NASA NTRS2007

Thermal Conductivity of Polyimide/Carbon Nanofiller Blends

In efforts to improve the thermal conductivity (TC) of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

Ghose, S.↗

NASA NTRS2006

Thermal Conductivity of Polyimide/Carbon Nanofiller Blends

Ultem(TM) was mixed with three different carbon-based nanofillers in efforts to increase the thermal conductivity of the polymer. After initial mixing, the nanocomposites were extruded or processed via the Laboratory Mixing Molder (LMM) process. High resolution scanning electron microscopy (HRSEM) revealed significant alignment of the nanofillers in the extruded samples. Thermal conductivity measurements were made both in the direction and perpendicular to the direction of alignment of nanofillers as well as for unaligned samples. It was found that the largest improvement in thermal conductivity was achieved in the case of aligned samples when the measurement was performed in the direction of alignment. Unaligned samples also showed a significant improvement in thermal conductivity and may be useful in applications when it is not possible to align the nanofiller. However the improvements in thermal conductivity did not approach those expected based on a rule of mixtures. This is likely due to poor phonon transfer through the matrix.

Delozier, D. M.↗

NASA NTRS2006

Thermal Conductivity of Polyimide/Nanofiller Blends

In efforts to improve the thermal conductivity of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

Ghose, S.↗

NASA NTRS2006

Preparation and Properties of Nanocomposites Prepared From Shortened, Functionalized Single-Walled Carbon Nanotubes

As part of a continuing materials development activity, low color space environmentally stable polymeric materials that possess sufficient electrical conductivity for electrostatic charge dissipation (ESD) have been investigated. One method of incorporating sufficient electrical conductivity for ESD without detrimental effects on other polymer properties of interest (i.e., optical and thermo-optical) is through the incorporation of single-walled carbon nanotubes (SWNTs). However, SWNTs are difficult to fully disperse in the polymer matrix. One means of improving dispersion is by shortening and functionalizing SWNTs. While this improves dispersion, other properties (i.e., electrical) of the SWNTs can be affected which can in turn alter the final nanocomposite properties. Additionally, functionalization of the polymer matrix can also influence nanocomposite properties obtained from shortened, functionalized SWNTs. The preparation and characterization of nanocomposites fabricated from a polyimide, both functionalized and unfunctionalized, and shortened, functionalized SWNTs will be presented.

Smith, J. G., Jr.↗

NASA NTRS2006

Thermal Conductivity of Ultem(TradeMark)/Carbon Nanofiller Blends

In an effort to improve polymer thermal conductivity (TC), Ultem(TradeMark) 1000 was compounded with nano-fillers of carbon allotropes. Ultem(TradeMark) 1000 was selected since it is both solution and melt processable. As-received and modified multiwalled carbon nanotubes (MWCNTs), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. MWCNTs were modified by functionalizing the surface through oxidization with concentrated acids, mixing with an alkyl bromide, and addition of alkyl and phosphorus compounds after initial treatment with n-butyl lithium. Functionalization was performed to improve the TC compatibility between the resin and MWCNTs. It was postulated that this may provide an improved interface between the MWCNT and the polymer which would result in enhanced TC. The nano-fillers were mixed with Ultem(TradeMark) 1000 in the melt and in solution at concentrations ranging from 5 to 40 wt%. Ribbons were extruded from the blends to form samples where the nano-fillers were aligned to some degree in the extrusion direction. Samples were also fabricated by compression molding resulting in random orientation of the nano-fillers. Thermal properties of the samples were evaluated by Differential Scanning Calorimetry (DSC) and Thermal Gravimetric Analyzer (TGA). Tensile properties of aligned samples were determined at room temperature. The specimens were cut from the ribbons in the extrusion direction; hence the nano-fillers are somewhat aligned in the direction of stress. Typically it was observed that melt mixed samples exhibited superior mechanical properties compared to solution mixed samples. As expected, increased filler loading led to increased modulus and decreased elongation with respect to the neat polymer. The degree of dispersion and alignment of the nano-fillers was determined by high-resolution scanning electron microscopy (HRSEM). HRSEM of the ribbons revealed that the MWCNTs and CNFs were predominantly aligned in the flow direction. The TC of the samples was measured using a Nanoflash(TradeMark) instrument. Since the MWCNTs and CNF are anisotropic, the TC was expected to be different in the longitudinal (parallel to the nanotube and fiber axis) and transverse (perpendicular to the nanotube and fiber axis) directions. The extruded ribbons provided samples for transverse TC measurements. However, to determine the TC in the longitudinal direction, the ribbons needed to be stacked and molded under 1.7 MPa and 270 C. Samples were then obtained by cutting the molded block with a diamond saw. The largest TC improvement was achieved for aligned samples when the measurement was performed in the direction of MWCNT and CNF alignment (i.e. longitudinal axis). Unaligned samples also showed a significant improvement in TC and may be potentially useful in applications when it is not possible to align the nano-filler. The results of this study will be presented.

Ghose, S.↗

NASA NTRS2004

Polyimide/Carbon Nanotube Composite Films for Electrostatic Charge Mitigation

Low color, space environmentally durable polymeric films with sufficient electrical conductivity to mitigate electrostatic charge build-up have been under investigation as part of a materials development activity. In the work described herein, single-walled carbon nanotubes (SWNT) solutions were dispersed in solutions of a novel ionomer in N,N-dimethylacetamide resulting in homogenous suspensions or quasi-solutions. The ionomer was used to aid in the dispersal of SWNTs in to a soluble, low color space environmentally durable polyimide. The use of the ionomer as a dispersant enabled the nanotubes to be dispersed at loading levels up to 3 weight % in a polyimide solution without visual agglomeration. The films were further characterized for their electrical and mechanical properties.

Delozier, D. M.↗

NASA NTRS2003

Polyimide Nanocomposites Prepared from High-Temperature, Reduced Charge Organoclays

Montmorillonite clays modified with the dihydrochloride salt of 1,3-bis(3-aminophenoxy)benzene (APB) were used in the preparation of polyimide/organoclay hybrid films. Organoclays with varying surface charge based upon APB were prepared and examined for their dispersion behavior in the polymer matrix. High molecular weight poly(amide acid) solutions were prepared in the presence of the organoclays. Films were cast and subsequently heated to 300C to cause imidization. The resulting nanocomposite films, containing 3 wt% of organoclay, were characterized by transmission electron microscopy and X-ray diffraction. The clay's cation exchange capacity (CEC) played a key role in determining the extent of dispersion in the polyimide matrix. Considerable dispersion was observed in some of the nanocomposite films. The most effective organoclay was found to have a CEC of 0.70 meq/g. Nanocomposite films prepared with 3-8 wt% of this organoclay were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), and thin-film tensile testing. High levels of clay dispersion could be achieved even at the higher clay loadings. Results from mechanical testing revealed that while the moduli of the nanocomposites increased with increasing clay loadings, both strength and elongation decreased.

Delozier, D. M.↗

NASA NTRS2003

Preparation and Characterization of Space Durable Polymer Nanocomposite Films from Functionalized Carbon Nanotubes

Low color, flexible, space durable polyimide films with inherent, robust electrical conductivity have been under investigation as part of a continuing materials development activity for future NASA space missions involving Gossamer structures. Electrical conductivity is needed in these films to dissipate electrostatic charge build-up that occurs due to the orbital environment. One method of imparting conductivity is through the use of single walled carbon nanotubes (SWNTs). However, the incompatibility and insolubility of the SWNTs severely hampers their dispersion in polymeric matrices. In an attempt to improve their dispersability, SWNTs were functionalized by the reaction with an alkyl hydrazone. After this functionalization, the SWNTs were soluble in select solvents and dispersed more readily in the polymer matrix. The functionalized SWNTs were characterized by Raman spectroscopy and thermogravimetric analysis (TGA). The functionalized nanotubes were dispersed in the bulk of the films using a solution technique. The functionalized nanotubes were also applied to the surface of polyimide films using a spray coating technique. The resultant polyimide nanocomposite films were evaluated for nanotube dispersion, electrical conductivity, mechanical, and optical properties and compared with previously prepared polyimide-SWNT samples to assess the effects of SWNT functionalization.

Delozier, D. M.↗

NASA NTRS2002

Preparation and Characterization of Polyimide/Organoclay Nanocomposites

Organically modified montmorrrillonite clay, containing a long chain aliphatic quarternary ammonium cation, was used to prepare polyimide/organoclay hybrids. Several approaches were examined in an attempt to achieve fully exfoliated nanocomposites. These included simple mixing of the clay in a pre-made high molecular weight poly(amide acid) solution; simple mixing followed by sonication of the organoclay/poly(amide acid) solutions; and the preparation of high molecular weight poly(amide acid)s in the presence of the organoclay dispersed in N-methyl-2-pyrrolidinone (NMP). The best results were obtained using the in-situ polymerization approach. The resulting nanocomposite films (both amide acid and imide), containing 3-8% by weight of organoclay, were characterized by differential scanning calorimetry (DSC), dynamic thermogravimetric analysis (TGA), transmission electron microscopy (TEM), X-ray diffraction (XRD), and thin film tensile properties. A significant degree of dispersion was observed in the nanocomposite films of the amide acid and the imide. After thermal treatment of amide acid films to effect imidization, in both air and nitrogen, the films were visually darker than control films without clay and the level of clay dispersion appeared to have decreased. In the latter case, the separation between the layers of the clay decreased to a spacing less than that present in the original organoclay. These observations suggest that thermal degradation of the aliphatic quarternary ammonium cation occurred likely during thermal treatment to effect imidization and solvent removal. These thermal degradation effects were less pronounced when thermal treatment was performed under nitrogen. The polyimide/organoclay hybrid films exhibited higher room temperature tensile moduli and lower strength and elongation to break than the control films.

Delozier, D. M.↗