Investigating the Crosslinking, Degradation, and Adhesion Behavior of Photovoltaic Encapsulants Under Thermal Accelerated Aging

Degradation of photovoltaic (PV) module encapsulant characteristics that lead to mechanical embrittlement and delamination remains a cause of failure in solar installations. A multiscale reliability model connecting the encapsulant mechanical and fracture properties to the degraded molecular structure and interfacial bonding to adjacent solar cell and glass substrates was previously published. The model, developed primarily for poly(ethylene-co-vinyl acetate) acetate (EVA) encapsulants, remains to be experimentally validated. Determining the degradation and crosslinking kinetics of alternative encapsulants, such as polyolefin elastomer (POE) and EVA/POE/EVA composites (EPE), can generalize the model. In this work, we subject fully cured EVA, POE, and EPE encapsulants to accelerated thermal aging to determine how high temperatures impact reaction kinetics. An increase in gel content (crosslinking) and decrease in crystallinity of the encapsulants under hot-aerobic (90 degrees C, 22% RH) and hot-anaerobic (90 degrees C, sealed in N 2 air) aging were observed, even in the absence of UV and crosslinking initiators. Fourier transform infrared spectroscopy (FTIR)-attenuated total reflectance analysis showed insignificant encapsulant degradation, demonstrating the critical role of UV and moisture in accelerating degradation. Adhesion testing performed on coupon-level specimens (cell/encapsulant/glass laminates) showed decreases in adhesion energy, Gc , from 5000 h of hot-dry (90 degrees C, ~1% RH) and hot-humid (90 degrees C, 60% RH) aging. POE coupons demonstrated the best stability, followed by EPE then EVA. For EVA and POE, hot-humid aged coupons experienced a larger decrease in Gc due to enhanced hydrolytic degradation. Hot-dry aging condition demonstrated that thermal degradation of the interface could be significant even if the encapsulant experiences negligible degradation in the absence of UV and elevated humidity.

accelerated aging↗
DOE OSTI2024

Determining the Crosslinking and Degradation Reaction Kinetics in Photovoltaic Encapsulants Using Accelerated Aging: Preprint

Degradation of photovoltaic (PV) module encapsulant mechanical characteristics that lead to embrittlement and delamination remains a cause of failure in solar installations. A multiscale reliability model based on detailed molecular degradation reaction kinetics was previously published, connecting the encapsulant mechanical properties (elastic modulus, yield strength, and adhesion energy) to the degraded molecular structure and interfacial bond density to adjacent solar cell and glass substrates. The model, developed primarily for poly(ethylene-co-vinyl acetate) (EVA) encapsulants, remains to be experimentally validated. Determining the degradation and crosslinking kinetics of alternative encapsulants, such as polyolefin elastomer (POE) and EVA/POE/EVA composites (EPE), can further generalize the model. Importantly, the activation energy for crosslinking of fully cured PV encapsulant products from temperature or UV is presently unknown or unavailable. In this work, we subject EVA, POE, and EPE encapsulants to a set of accelerated aging conditions, varying the temperature, UV intensity, and relative humidity. We use DSC, FTIR, and Soxhlet extraction (gel content) to characterize the encapsulants' changing molecular structure. This allows for determination of the photochemical degradation and crosslinking kinetics of the encapsulants. Preliminary results show an increase in gel content (crosslinking) and a decrease in crystallinity of EVA, POE, and EPE encapsulants under hot-aerobic (90 deg C, 22% RH) and hot-anaerobic (90oC, sealed in N2 air) accelerated aging, even in the absence of UV and crosslinking initiating agents. For a least squares regression with an assumed first-order crosslinking kinetics, the crosslinking rate parameters were computed for the three encapsulants under hot-aerobic and hot-anaerobic aging conditions. FTIR analysis showed insignificant encapsulant degradation for hot-aerobic and hot-anaerobic aging, demonstrating the critical role of UV and moisture in accelerating degradation. Aging conditions with UV exposure and elevated humidity are presently in progress.

adhesion↗
DOE OSTI2024

Indirect Liftoff Mechanism for High‐Throughput, Single‐Source Laser Scribing for Perovskite Solar Modules

A high‐throughput, single‐source laser scribing method exploiting a transparent conducting oxide (TCO) indirect liftoff mechanism is developed to produce serially interconnected perovskite solar modules. The TCO‐based indirect liftoff mechanism relies solely on laser absorption in the front transparent electrode material reducing thermal damage to the overlying layers and allowing for fast scribing speeds with low‐cost μs‐pulse duration fiber laser systems. Minimal resistive power losses are observed with the method compared to conventional ablative laser scribes, maintaining the power conversion efficiencies of small‐area devices (≈0.2 cm 2 ) across significantly larger deposition areas (≈1 cm 2 ). Finally, demonstrating > 3 m s −1 processing speeds, TCO‐based liftoff provides the highest throughput laser scribing method for thin‐film photovoltaic devices produced on glass/TCO substrates, capable of processing large‐area perovskite solar modules at a manufacturing scale.

14 SOLAR ENERGY↗
DOE OSTI2023

Predicting encapsulant delamination in photovoltaic modules bridging photochemical reaction kinetics and fracture mechanics

Abstract Photovoltaic (PV) modules are subjected to environmental stressors (UV exposure, temperature, and humidity) that cause degradation within the encapsulant and its interfaces with adjacent glass and cell substrates. To save experimental time and to enable long‐term assessment with intensive degradation only taking place after many years, the development of predictive models is indispensable. Previous works have modeled the delamination of the ethylene vinyl acetate (EVA) encapsulant/glass and encapsulant/cell interfaces under field aging conditions with fundamental photochemical degradation reactions that lead to molecular scission and loss of interfacial adhesion, characterized by the fracture resistance, G c . However, these models were fundamentally limited in that the following aspects were not incorporated: (i) molecular crosslinking in the field, (ii) synergistic autocatalytic interactions of degradation mechanisms, (iii) connection between degraded encapsulant structure and its mechanical properties, and (iv) rigorous treatment of the plasticity contribution to G c with finite element models. Here, we present a time‐dependent multiscale model that addresses these limitations and is applicable to a wide range of encapsulants and interfaces. For the reference EVA encapsulant and its interfaces with the glass and cell, the presented model predicts an initial rise in G c in the first 3 years of field aging from crosslinking, then a subsequent sharp decline from degradation mechanisms. We used nanoindentation to measure the changes in EVA mechanical properties over exposure time to tune the model parameters. The model predictions of G c and mechanical properties match with experimental data and show an improvement compared to previous models. The model can even predict switches in failure interfaces, such as the observed EVA/cell to EVA/glass transition. We also conducted a sensitivity analysis study by varying the degradation and crosslinking kinetic parameters to demonstrate their effects on G c . Model extensions to polyolefin elastomer‐ and silicone‐encapsulants and their interfaces are also demonstrated.

Liu, Kuan↗
DOE OSTI2023

Water vapor transmission rate measurement for moisture barriers using infrared imaging

Here, in this work, we demonstrate a spatially resolved imaging methodology for water vapor transmission rate (WVTR) testing that relies on quantified infrared characterization at water absorption bands. This technique is validated using a moisture barrier on a polymer substrate via calibration of the infrared image intensity with moisture content in the polymer substrate from images taken at different times. The method is compared to existing state of the art techniques such as membrane permeation measurement with coulometric phosphorous pentoxide sensor and optical calcium film testing. This fast, non-destructive and in-situ method enables defect visualization and shows the WVTR with a sensitivity limit of 5·10 –5 g/m 2 /day.