NASA NTRS1991

The effect of stress on hydrogen uptake and desorption by A-286

The uptake and desorption of hydrogen by A-286 as a function of stress was studied using electrochemical methods. It was found that the apparent surface hydrogen concentration, the mean hydrogen concentration, and the hydrogen distribution uniformity all increased up to a stress level 50 percent of yield and decreased thereafter. The value of the hydrogen diffusion coefficient was relatively unaffected by stress while the percent of trapped hydrogen appeared to decrease with increasing stress.

Danford, Merlin D.↗

NASA NTRS1990

Polytetrafluoroethylene-Impregnated Anodization For Aluminum

Technical memorandum describes experiments on ability of two commercial coatings and of standard hard anodization to protect aluminum against corrosion. Both commercial coatings, Polylube and Tufram, polytetrafluoroethylene-impregnated anodizations. Standard hard-anodized coating found to provide greatest protection.

Danford, Merlin D.↗

NASA NTRS1989

Electrochemical Studies Of Aluminum Coated With Primer

Technical paper describes experiments using ac-impedance method of analyzing corrosion of metal surfaces and breakdown of protective coatings. Alternating-current-impedance scans provide more detailed information, indicating changes in corrosion rates, progressive deterioration of coatings, changes in metal surfaces, and reaction mechanisms. Changes in conditions of coatings detected by ac method before dc methods show increase in metal-corrosion current. Measurements of impedance as function of frequency provides sufficient data to enable resistances and capacitances to be determined by performing least-squares fit. Knowledge of dependence of these values on time leads to more detailed understanding of corrosion process.

Danford, Merlin D.↗

NASA NTRS1989

The corrosion protection of aluminum by various anodizing treatments

Corrosion protection to 6061-T6 aluminum, afforded by both teflon-impregnated anodized coats (Polylube and Tufram) and hard-anodized coats (water sealed and dichromate sealed), was studied at both pH 5.5 and pH 9.5, with an exposure period of 28 days in 3.5 percent NaCl solution (25 C) for each specimen. In general, corrosion protection for all specimens was better at pH 9.5 than at pH 5.5. Protection by a Tufram coat proved superior to that afforded by Polylube at each pH, with corrosion protection by the hard-anodized, water-sealed coat at pH 9.5 providing the best protection. Electrochemical work in each case was corroborated by microscopic examination of the coats after exposure. Corrosion protection by Tufram at pH 9.5 was most comparable to that of the hard-anodized samples, although pitting and some cracking of the coat did occur.

Danford, Merlin D.↗

NASA NTRS1988

Diffusion Analysis Of Hydrogen-Desorption Measurements

Distribution of hydrogen in metal explains observed desorption rate. Report describes application of diffusion theory to anaylsis of experimental data on uptake and elimination of hydrogen in high-strength alloys of 25 degree C. Study part of program aimed at understanding embrittlement of metals by hydrogen. Two nickel-base alloys, Rene 41 and Waspaloy, and one ferrous alloy, 4340 steel, studied. Desorption of hydrogen explained by distribution of hydrogen in metal. "Fast" hydrogen apparently not due to formation of hydrides on and below surface as proposed.

Danford, Merlin D.↗

NASA NTRS1988

Galvanic Corrosion In (Graphite/Epoxy)/Alloy Couples

Effects of galvanic coupling between graphite/epoxy composite material, G/E, and D6AC steel, 6061-T6 aluminum, and Inconel(R) 718 nickel alloy in salt water described in report. Introductory section summarizes previous corrosion studies of G/E with other alloys. Details of sample preparation presented along with photographs of samples before and after immersion.

Danford, Merlin D.↗

NASA NTRS1987

Hydrogen trapping and the interaction of hydrogen with metals

A method has been developed for the determination of trapped hydrogen in metal alloys, involving the determination of mobile hydrogen using the electrochemical method and the determination of total hydrogen with the fusion method, the difference in hydrogen concentrations being due to trapped hydrogen. It has been found that hydrogen enters body-centered cubic structures through the grain bodies rather than through the grain boundaries. Hydrogen also diffuses much more rapidly in body-centered cubic structures on charging than in face-centered cubic structures, the hydrogen distribution being more uniform in nature. The energy necessary to cause hydrogen embrittlement is postulated to arise from the changes in crystal lattice energies brought about through interaction of hydrogen with atoms in the metal lattice. The total energy change is more negative for body-centered cubic structures, believed to be the cause of a greater tendency toward hydrogen embrittlement. Finally, the agreement of hydrogen concentrations obtained at 25 C by the electrochemical method with those obtained by the fusion method are taken as a strong indication of the power and validity of the electrochemical method.

Danford, Merlin D.↗

NASA NTRS1987

The corrosion mechanisms for primer coated 2219-T87 aluminum

To investigate metal surface corrosion and the breakdown of metal protective coatings, the ac Impedance Method was applied to zinc chromate primer coated 2219-T87 aluminum. The EG&GPARC Model 368 ac Impedance Measurement System, along with dc measurements with the same system using the Polarization Resistance Method, was used to monitor changing properties of coated aluminum disks immersed in 3.5 percent NaCl solutions buffered at pH 5.5 and pH 8.2 over periods of 40 days each. The corrosion system can be represented by an electronic analog called an equivalent circuit consisting of resistors and capacitors in specific arrangements. This equivalent circuit parallels the impedance behavior of the corrosion system during a frequency scan. Values for resistances and capacitances, that can be assigned in the equivalent circuit following a least squares analysis of the data, describe changes occurring on the corroding metal surface and in the protective coatings. A suitable equivalent circuit has been determined which predicts the correct Bode phase and magnitude for the experimental sample. The dc corrosion current density data are related to equivalent circuit element parameters.

Danford, Merlin D.↗