Austenite Formation and Manganese Partitioning during Double Soaking of an Ultralow Carbon Medium‐Manganese Steel

Double soaking (DS) is a thermal processing route intended to produce austenite–martensite microstructures in steels containing austenite‐stabilizing additions and consists of intercritical annealing (primary soaking), followed by heating and brief isothermal holding at an increased temperature (secondary soaking), and quenching. Herein, experimental dilatometry during DS of a medium‐manganese (Mn) steel with nominally 7 wt% Mn and an ultralow residual carbon concentration, in combination with phase‐field simulations of austenite formation during secondary soaking, is presented. The feasibility of maintaining heterogeneous Mn distributions during DS is demonstrated and insight is provided on the effects of the secondary soaking temperature and prior Mn distribution on the ferrite‐to‐austenite phase transformation during the secondary soaking portion of the DS treatment.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Quench and Partitioning Steels

Quench and Partitioning (Q&P) steels are produced by implementing a unique thermal history designed to produce microstructures that contain martensite, and potentially ferrite, along with significant amounts of retained austenite stabilized by high carbon contents. Carbon-stabilized austenite is obtained by carbon transfer from martensite into austenite after a controlled amount of martensite is introduced by judicious selection of a so-called quench temperature at which quenching below the martensite start temperature is interrupted. Following the quench interruption, during the partitioning step, the steel is either held at the quench temperature or brought to a higher temperature and held for a specific time, to stimulate carbon transfer from martensite to austenite, to decrease the carbon supersaturation in martensite and correspondingly stabilize the austenite by carbon enrichment. A final quench to room temperature may be associated with the transformation of a certain fraction of austenite into secondary or “fresh” martensite, which is usually undesirable. A review of the Q&P process is presented, including prediction of austenite retention, alloying effects on its stabilization, a mechanical properties survey, including tensile and local formability relevant to sheet steels for automotive applications, along with perspectives on reactions competing with carbon partitioning that may operate during partitioning.

Kang, Singon↗