Promoting Reversibility of Multielectron Redox in Alkali-Rich Sulfide Cathodes through Cryomilling
We report conventional cathodes for Li-ion batteries (LIBs) are reaching their theoretical capacity limits. One way to meet the growing demands for high-capacity LIBs is by developing so-called Li-rich cathode materials that greatly benefit from additional capacities from anionic moieties in the structure. Li-rich materials are intrinsically subject to higher degrees of (de)intercalation, leaving the particles more prone to fractures and thus rapid capacity fade. Alkali-rich LiNaFeS 2 reversibly cycles with capacities exceeding 300 mAh g -1 , but its capacity fades faster than an isostructural material Li 2 FeS 2 . Using synchrotron-based transmission X-ray microscopy (TXM), we demonstrate that the capacity fade of LiNaFeS 2 stems from particle fractures in the first charge cycle. We improve the cycling performance of LiNaFeS 2 by means of cryomilling, which enhances capacity retention at cycle 50 by 76%. Through crystallographic and morphological characterization techniques, we confirm that cryomilling not only decreases particle and crystallite size while increasing microstrain but also prevents particles from fracturing. Cryomilling is a powerful tool to engineer nanoscale battery materials, and TXM allows the direct observation of morphological changes of the particles, which can be leveraged to develop next-generation cathode materials for LIBs.