static strength and fatigue limit by about 100 percent compared to a simple pin-bearing case, which had no through-the-thickness constraint. The static strength improvement was explained in terms of failure modes. Bolt clampup also influenced the hole elongation that developed before failure. For both the static and fatigue tests, the hole elongations were much larger for the low-torque clampup. Tests in water degraded static bearing strength only slightly, but reduced the fatigue limit about 40 percent below that for tests conducted in air.
Stresses were calculated for finite-width orthotropic laminates with a circular hole and remote uniaxial loading using a two-dimensional finite element analysis with both uniform stress and uniform displacement boundary conditions. Five different laminates were analyzed. Computed results are presented for selected combinations of hole diameter/sheet-width ratio d/w and length-to-width ratio L/w. For small L/w values, the stress-concentration factors K sub tn were significantly different for the uniform stress and uniform displacement boundary conditions. Typically, for the uniform stress condition, the K sub tn values were much larger than for the infinite strip reference condition; however, for the uniform displacement condition, they were only slightly smaller than for this reference. The results for long strips are also presented as width correction factors. For d/w less or = 0.33, these width correction factors are nearly equal for all five laminates.
Fatigue-crack initiation and early stages of growth in notched 2024-T3 aluminum alloy sheet specimens were monitored during constant-amplitude fatigue tests conducted for a range of stress ratios. A video tape system was developed to detect fatigue cracks 0.1 mm in length on the sheet surface and to monitor their growth. Fatigue cracks initiated either at the notch corner or on the notch surface. Most of the first fatigue cracks started as notch-corner cracks, and the crack-initiation period was defined as the number of cycles for which the crack was 0.1 mm in length on the sheet surface. For each of the stress ratios used, the results showed that at the low stress levels, the crack-initiation period constituted at least 90 percent of the fatigue lives. However, for the negative stress ratios at the high stress levels, cracks started as early as at about 40 percent of the fatigue lives.
Cyclic debonding rates were measured during constant-amplitude loading of specimens made of graphite/epoxy bonded to aluminum and S-glass/epoxy bonded to aluminum. Both room-temperature and elevated-temperature curing adhesives were used. Debonding was monitored with a photoelastic coating technique. The debonding rates were compared with three expressions for strain-energy release rate calculated in terms of the maximum stress, stress range, or a combination of the two. The debonding rates were influenced by both adherent thickness and the cyclic stress ratio. For a given value of maximum stress, lower stress ratios and thicker specimens produced faster debonding. Microscopic examination of the debonded surfaces showed different failure mechanisms both for identical adherends bonded with different adhesive and, indeed, even for different adherends bonded with identical adhesives. The expressions for strain-energy release rate correlated the data for different specimen thicknesses and stress ratios quite well for each material system, but the form of the best correlating expression varied among material systems. Empirical correlating expressions applicable to one material system may not be appropriate for another system.
A fatigue analysis, based on finite-element calculations and fatigue tests, was conducted for an aluminum-alloy sheet specimen with a steel interference-fit bolt. The stress analysis of the region near the bolt hole showed that the beneficial effect of an interference-fit bolt can be interpreted as the combined result of two effects: (1) load transfer through the bolt and (2) the compressive interference stresses in the sheet. Results of the fatigue tests show that progressively higher interference levels produced longer fatigue lives. The tests also show that a high level of interference prevents fretting at the bolt-sheet interface and that interferences larger than this level produced little additional improvement in fatigue life.
Strain energy release rates were used to correlate cyclic debonding between metal sheets and composite reinforcement. An expression for the strain energy release rate was derived and applied to fatigue test results for three material systems: graphite bonded to aluminum with both a room temperature and an elevated temperature curing adhesive; and, S-glass bonded to aluminum with an elevated temperature curing adhesive. For each material system, specimens of several thicknesses were tested with a range of fatigue loads. Cyclic debonding was monitored using a photoelastic technique. A close correlation was found between the observed debond rates and the calculated strain energy release rates for each material system.
The applicability of acoustic emission technique to measure fatigue cracks in aluminum alloy specimens was investigated. There are several variables, such as the metallurgical and the physical treatment of the specimen, that can affect the level of acoustic activity of a fatigue specimen. It is therefore recommended that the acoustic emission technique be supplemented by other nondestructive evaluation methods to obtain quantitative data on crack growth.
The stresses and strains in a uniaxially loaded sheet with an unloaded interference-fit bolt were calculated by an elastoplastic finite-element analysis. The material properties represented a 7075-T6 aluminum alloy sheet and a steel bolt. The analysis considered the two ideal cases of no slip and no friction at the bolt-sheet interface for a single combination of bolt diameter, interference level, and cyclic loading. When the bolt was inserted, the sheet deformed plastically near the hole; the first tensile load cycle produced additional yielding, but subsequent cycles to the same level caused only elastic cyclic stresses. These stresses together with fatigue data for unnotched specimens were used to estimate crack initiation periods and initiation sites. The cases analyzed with interference-fit bolts were predicted to have crack initiation periods which were about 50 times that for a clearance-fit bolt. Crack initiation was predicted to occur on the transverse axis at a distance of about one radius from the hole.
A semianalytical method was developed for determining elastoplastic cyclic stresses and strains at notch roots in metallurgically bonded metal laminates. The method is based on the Neuber equation, which was used with an effective stress-strain curve for the laminate. It was applied to laminates containing a circular hole which were subjected to one cycle of reversed loading. The laminates consisted of two elasto-perfectly-plastic materials with different yield strengths and with either equal or different Young's moduli. A laminate of high-strength titanium alloy with alternate layers of commercially pure titanium was also analyzed. The accuracy of the method was evaluated by comparing the stresses and strains with those calculated from a finite-element analysis. The results estimated by the simple method based on the Neuber equation agreed closely with the results computed from the more elaborate finite-element analysis.
Strain energy release rates were used to correlate cyclic debonding between metal sheets and composite reinforcement. An expression for the strain energy release rate was derived and applied to fatigue test results for three material systems: graphite bonded to aluminum with both a room temperature and an elevated temperature curing adhesive, and S-glass bonded to aluminum with an elevated temperature curing adhesive. For each material system, several thicknesses were tested with a range of fatigue loads. Cyclic debonding was monitored using a photoelastic technique. A close correlation was found between the observed debond rates and the calculated strain energy release rates for each material system.
The stresses in a sheet with an interference-fit bolt have been calculated for two sheet-bolt interface conditions: a frictionless interface and a fixed (no-slip) interface. The stress distributions were calculated for various combinations of sheet and bolt moduli. The results show that for repeated loading the local stress range is significantly smaller if an interference bolt is used instead of a loosely fitting one. This reduction in local stress range is more pronounced when the ratio of bolt modulus to sheet modulus is large. The analysis also indicates that currently used standard values of interference cause yielding in the sheet.
Fatigue crack growth from a circular hole was investigated experimentally and analytically. An aluminum-alloy sheet specimen was cycled under a single level of loading with and without prior high loads. Tests showed that the crack propagation life was significantly longer when the high loads were applied initially. This longer life was attributed to compressive residual stresses produced near the hole by the initial high loads. The residual stresses near the hole were determined by an elastoplastic analysis and were then used to develop a stress-intensity solution for a crack growing through the residual stress field. This solution and a similar solution for the case of no prior loading were used to predict crack growth. The predicted crack growth agreed closely with the experimental values.
The effects of loading sequence on crack-initiation period were investigated for notched aluminum-alloy specimens under high-low two-step loading with special emphasis on local cyclic stresses and strains at the notch root. Local stress and strain were determined by a procedure based on an equation proposed by Neuber which relates elastoplastic stress and strain at a notch. Local stress and strain were also measured experimentally to verify the Neuber equation. The effects of initial high load on the crack-initiation periods were demonstrated with notched specimens and were simulated in unnotched specimens fatigue tested with local stress sequences. An analysis of the results indicated that sequence effects were not caused solely by local residual stresses, as is usually assumed; the existence of a damaging effect, resulting from the high local strain cycles, was demonstrated. The sequence effects observed with notched specimens were interpreted as the combined result of residual stresses and high local strain cycles.
Notched metal crack initiation, determining high cyclic loads effects by prior local plastic behavior at stress concentration
Elastoplastic stress-strain behavior at notch roots in sheet specimens under constant amplitude loading
Fatigue cracking at stress concentration under cyclic loading