NASA NTRS1990

Cation distributions on rapidly solidified cobalt ferrite

The cation distributions in two rapidly solidified cobalt ferrites have been determined using Moessbauer spectroscopy at 4.2 K in an 8-T magnetic field. The samples were obtained by gas atomization of a Co0-Fe2O3-P2O5 melt. The degree of cation disorder in both cases was greater than is obtainable by cooling unmelted cobalt ferrite. The more rapidly cooled sample exhibited a smaller departure from the equilibrium cation distribution than did the more slowly cooled sample. This result is explained on the basis of two competing effects of rapid solidification: high cooling rate of the solid, and large undercooling.

De Guire, Mark R.↗

NASA NTRS1990

Superconducting glass-ceramics in the Bi-Sr-Ca-Cu-O system

Differential thermal analysis, XRD, SEM, and resistivity measurements, have been used to study the recrystallization during various heat treatments of a Bi1.5SrCaCu2O(z) glass obtained by rapid quenching from the melt. Heating at 450 C formed the Bi(2+x)Sr(2-x)-CuO(z) solid solution designated 'R'. Between 765 and 845 C, R reacts slowly with the glass to form the 80 K superconductor Bi2(Sr,Ca)3Cu2O(z), together with CuO. Heating for 7 days at the higher temperature, followed by slow cooling, raised the temperature of zero resistance to 77 K.

De Guire, Mark R.↗

NASA NTRS1989

The cooling rate dependence of cation distributions in CoFe2O4

The room-temperature cation distributions in bulk CoFe2O4 samples, cooled at rates between less than 0.01 and about 1000 C/sec, have been determined using Mossbauer spectroscopy in an 80-kOe magnetic field. With increasing cooling rate, the quenched structure departs increasingly from the mostly ordered cation distribution ordinarily observed at room temperature. However, the cation disorder appears to saturate just short of a random distribution at very high cooling rates. These results are interpreted in terms of a simple relaxation model of cation redistribution kinetics. The disordered cation distributions should lead to increased magnetization and decreased coercivity in CoFe2O4.

De Guire, Mark R.↗

NASA NTRS1989

Gas atomization of cobalt ferrite-phosphate melts

XRD, Moessbauer spectroscopy, and EDXS have been used to characterize a rapidly-solidified (Co,Fe)3O4 spinel generated in a cobalt-iron-phosphate glass matrix by gas atomization of melts. Of the two compositions tested, that containing 20 mol pct P2O5 exhibited randomly-oriented ferrite crystallization whose growth appears to have been diffusion-controlled. Unlike the ferrite, in which the iron has both tetrahedral and octahedral coordination, the iron in the glassy matrix was primarily of distorted-octahedral coordination. Calculations indicate that the cooling rates obtained with oxide melts vary strongly with droplet size, but less strongly with melt temperature.

De Guire, Mark R.↗

NASA NTRS1987

Phase equilibria in the iron oxide-cobalt oxide-phosphorus oxide system

Two novel ternary compounds are noted in the present study of 1000 C solid-state equilibria in the Fe-Co-P-O system's Fe2O3-FePO4-Co3(Po4)2-CoO region: CoFe(PO4)O, which undergoes incongruent melting at 1130 C, and Co3Fe4(PO4)6, whose incongruent melting occurs at 1080 C. The liquidus behavior-related consequences of rapidly solidified cobalt ferrite formation from cobalt ferrite-phosphate melts are discussed with a view to spinel formation. It is suggested that quenching from within the spinel-plus-liquid region may furnish an alternative to quenching a homogeneous melt.