NASA NTRS2003

Survivability of Affordable High Temperature Polymer Matrix Composites for Propulsion Engine Components

PMR-type polyimides are regarded as state of the art high temperature polymers, due to their excellent thermo-mechanical properties and thermo-oxidative stability. One of their drawbacks, however is the inability to process them using cost-effective processing methods such as Resin Transfer Molding (RTM) and Resin Film Infusion (RFI). Development of low viscosity, high temperature polymers has been the subject of intense research. Recently, a new generation of low viscosity polyimides were synthesized by the introduction of twisted biphenyl or binapthyl groups into the backbone. This report details the progress for Year 1, which has involved acquiring samples and initiating Phases I and II of the proposed research. Specifically, studies of the process-property relationships of a series of polymers using oligomers based on 2,3,3' ,4'-biphenyltertracarboxylic dianhydride (PBDA) and a mixture of a diamine, BAX and a triamine, 1,3,5-Tris (4-aminophenoxybenzene), TAB, where the amount of TAB was varied have been initiated. The sample containing 10 percent TAB possesses a slightly higher degree of crystalline order versus that of the 20 percent TAB sample, based on x-ray diffraction studies of the b-staged oligomers. Both systems lose all of the crystalline order upon curing, however. The chemorheology has been studied as a function of the TAB content. While the magnitude of the viscosity is essentially the same for both systems, the cure kinetics of the 10 percent TAB system is faster than that for the 20 percent TAB system. The sample exhibits a melting-recrystallization-remelting behavior before the crosslinking commences. Correlation of other kinetic parameters, such as the activation energies for curing, the Tg and mechanical properties to the structure of these systems is underway. Future studies will involve characterization of mechanical and thermal properties of the pure resins and the fabrication of fiber reinforced composites using these materials.

Dean, Derrick↗

NASA NTRS2003

Structural Evolution and Mechanical Properties of PMR-15/Layered Silicate Nanocomposites

In the first year of this research, we successfully synthesized and characterized Polymer/ Layered Silicate nanocomposite using the polyimide PMR-15 as the polymer and several layered silicate nanoparticles. We have scaled up the process to allow fabrication of monoliths using these nanocomposites. The morphology of these systems was found to evolve during processing to an exfoliated structure for one system and intercalated for the rest. Correlation with Transmission Electron Microscopy studies is underway. Dynamic mechanical analysis (DMA) results showed a significant increase in the thermomechanical properties (E' and E'') of 2.5 wt.% clay loaded nanocomposites in comparison to the neat polyimide. Increasing the clay loading to 5 wt.% decreased these properties. Higher glass transition temperatures were observed for 2.5 wt.% nanocomposites compared to the neat polyimide. A lower coefficient of thermal expansion was observed only for the PGV/PMR-15 nanocomposite. An improvement in the flexural properties (modulus, strength and elongation) was observed for the 2.5 wt.% nanocomposite but not for the 5 wt.% nanocomposites. The improved barrier properties polymer/ silicate nanocomposites suggest that moisture uptake should be decreased for PMR-15 nanocomposites. The results of some recent experiments to examine delineate the ability of the silicate nanoparticles in improving the hydrolytic degradation of PMR-15 will be discussed.

Campbell, Sandi↗

NASA NTRS2002

Viscoelastic and Mechanical Properties of Thermoset PMR-type Polyimide-Clay Nanocomposites

High temperature thermoset polyimide-clay nanocomposites were prepared by blending 2.5 and 5 wt% of an unmodified Na(+-) montmorillonite (PGV) and two organically modified FGV (PGVCl0COOH, PGVC12) with a methanol solution of PMR-15 precursor. The methanol facilitated the dispersal of the unmodified clay. Dynamic mechanical analysis results showed a significant increase in the thermomechanical properties (E' and E") of 2.5 wt% clay loaded nanocomposites in comparison with the neat polyimide. Higher glass transition temperatures were observed for 2.5 wt% nanocomposites compared to the neat polyimide. Flexural properties measurements for the 2.5 wt% nanocomposites showed a significant improvement in the modulus and strength, with no loss in elongation. This trend was not observed for the 5 wt% nanocomposites. An improvement in the CTE was observed for the PGV/PMR-15 nanocomposites, while a decrease was observed for the organically modified samples. This was attributed to potential variations in the interface caused by modifier degradation.

Abdalla, Mohamed O.↗

NASA NTRS2001

Polyimide Based Nanocomposites for Affordable Space Transport

In setting forth its strategic plan, NASA has indicated that low-cost access to space is the key to unleashing the commercial potential of space and greatly expanding space research and exploration. The development of advanced materials will be an enabling technology for this quest for low-cost space access. In this research program, we are attempting to address the need for new advanced materials by developing high-performance nanodispersed inorganic/organic and organic/organic polyimide composites utilizing specific interactions. Our goal is to systematically manipulate these interactions and investigate the resulting processing morphology-property relationships. Specifically, we will investigate three main parameters on these relationships. These include (1) the type of polyimide; (2) the structure of the inorganic nanoparticle being used; and (3) manipulation of the interfacial energy. During the first year of this effort, we have demonstrated the successful synthesis of PMR-15/layered silicate nanocomposites. Morphological studies indicate that exfoliated structures were obtained in most instances, with a mixture of exfoliated and intercalated structures being observed also. Significant enhancements of the onset of decomposition were obtained by varying the strength of the interaction between the nanoparticle and the polymer. Varying the amount of a specific nanoparticle also affected the decomposition temperatures. A slight catalytic effect of the nanoparticles on both the imidization and crosslinking reaction has been observed and will be presented. In addition, incorporation of the nanoparticles was found to increase the glass transition temperature and slightly broaden the breadth of this relaxation.

Dean, Derrick↗