NASA NTRS2016

A Modified Edge Crack Torsion Test for Measurement of Mode III Fracture Toughness of Laminated Tape Composites

Modifications to the edge crack torsion (ECT) test are studied to improve the reliability of this test for measuring the mode-III fracture toughness, G (sub IIIc), of laminated tape fiber-reinforced polymeric (FRP) composites. First, the data reduction methods currently used in the ECT test are evaluated and deficiencies in their accuracy are discussed. An alternative data reduction technique, which uses a polynomial form to represent ECT specimen compliance solution, is evaluated and compared to FEA (finite element analysis) results. Second, seven batches of ECT specimens are tested, each batch containing specimens with a preimplanted midplane edge delamination and midplane plies with orientations of plus theta divided by minus theta, with theta ranging from 0 degrees to 90 degrees in 15-degree increments. Tests on these specimens show that intralaminar cracking occurs in specimens from all batches except for which theta = 15 degrees and 30 degrees. Tests on specimens of these two batches are shown to result in mode-III delamination growth at the intended ply interface. The findings from this study are encouraging steps towards the use of the ECT test as a standardized method for measuring G (sub IIIc), although further modification to the data reduction method is required to make it suitable for use as part of a standardized test method.

Czabaj, Michael W.↗

NASA NTRS2013

Observation of Intralaminar Cracking in the Edge Crack Torsion Specimen

The edge crack torsion (ECT) test is evaluated to determine its suitability for measuring fracture toughness associated with mode III delamination growth onset. A series of ECT specimens with preimplanted inserts with different lengths is tested and examined using nondestructive and destructive techniques. Ultrasonic inspection of all tested specimens reveals that delamination growth occurs at one interface ply beneath the intended midplane interface. Sectioning and optical microscopy suggest that the observed delamination growth results from coalescence of angled intralaminar matrix cracks that form and extend across the midplane plies. The relative orientation of these cracks is approximately 45 deg with respect to the midplane, suggesting their formation is caused by resolved principal tensile stresses arising due to the global mode-III shear loading. Examination of ECT specimens tested to loads below the level corresponding to delamination growth onset reveals that initiation of intralaminar cracking approximately coincides with the onset of nonlinearity in the specimen's force-displacement response. The existence of intralaminar cracking prior to delamination growth onset and the resulting delamination extension at an unintended interface render the ECT test, in its current form, unsuitable for characterization of mode III delamination growth onset. The broader implications of the mechanisms observed in this study are also discussed with respect to the current understanding of shear-driven delamination in tape-laminate composites.

Czabaj, Michael W.↗

NASA NTRS1990

Probabilistic failure assessment with application to solid rocket motors

A quantitative methodology is being developed for assessment of risk of failure of solid rocket motors. This probabilistic methodology employs best available engineering models and available information in a stochastic framework. The framework accounts for incomplete knowledge of governing parameters, intrinsic variability, and failure model specification error. Earlier case studies have been conducted on several failure modes of the Space Shuttle Main Engine. Work in progress on application of this probabilistic approach to large solid rocket boosters such as the Advanced Solid Rocket Motor for the Space Shuttle is described. Failure due to debonding has been selected as the first case study for large solid rocket motors (SRMs) since it accounts for a significant number of historical SRM failures. Impact of incomplete knowledge of governing parameters and failure model specification errors is expected to be important.

Jan, Darrell L.↗

NASA NTRS1990

An experimental investigation of delamination buckling and growth

An experimental investigation of delamination buckling and growth in compression loaded composite laminates is described. Compression tests were conducted on impact damaged laminates and laminates containing preimplanted delaminations. These tests were performed utilizing a fixture designed to prevent global buckling. The results of this study indicate that considerations in addition to initial defect geometry influence the shape of the boundary of the buckled region. Further, idealized delamination buckling from preimplanted delaminations may occur quite differently than in the case of an impact damaged laminate. The growth of a delamination following buckling may follow an irregular path and may involve the delamination growing into different interfaces.

Davidson, Barry D.↗