Crunkleton, Daniel W.

DOE OSTI2024

Vascular Carbon/Carbon composites for concentrated solar power

Due to their exceptional mechanical and thermal properties under high temperature conditions, for the first time, a novel vascular (embedded channels) Carbon/Carbon (C/C) composite was developed for use as a modular concentrated solar power (CSP) gas receiver. The fabrication process involves the combination of the vaporization of sacrificial component (VaSC) technique with conventional methods to produce C/C composites with well preserved channels. Different heat treatments were evaluated together with X-ray diffraction (XRD) analysis to determine optimal fabrication conditions that maintains the material and channel’s integrity. Mechanical testing confirms that structural integrity is maintained, with statistical analyses indicating no compromise in flexural strength or modulus. Furthermore, this research introduces an innovative pathway for efficient CSP gas receivers, which can bridge the gap towards improved energy generation efficiency in next-gen CSP plants through higher operating temperatures with the use of C/C composites.

14 SOLAR ENERGY↗

DOE OSTI2022

Prediction of curing kinetics of resorcinol‐added resole phenolic resins using differential scanning calorimetry for the fabrication of carbon/carbon composites

Phenolic resins are commonly used as carbon precursors for the fabrication of carbon/carbon composites due to their high carbon yield and aromatic nature. To decrease curing times, acid catalysts are generally used, but the addition of resorcinol was found to have a similar effect while being incorporated into the resin matrix with no contamination or corrosion issues. In this work, the curing kinetics of pure, 10, 20, and 30 wt% resorcinol-added phenolic resins were investigated through differential scanning calorimetry. Heating rates of 0.5, 1, 2.5, and 5°C min -1 were used with several curing models to predict isothermal curing. Averaged mean absolute error (MAE) for the isoconversional mathematical approaches namely Kissinger–Akahira–Sunose (MAE = 12.9 min), Flynn–Wall–Ozawa (15.8 min), and Vyazovkin (14 min) show that these methods provide the best predictions, attributed to their adoption of an activation energy that depends on the extent of cure (E a (α)). The Kissinger method (MAE = 36 min), which depends only on peak temperature with a constant activation energy assumption, and the data noise sensitive Friedman model (MAE = 1144.7 min) provide the least accurate results. Thermogravimetric analysis revealed that resorcinol decreases the curing times by up to 71% without lowering carbon yield.

36 MATERIALS SCIENCE↗