DOE OSTI2024

Hydride-Based Interlayer for Solid-State Anode-Free Battery

Solid-state batteries (SSBs) are considered a promising approach to realizing an anode-free concept with high energy densities. However, the initial Coulombic efficiency (ICE) has remained insufficient for anode-free batteries using sulfide-based solid electrolytes (SEs). Herein, we incorporated a hydride-based interlayer, 3LiBH 4 -LiI (LBHI), between a typical sulfide SE, Li 6 PS 5 Cl, and the Cu current collector. Further, by investigating the Li plating and stripping behaviors and the (electro)chemical stability between SEs and plated Li, we demonstrated that LBHI can effectively improve interfacial stability, leading to an ICE exceeding 94% in anode-free half cells. This interlayer also improves Coulombic efficiencies and specific capacities in anode-free full cells. Furthermore, the utilization of LBHI enables one to study Li plating behaviors without interference from interfacial (electro)chemical instabilities. The analysis of stack pressure evolution during electrochemical cycling reveals that soft shorting in SSBs arises from both dendrite formation and deformation, offering insights into further optimizing solid-state anode-free batteries.

25 ENERGY STORAGE↗

DOE OSTI2023

Structural evolution during solution-based synthesis of Li 7 P 3 S 11 solid electrolyte by synchrotron X-ray total scattering

Solution-based synthesis has emerged as a promising approach for scalable and efficient synthesis of solid electrolytes (SEs). However, the ionic conductivity of solution-synthesized SEs is much lower than that of SEs synthesized by solid state approaches. The structural evolution during the synthesis of SEs is crucial to explaining the decreased ionic conductivities but has not been well understood. Here, in this work, we use synchrotron X-ray total scattering combined with pair distribution function (PDF) analysis to understand the structural evolution during annealing of the solution-processed precursor for the synthesis of Li 7 P 3 S 11 SEs. Combining Bragg diffraction and diffuse scattering, X-ray total scattering enables detection of structural information including phase transition and crystallinity. The results show that the formation of Li 7 P 3 S 11 glass-ceramic starts at 230 °C. Increasing the annealing temperature helps to improve the crystallinity, but the degree of crystallization is still lower than 70.3% even after annealing at 290 °C when thermal decomposition of Li 7 P 3 S 11 to Li 4 P 2 S 6 has occurred. PDF analysis also revealed the existence of acetonitrile used in the solution-based synthesis in the SEs after annealing at high temperatures. The results rationalize the synthesis–property relationship, explain why annealing at 290 °C provides the highest ionic conductivity at the studied temperatures due to an optimal balance for achieving a high crystallinity while suppressing severe decomposition of Li 7 P 3 S 11 , and provide novel insights to develop approaches for synthesizing superior Li 7 P 3 S 11 SEs on a large scale.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗