Davis, Kristopher Olan

DOE OSTI2024

Laser‐Sintered Silver Metallization for Silicon Heterojunction Photovoltaic Cells

Herein, a novel metallization technique is reported for crystalline silicon heterojunction (SHJ) solar cells in which silver (Ag) fingers are printed on the SHJ substrates by dispensing Ag nanoparticle‐based inks through a needle and then sintered with a continuous‐wave carbon dioxide (CO 2 ) laser. The impact of the Ag ink viscosity on the line quality and the line resistance is investigated on three Ag inks with different viscosities. Increasing ink viscosity yields higher Ag contact heights, larger aspect ratios, and lower line resistance values. The Ag line height increases from less than a micrometer to ≈18.62 ± 3.48 μm with the increasing viscosity. Photoluminescence imaging shows that the low‐resistance Ag metal contacts obtained do not result in any passivation damage of the SHJ substrate. This is because the wavelength of light emitted from the CO 2 laser (i.e., 10.6 μm) leads to optical absorption in the Ag, but this light is effectively transparent to the transparent conductive oxide film, amorphous silicon films, and crystalline silicon substrate. Bulk resistivity values as low as 6.5 μΩ cm are obtained for the laser‐sintered Ag contact and printed using the Ag ink with the highest viscosity in this work.

Mousumi, Jannatul Ferdous↗

DOE OSTI2020

Enabling Efficiencies > 22.5% with Metal Oxide Passivating Contacts using Low-Cost Spatial Atomic Layer Deposition (Final Technical Report)

In this project, the University of Central Florida (UCF) worked to both increase module efficiency and reduce manufacturing cost by driving demonstrated lab-scale passivating contact technology using materials and processes compatible with high-volume manufacturing for crystalline silicon (c-Si) photovoltaic (PV) cells. Passivating contacts have garnered significant attention in recent years. They provide a means of suppressing contact recombination, a loss mechanism that limits the performance of industrially relevant cell architectures like Al back surface field (Al-BSF) cells and passivated emitter and rear cells (PERC). Most of the development of passivating contact technology has focused on the use of doped amorphous silicon or doped polysilicon contacts, but both suffer from parasitic optical absorption amongst other issues. Our team developed fully transparent hole-selective heterojunctions, deposited using atomic layer deposition (ALD), and showed how they could be incorporated into c-Si PV cells. The team conducted experiments to understand the process-structure-property relationship of hole-selective oxides, surface passivation oxide materials, and transparent conductive oxides deposited by ALD, and use that understanding to reduce contact recombination, contact resistivity, and parasitic optical absorption within c-Si PV cells. Before getting into the details of the report, we would like to note that COVID-19 has made it more challenging to conduct experimental research at UCF. UCF has a number of mandatory policies in place to ensure social distancing, testing, and contact tracing are all carried out in day-to-day operations. Despite these challenges, we worked diligently to make progress on this project in a manner that was as safe as possible. Over the course of the project, the UCF team and its collaborators have made the following discoveries and developments.

14 SOLAR ENERGY↗