Engineering topics
Publications and source records attributed to Decarlo, J. L..
Report describes experiments in directional solidification of eutectic Mn/Bi in magnetic field. Study determines whether effects of gravitationally-induced convection reduced or eliminated by magnetic field. Morphological, thermal, and magnetic analyses done on samples grown at various speeds and various applied strengths. Magnetic effects similar to those of low gravity.
Off-eutectic compositions of Bi-Mn were directionally solidified in applied transverse magnetic fields up to 3 kG, to determine the effects on thermal and solutal convection. Plane front directional solidification of eutectic and near-eutectic Bi-Mn results in a two-phase rodlike morphology consisting of ferromagnetic MnBi rods in a Bi solid solution matrix. Compositions of either side of the eutectic were studied in growth orientations vertically up and down. Temperature gradient was monitored during growth by means of an in-situ thermocouple. For Bi-rich compositions, the magnetic field appeared to increase mixing as determined from thermal, morphological, chemical, and magnetic analyses. For Mn-rich compositions, morphological and chemical analyses suggest some reduction in mixing due to application of the magnetic force. The capability for carrying out directional solidification of Bi-Mn in high longitudinal magnetic fields was established.
Off-eutectic compositions of Bi-Mn were directionally solidified in applied transverse magnetic fields up to 3 kG to determine the effects on thermal and solutal convection. For Bi-rich compositions, the magnetic field appeared to increase mixing as determined from thermal, morphological, chemical and magnetic analyses. For Mn-rich compositions morphological and chemical analyses suggest some reduction in mixing due to application of the magnetic field. Conductivity gradients in the melt are suggested as a possible mechanism for the observed results.
Application of 3-kG magnetic field reduces thermal and solutal convection in Bi/MnBi melt in Bridgman-Stockbarger (moving-vertical-thermalgradient) furnace operating in normal gravitational field. Resulting Bi/MnBi alloy samples had properties similar to samples grown under nearly zero gravity. New technique proves useful in growing more uniform, defect-free semiconductor materials from such other electrically conductive melts.
Samples of eutectic Bi/Mn alloy were directionally solidified in the presence of a transverse magnetic field to determine if gravity-induced convection effects could be reduced or eliminated. The microstructure of Bi/MnBi is characterized by a regular, aligned-rod eutectic morphology that is sensitive to growth conditions. This, combined with ferromagnetism of one of the components, MnBi, can be used to eliminate whether convection effects are significant enough to be effected by the presence of a static, homogeneous, magnetic field.
Samples of rod eutectics Bi/MnBi were directionally solidified in a growth-up Bridgman-Stockbarger configuration in the presence of a transverse magnetic field up to 3 kg to determine whether gravity-driven convective effects could be reduced or eliminated. The experiments were carried out over a range of furnace velocities, V, of 0.2 to 50 cm per hour with a thermal gradient at the liquid-solid interface of 100 C/cm and 150 C/cm. Morphological, thermal and magnetic analyses were carried out on samples grown with and without an applied magnetic field. For samples grown at V greater than 3 cm per hour in a transverse magnetic field, reduced mean rod diameter and interrod spacing occurred as well as undercooling and increased coercive strength. The data agreed with that obtained for low-g growth at 50 cm per hour and 30 cm per hour.