Hierarchical microstructure of Yb-filled skutterudites through ultrasonically atomized spherical powders for enhanced thermoelectric performance
Hierarchical microstructures are widely explored as a strategy to reduce lattice thermal conductivity in thermoelectric materials while preserving favorable electronic transport. Here we demonstrate that ultrasonic atomization of precursor powders provides an intrinsic pathway to generate such architectures in n-type Yb0.3Co4Sb12 skutterudites. Materials were synthesized by both conventional sealed-ampoule and ultrasonic atomization routes, each yielding essentially single-phase skutterudite after densification. However, the atomized spherical powders undergo a distinct reaction-driven microstructural evolution during thermal treatment prior to densification. Electron microscopy reveals that the skutterudite phase within the particles induces swelling, cracking, and fragmentation of the droplets before consolidation. Multimodal structural and microstructural characterizations show that densification of these fragmented powders produces a hierarchical microstructure consisting of submicron grains, micrometer-scale faceted crystallites, and powder-derived domains separated by oxide-decorated boundaries. Comprehensive thermoelectric transport measurements evidence that this multiscale architecture lowers the lattice thermal conductivity while maintaining favorable electronic transport, leading to an average ~10% enhancement in the thermoelectric figure of merit. Complementary 121Sb Mössbauer spectroscopy further indicates lattice softening in the atomized material. These results demonstrate that ultrasonic atomization provides an effective route to engineer hierarchical microstructures in skutterudite thermoelectrics and offers a promising strategy for tailoring thermal transport in energy-conversion materials.