Effects of surface anisotropy on the surface morphological response of plasma-facing tungsten
Not Available
Patel, Omeet N. (ORCID:0000000200598351)↗
Engineering topics
Dasgupta, Dwaipayan (ORCID:000000019405922X)
Publications and source records attributed to Dasgupta, Dwaipayan (ORCID:000000019405922X).
Assessment of the literature about Be-W mixed material layer formation in the fusion reactor environment
Abstract All plasma facing surfaces in a fusion reactor, whether initially pure or an alloy, will rapidly evolve into a mixed material due to plasma-induced erosion, migration and redeposition. Beryllium (Be) erosion from the main chamber, and its transport and deposition on to a tungsten (W) divertor results in the growth of mixed Be-W layers, which can evolve to form beryllides. These Be-W mixed materials exhibit generally less desirable properties than pure tungsten or pure beryllium, such as lower melting points. In order to better understand the parameter space for growth of these alloys, this paper reviews the literature on Be-W mixed material formation experiments—in magnetically confined fusion reactors, in linear plasma test stands, and during thin-film deposition—and on computational modeling of Be-W interactions, as well as briefly assesses the Be-W growth kinetics. We conclude that the following kinetic steps drive the material mixing: adsorption of the implanted/deposited ion on the metal surface; diffusion of the implanted/deposited ion from surface into the bulk, which is accelerated by defects; and loss of deposited material through erosion. Adsorption dominates (or prevents) material mixing in thin-film deposition experiments, whereas diffusion drives material mixing in plasma exposures due to the energetic ion implantation.
70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
Helium bubble size effects on the surface morphological response of plasma-facing tungsten
Abstract We report a simulation study on the effects of helium (He) bubble size on the morphological evolution and pattern formation on the surface of tungsten used as a plasma-facing component (PFC) in nuclear fusion devices. We have carried out a systematic investigation based on self-consistent dynamical simulations of surface morphological evolution according to an atomistically-informed, 3D continuum-scale model that captures well the relevant length and time scales of surface nanostructure formation in PFC tungsten. The model accounts for PFC surface diffusion, driven by the biaxial compressive stress originating from the over-pressurized He bubbles in the near-surface region of PFC tungsten as a result of He plasma exposure, combined with the formation of self-interstitial atoms in tungsten that diffuse toward the PFC surface and the flux of surface adatoms generated as a result of surface vacancy-adatom pair formation upon He implantation; this transport of surface adatoms contributes to the anisotropic growth of surface nanostructural features due to the different rates of adatom diffusion along and across step edges of islands on the tungsten surface. Our detailed analysis reveals that varying the average He bubble size plays an important role in the PFC surface growth kinetics as well as the resulting surface topography. Specifically, we find that an increase in the He bubble size leads to a deceleration in the growth rate of the tungsten nanotendrils that emanate from the PFC surface. We also find that the separation distance between the resulting surface features increases with increasing He bubble size, as well as over time. This coarsening effect is a thermally activated process resulting in an accurate description of the temperature dependence of the average surface feature separation by an Arrhenius relation.
36 MATERIALS SCIENCE↗
Impact of Soret effect on hydrogen and helium retention in PFC tungsten under ELM-like conditions
Abstract In our previous work, we have demonstrated using nonequilibrium molecular-dynamics simulations that the fluxes of helium and self-interstitial atoms in the presence of a thermal gradient in tungsten are directed opposite to the heat flux, indicating that species transport is governed by a Soret effect, namely, thermal-gradient-driven diffusion, characterized by a negative heat of transport that drives species transport uphill, i.e. from the cooler to the hot regions of the tungsten sample. In this work, the findings of our thermal and species transport analysis have been implemented in our cluster-dynamics code, Xolotl, which has been used to compute temperature and species profiles over spatiotemporal scales representative of plasma-facing component (PFC) tungsten under typical reactor operating conditions, including extreme heat loads at the plasma-facing surface characteristic of plasma instabilities that induce edge localized modes (ELMs). We demonstrate that the steady-state species profiles, when properly accounting for the Soret effect, vary significantly from those where temperature-gradient-driven transport is not accounted for and discuss the implications of such a Soret effect on the response to plasma exposure of plasma-facing tungsten. Although our cluster-dynamics simulations do not yet include self-clustering of helium or hydrogen blister formation, our simulation results show that the Soret effect substantially reduces helium and hydrogenic species retention inside PFC tungsten.
36 MATERIALS SCIENCE↗
Effects of surface vacancy-adatom pair formation on PFC tungsten surface morphological response
Abstract We report a simulation study of the effect of He-irradiation-induced surface vacancy-adatom pair formation on the surface morphological evolution of plasma-facing component (PFC) tungsten and examine a number of factors that impact such evolution. Our analysis is based on self-consistent dynamical simulations according to an atomistically-informed, continuum-scale surface evolution model that has been developed following a hierarchical multiscale modeling strategy and can access the spatiotemporal scales of relevance to fuzz formation. The model accounts for the flux of surface adatoms generated as a result of the surface vacancy-adatom pair formation effect upon He implantation, which contributes to the anisotropic growth of surface nanostructural features due to the different rates of adatom diffusion along and across step edges of islands on the tungsten surface. We have carried out atomic-scale computations of optimal diffusion pathways along and across island step edges on the W(110) surface and calculated Ehrlich–Schwoebel (ES) barriers in adatom diffusion along and across such step edges. This aspect of surface adatom diffusion contributes to anisotropic surface atomic fluxes, terrace and step diffusive currents, and has been incorporated into our PFC surface evolution model, which predicts the formation of preferentially aligned nanoridge stripe patterns on the PFC surface. We establish that these anisotropic diffusive currents accelerate nanotendril growth on the PFC surface and the onset of surface nanostructure pattern formation. We also explore systematically the dependence of the PFC surface morphological response on the surface temperature and He ion incident flux, characterize in detail the resulting surface topographies and growth kinetics, and compare the predicted surface morphologies with experimental observations. Our simulation predictions for the emerging surface nanostructure patterns under certain plasma exposure conditions are consistent with experimental findings in the literature.
36 MATERIALS SCIENCE↗
Hole formation effect on surface morphological response of plasma-facing tungsten
We report simulation results on the effect of helium (He) bubble bursting-mediated surface hole formation on the surface morphological response of tungsten plasma-facing components (PFCs) in nuclear fusion devices. Our analysis is based on an atomistically informed, continuum-scale model, which is capable of accessing the spatiotemporal scales relevant to the fuzz nanostructure formation process on the surface of PFC tungsten. Our simulations account, in an empirical fashion, for two types of subsurface bubble dynamical phenomena in the nanobubble region of PFC tungsten during He plasma irradiation, involving bubble bursting and surface crater formation. We demonstrate that the hole formation effect on the PFC tungsten surface accelerates the growth rate of nanotendrils and the onset of fuzz formation. As a result, the predicted incubation time for surface nanotendril growth is shortened, in agreement with experimental data of incubation fluence at comparable plasma exposure conditions. We also explore systematically the dependence of the PFC surface morphological response on the areal density of holes introduced at regular time intervals onto the He-implanted tungsten surface, a parameter in our analysis that serves as a proxy for the rate of He bubble bursting. More importantly, our simulations capture fine surface features in the PFC tungsten surface morphology and predict that the average spacing between nanotendrils is on the order of 100 nm, consistent with the experimental findings.
Chen, Chao-Shou (ORCID:0000000307910042)↗