Engineering topics
Publications and source records attributed to Dede, Stefania.
With the installation of the Mark-IV target at LANSCE in 2022 significant changes of the beam-related backgrounds at DANCE are observed. DANCE is located at flight path 14 (FP-14) in the experimental area 2 (ER-2) at LANSCE. This new background is so severe that the array is not operational for several microseconds after the protons hit the spallation target (Figures 1 - 3).
Combustion reactions in europium nitrate – acetylacetone – 2-methoxyethanol solutions and gels were investigated to produce europium (III) oxide (Eu 2 O 3 ) nanocrystalline materials and thin films. Thermal analyses of solutions indicated that the 2-methoxyethanol solvent also acts as a fuel in the absence of acetylacetone. Adding acetylacetone increases the overall heat of the reaction. Thermal analysis results revealed that the slow oxidation of unburned hydrocarbon residues follows the primary combustion reaction. Time-temperature profile measurements of the bulk combustion synthesis process in air and nitrogen atmospheres enabled the extraction of the maximum reaction temperature and the heating and cooling rates in the combustion zone. Several direct correlations exist between measured combustion parameters and the phase composition of the products. Combustion in air results in mixed-phase cubic and monoclinic nanocrystalline Eu 2 O 3 . Increasing the acetylacetone concentration in solutions increases the synthesis temperature and decreases the quantity of cubic Eu 2 O 3 . Here, the reaction of solutions in a nitrogen atmosphere or diluted with Eu 2 O 3 provides control of the product phase composition and reduces the quantity of the monoclinic phase. Transmission electron microscopy imaging shows that the Eu 2 O 3 end products are highly porous aggregates of nanocrystalline particles. Electrospraying of reactive solutions onto different substrates followed by short annealing makes the preparation of Eu 2 O 3 materials with diverse morphologies possible.
A simple and efficient target preparation method is developed combining spin coating and solution combustion synthesis. Multiple smooth and uniform UO 2 targets have been prepared using this method on a variety of backings (aluminium, carbon, silicon) used in nuclear physics experiments. The thicknesses of the targets can be precisely tuned by changing the number of coatings within the range of ~50-1000 µm/cm 2 . These targets are highly uniform (<5% deviation), robust, and remain strongly adherent to their backings even after being irradiated by high doses (10 17 ions/ cm 2 ) of 1.7 MeV Ar 2+ ions.
Combustion synthesis is used to prepare thin UO 2 films on aluminum alloy substrates. This simple preparation method involves electrospraying uranyl nitrate + acetylacetone + 2-methoxyethanol solution on the substrate, followed by a short annealing at 350 or 550 °C. The irradiation of films with a 40 Ar 2+ ion beam (energy of 1.7 MeV and fluences of 7.7 × 10 16 and 1.3 × 10 17 ions/cm 2 ) is conducted to investigate irradiation-induced restructuring processes. High-resolution transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) investigations show that the annealing temperature significantly influences the crystallinity and stability of materials during irradiation. A small amount of Mg in the alloy substrate diffuses into the amorphous Al 2 O 3 interfacial layer between the film and the substrate. Local thermal spikes from the incoming ions facilitate the irradiation-induced mixing of immiscible Al 2 O 3 and UO 2 for the materials prepared at 350 °C. This mass diffusion produces relatively large cavities at the interface. Selective diffusion of a more significant amount of Mg for the materials prepared at 550 °C suppresses the mixing of the Al 2 O 3 interlayer with the film but forms Mg y U 1–y O 2±x solid solutions during irradiation. Local thermal heating triggers the precipitation of a discontinuous crystalline MgO layer close to the film surface. As a result, the enhanced and selective diffusion of Mg into the film makes the materials prepared at 550 °C more robust and mechanically stable than those prepared at 350 °C.