Search NASA⌕ Search

Engineering topics

Daw, M. S.

Publications and source records attributed to Daw, M. S..

Calculation of mode lifetimes in weakly anharmonic solids using self-consistent ensemble eigenstates of the Liouvillian

Recent schemes for the efficient calculation of vibrational mode frequencies and lifetimes in weakly anharmonic systems such as solid crystal structures have shown promise, with simple relationships being observed between low order moments of the Liouvillian and the observed lifetime. While only shown empirically, two parameters seemed sufficient to determine the lifetime to high accuracy over a large range of temperatures for a few simple low degree of freedom models and a Lennard–Jones solid. In this paper we analytically reproduce the numerically observed relationship using a few generally applicable assumptions about the density of states. This advance is made by studying the autocorrelation based on an “ensemble eigenstate” of the Liouvillian. We propose the use of this ensemble eigenstate as the basis for autocorrelations to simplify calculations in richer systems. Finally, an analysis is also performed of the relationship between canonical and microcanonical autocorrelation functions and a long standing error in the long time behavior of such functions originally presented by Sen, Sinkovits, and Chakravarti is corrected.

36 MATERIALS SCIENCE↗

Observations of Glide and Decomposition of a<101> Dislocations at High Temperatures in Ni-Al Single Crystals Deformed along the Hard Orientation

Ni-44at.% Al and Ni-50at.% single crystals were tested in compression in the hard (001) orientations. The dislocation processes and deformation behavior were studied as a function of temperature, strain and strain rate. A slip transition in NiAl occurs from alpha(111) slip to non-alphaaaaaaaaaaa9111) slip at intermediate temperatures. In Ni-50at.% Al single crystal, only alpha(010) dislocations are observed above the slip transition temperature. In contrast, alpha(101)(101) glide has been observed to control deformation beyond the slip transition temperature in Ni-44at.%Al. alpha(101) dislocations are observed primarily along both (111) directions in the glide plane. High-resolution transmission electron microscopy observations show that the core of the alpha(101) dislocations along these directions is decomposed into two alpha(010) dislocations, separated by a distance of approximately 2nm. The temperature window of stability for these alpha(101) dislocations depends upon the strain rate. At a strain rate of 1.4 x 10(exp -4)/s, lpha(101) dislocations are observed between 800 and 1000K. Complete decomposition of a alpha(101) dislocations into alpha(010) dislocations occurs beyond 1000K, leading to alpha(010) climb as the deformation mode at higher temperature. At lower strain rates, decomposition of a alpha(101) dislocations has been observed to occur along the edge orientation at temperatures below 1000K. Embedded-atom method calculations and experimental results indicate that alpha(101) dislocation have a large Peieris stress at low temperature. Based on the present microstructural observations and a survey of the literature with respect to vacancy content and diffusion in NiAl, a model is proposed for alpha(101)(101) glide in Ni-44at.%Al, and for the observed yield strength versus temperature behavior of Ni-Al alloys at intermediate and high temperatures.

Srinivasan, R.↗