NASA NTRS1995

Relative performance comparison between baseline labyrinth and dual-brush compressor discharge seals in a T-700 engine test

In separate series of YT-700 engine tests, direct comparisons were made between the forward-facing labyrinth and dual brush compressor discharge seals. Compressor speeds to 43 000 rpm, surface speeds to 160 m/s (530 ft/s), pressures to 1 MPa (145 psi), and temperatures to 680 K (765 F) characterized these tests. The wear estimate for 46 hr of engine operations was less than 0.025 mm (0.001 in.) of the Haynes 25 alloy bristles running against a chromium-carbide-coated rub runner. The pressure drops were higher for the dual-brush seal than for the forward-facing labyrinth seal and leakage was lower-with the labyrinth seal leakage being 2-1/2 times greater-implying better seal characteristics, better secondary airflow distribution, and better engine performance (3 percent at high pressure to 5 percent at lower pressure) for the brush seal. (However, as brush seals wear down (after 500 to 1000 hr of engine operation), their leakage rates will increase.) Modification of the secondary flow path requires that changes in cooling air and engine dynamics be accounted for.

Hendricks, Robert C.↗

NASA NTRS1995

Metallographic Analysis of Brush Bristle and Integrity Testing of Brush Seal in Shroud Ring of T-700 Engine

Post-test investigation of a T-700 engine brush seal found regions void of bristles ('yanked out'), regions of bent-over bristles near the inlet, some 'snapped' bristles near the fence, and a more uniform 'smeared' bristle interface between the first and last axial rows of bristles. Several bristles were cut from the brush seal, wax mounted, polished, and analyzed. Metallographic analysis of the bristles near the rub tip showed tungsten-rich phases uniformly distributed throughout the bristle with no apparent change within 1 to 2 micron of the interface except for possibly a small amount of titanium, which would represent a transfer from the rotor. Analysis of the bristle wear face showed nonuniform tungsten, which is indicative of material resolidification. The cut end contained oxides and internal fractures; the worn end was covered with oxide scale. Material losses due to wear and elastoplastic deformation within the shear zone and third-body lubrication effects in the contact zone are discussed.

Hendricks, Robert C.↗

NASA NTRS1994

Relative performance comparison between baseline labyrinth and dual-brush compressor discharge seals in a T-700 engine test

In separate series of T-700 engine tests, direct comparisons were made between the forward-facing labyrinth and dual-brush compressor discharge seals. Compressor speeds to 43,000 rpm, surface speeds to 160 m/s (530 ft/s), pressures to 1 MPa (145 psi), and temperatures to 680 K (765 F) characterized these tests. The wear estimate for 40 hr of engine operations was less than 0.025 mm (0.001 in.) of the Haynes 25 alloy bristles running against a chromium-oxide-coated rub runner. The pressure drops were higher for the dual-brush than for the forward-facing labyrinth seal, implying better seal characteristics and engine performance for the brush seal. Modification of the secondary flow path requires that changes in cooling air and engine dynamics be accounted for.

Hendricks, Robert C.↗

NASA NTRS1994

Some metallographic results for brush bristles and brush segments of a shroud ring brush seal tested in a T-700 engine

Post-test investigation of a T-700 engine brush seal found regions void of bristles ('yanked out'), regions of bent-over bristles near the inlet, some 'snapped' bristles near the fence, and a more uniform smeared bristle interface between the first and last axial rows of bristles. Several bristles and four brush segments were cut from the brush seal, wax mounted, polished, and analyzed. Metallographic analysis of the bristle near the rub tip showed tungsten-rich phases uniformly distributed throughout the bristle, no apparent change within 1 mu m of the interface, and possibly a small amount of titanium, which would represent a transfer from the rotor. Analysis of the bristle wear face showed nonuniform tungsten, which is indicative of material resolidification. The cut end contained oxides and internal fractures; the worn end was covered with oxide scale. Material losses due to wear and elastoplastic deformation within the shear zone and third-body lubrication effects in the contact zone are discussed.

Hendricks, Robert C.↗