Laser Line Scan Characterization of Cavitation-Induced Erosion to SNS Mercury Target Vessels
The mercury-facing surfaces of the Spallation Neutron Source target vessel are damaged during operation by a phenomenon called cavitation-induced erosion. To date, erosion damage has caused leaks to develop in two target modules, which necessitated interruptions in operation to replace the target module. Samples are routinely removed from the beam entrance region of SNS targets after removal from service and analyzed to learn about the damage processes occurring in the targets during operation. A laser line scan system was used to produce point-cloud models of the target samples, which were used to calculate various erosion metrics and characterize the erosion damage to each sample. The scans revealed the maximum depth of erosion and the location where the maximum erosion occurred for each sample. The results quantified and illustrated the difference in erosion patterns between different target designs. Data from the scans also showed the maximum depth of erosion was greatly reduced at all locations examined in the SNS targets operated with gas injection. The data produced by these scans will be used to compare erosion damage to future targets in order to quantify the erosion in targets with different design features and operational histories.