Silicon Materials Task of the Low Cost Solar Array Project, Phase 3. Effect of Impurities and Processing on Silicon Solar Cells

The effects of impurities, various thermochemical processes, and any impurity process interactions on the performance of terrestrial silicon solar cells are defined. Determinations of the segregation coefficients of tungsten, tantalum, and cobalt for the Czochralski pulling of silicon single crystals are reported. Sensitive neutron activation analysis was used to determine the metal impurity content of the silicon while atomic absorption was used to measure the metal content of the residual liquid from which the doped crystals were grown. Gettering of Ti doped silicon wafers improved cell performance by one to two percent for the highest temperatures and longest times. The HCl is more effective than POCl3 treatments for deactivating Ti but POCl3 and HCl produced essentially identical results for Mo or Fe.

Hopkins, R. H.↗
NASA NTRS1979

Array Automated Assembly Task for the Low Cost Solar Array Project, Phase 2

Using silk screened evaporated and sputtered Al as the metal source, the formation of Al back surface fields was studied. The most satisfactory results were those obtained with the sputtered A1 and in which open circuit voltages (V sub oc) of 0.585 v (12 ohm cm FZ silicon) were achieved. The ultrasonic interconnect process is discussed. The process is shown to be satisfactory, but increased pull-strength may be obtained if some form of sintering is carried out on the metallized contacts. Plasma etching is shown to be feasible as a replacement for wet chemical cleaning prior to diffusion. Initial results on cells prepared by using electroless Pd/Ni plus either electroplated Ag or Cu show slightly poor performance than cells with the baseline evaporated Ti/Pd/Ag system. A mask designed for the 1.6 x 7.0 cm and 2.0 x 7.0 cm cells is described. This mask has a lower area coverage and total lower resistive loss than the previous mask design. It is also shown that the cell width should not exceed 2.0 - 3.0 cm for optimum efficiency.

Campbell, R. B.↗
NASA NTRS1979

Effects of Impurities and Processing on Silicon Solar Cells, Phase 3

Results of the 14th quarterly report are presented for a program designed to assess the effects of impurities, thermochemical processes and any impurity process interactions on the performance of terrestrial silicon solar cells. The Phase 3 effort encompasses: (1) potential interactions between impurities and thermochemical processing of silicon; (2) impurity-cell performance relationships in n-base silicon; (3) effect of contaminants introduced during silicon production, refining or crystal growth on cell performance; (4) effects of nonuniform impurity distributions in large area silicon wafers; and (5) a preliminary study of the permanence of impurity effects in silicon solar cells.

Hopkins, R. H.↗
NASA NTRS1979

Phase Two of the Array Automated Assembly Task for the Low Cost Solar Array Project

Various top contact metal systems were studied. Only Ti Pd Cu approaches baseline (Ti Pd Ag) quality, but this system shows a lack of long term stability. Aluminum back surface field structures were fabricated and thicknesses of p superscript + material of up to 7.0 microns were achieved with open circuit voltages of 0.59V. A general purpose ultrasonic welder was purchased and tests using various metal foils are under way. During fabrication of the demonstration module, several cells became cracked. Due to redundancy of interconnections, the module was not open circuited but the efficiency was reduced to 8.8%. The broken cell was interconnected with a strap across the back and the efficiency was increased to 11.5%. A cost analysis was made and the results indicate a selling price of $0.56/watt peak (in 1986 with 1975 dollars).

Campbell, R. B.↗
NASA NTRS1979

Silicon materials task of the low cost solar array project. Phase 3: Effect of impurities and processing on silicon solar cells

The 13th quarterly report of a study entitled an Investigation of the Effects of Impurities and Processing on Silicon Solar Cells is given. The objective of the program is to define the effects of impurities, various thermochemical processes and any impurity-process interactions on the performance of terrestrial silicon solar cells. The Phase 3 program effort falls in five areas: (1) cell processing studies; (2) completion of the data base and impurity-performance modeling for n-base cells; (3) extension of p-base studies to include contaminants likely to be introduced during silicon production, refining or crystal growth; (4) anisotropy effects; and (5) a preliminary study of the permanence of impurity effects in silicon solar cells. The quarterly activities for this report focus on tasks (1), (3) and (4).

Hopkins, R. H.↗
NASA NTRS1979

Phase 2 of the array automated assembly task for the low cost solar array project

The process sequence for the fabrication of dendritic web silicon into solar panels was modified to include aluminum back surface field formation. Plasma etching was found to be a feasible technique for pre-diffusion cleaning of the web. Several contacting systems were studied. The total plated Pd-Ni system was not compatible with the process sequence; however, the evaporated TiPd-electroplated Cu system was shown stable under life testing. Ultrasonic bonding parameters were determined for various interconnect and contact metals but the yield of the process was not sufficiently high to use for module fabrication at this time. Over 400 solar cells were fabricated according to the modified sequence. No sub-process incompatibility was seen. These cells were used to fabricate four demonstration modules. A cost analysis of the modified process sequence resulted in a selling price of $0.75/peak watt.

Campbell, R. B.↗
NASA NTRS1978

Computer modeling of dendritic web growth processes and characterization of the material

High area throughput rate will be required for the economical production of silicon dendritic web for solar cells. Web width depends largely on the temperature distribution on the melt surface while growth speed is controlled by the dissipation of the latent heat of fusion. Thermal models were developed to investigate each of these aspects, and were used to engineer the design of laboratory equipment capable of producing crystals over 4 cm wide; growth speeds up to 10 cm/min were achieved. The web crystals were characterized by resistivity, lifetime and etch pit density data as well as by detailed solar cell I-V data. Solar cells ranged in efficiency from about 10 to 14.5% (AM-1) depending on growth conditions. Cells with lower efficiency displayed lowered bulk lifetime believed to be due to surface contamination.

Seidensticker, R. G.↗
NASA NTRS1978

Characterization of the effects of metallic impurities on silicon solar cell performance

The effects of controlled concentrations of secondary impurities (Al, C, Ca, Cr, Cu, Fe, Mg, Mn, Mo, Ta, Ti, V, Zn, and Zr), incorporated alone or in combinations into Czochralski and float zone crystals, on the performance of silicon solar cells were investigated. Impurity concentrations ranged from 10 to the 11th to 10 to the 17th/cu cm. Solar cells were fabricated by a conventional diffusion process and characterized by computer reduction of current-voltage data. The data suggest that performance loss primarily results from reduction of the base diffusion length. On the basis of this assumption, a first order analytic model which predicts cell performance as a function of impurity concentrations is developed. Calculated performance parameters are in good agreement with observation, except for some impurities, such as Fe, Cu and Ni, which degrade cells via recombination and defects in the junction space-charge region. N-base devices are less affected by impurities, although degradation mechanisms appear to be the same as in p-devices. There seems to be very limited interaction between impurities in multiply-doped cells.

Davis, J. R.↗
NASA NTRS1976

Silicon materials task of the low cost solar array project, part 2

Purity requirements for solar cell grade silicon material was developed and defined by evaluating the effects of specific impurities and impurity levels on the performance of silicon solar cells. Also, data was generated forming the basis for cost-tradeoff analyses of silicon solar cell material. Growth, evaluation, solar cell fabrication and testing was completed for the baseline boron-doped Czochralski material. Measurements indicate Cn and Mn seriously degrade cell performance, while neither Ni nor Cu produce any serious reduction in cell efficiency.

Hopkins, R. H.↗
NASA NTRS1976

Silicon solar cells from transition metal doped Czochralski and web crystals

The influence of metallic impurities on solar cell characteristics has been examined to establish the cost sensitive purity versus performance trade-offs. Solar cells were fabricated on 2 to 4 ohm-cm p-type substrates obtained by Czochralski and dendritic web growth processes. Controlled amounts of metallic impurities were introduced into the melt during growth and included Fe, Cr, Mn, Ni, Cu, Ti, V, Zr, Mg, Zn, and Al. Impurity concentrations in the crystals were determined using emission and mass spectrographic techniques and in some cases by neutron activation analysis. The solar cells were characterized by means of a computer program to curve-fit measured voltage-current data. The principal effect of the added impurities is a degradation of lifetime and diffusion length.