Computationally-Guided ODS Refractory HEAs via Additive Manufacturing
This document is the final report for ARPA-E ULTIMATE project DE-AR0001422. To achieve higher efficiency turbine operation, the RTX Technology Research Center (RTRC) explored the use of additive manufacturing (AM) to produce test specimens of novel high entropy alloys (HEA) enhanced with oxide dispersion strengthening (ODS). HEAs, with multiple principal elements, offer a vast alloy design space rich with unique properties especially enhanced solid solution strengthening. ODS alloys historically are some of the best performing materials for high temperature applications. Leveraging AM enables near net shape part production and incorporation of ODS into the alloy. Density, melting temperature, and elevated temperature strength properties of several novel HEA compositions were found to meet or exceed program targets; however, obtaining sufficient room temperature ductility in these alloys proved challenging. In order to obtain an alloy with sufficient ductility, the team explored more conventional refractory alloy compositions, focusing on a niobium based alloy. This inherently ductile alloy also satisfied program metrics for cost, density, and fracture toughness. Results showed the oxide dispersions increased high temperature strength, and improved creep resistance compared to the conventional alloy, though the program creep metric was not met. Further tuning of the alloy chemistry, and optimization of the oxide dispersion, is likely required to improve creep resistance.