NASA NTRS2001

Addition Polyimides from Non-Mutagenic Diamines

Studies were conducted to find an acceptable non-mutagenic diamine to replace 4,4'-methylenedianiline (MDA), a suspect carcinogen, which is currently being used in PMR-15 polyimide applications. Several diamines containing fluorine and trifluoromethyl substituent groups were synthesized. The diamines were polymerized with the dimethyl ester of 3,3',4,4'-benzophenone tetracarboxylic acid (BTDE), using the monomethyl ester of nadic acid (NE) as an endcap. The effect of diamine structure on rheological properties, glass transition temperature, and thermo-oxidative stability was investigated. Unidirectional laminates were fabricated from selected resins, using carbon fiber as the reinforcement. The results indicate that some of the diamines containing trifluoromethyl groups are non-mutagenic, and have potential to replace MDA in PMR polyimides for long-term applications at temperatures up to 300 C.

Delvigs, Peter↗

NASA NTRS1994

Structure-property relationships in addition polyimides. 1: Resins from four-ring aromatic diamines containing carbonyl and methylene groups

In an effort to improve the processing characteristics of addition-type polyimide resins the use of flexibilized four-ring aromatic diamine moieties was investigated. A series of 12 diamines containing carbonyl and methylene, as well as oxo and thio bridging groups, was synthesized. The diamines were polymerized with the dimethyl ester of 3.3', 4.4' - benzophenonetetracarboxylic acid (BTDE), using the monomethyl ester of nadic acid (NE) as an end-cap. The effect of diamine structure on the solubility and rheological properties during cure was determined. This paper also describes the effect of diamine structure and formulated molecular weight on the glass transition temperature and thermo-oxidative stability at elevated temperatures after various post-cure regimes. The results indicate that polyimides from some of the diamines containing methylene connecting groups have potential as matrix resins for long-term applications at temperatures up to 300 C.

Delvigs, Peter↗

NASA NTRS1991

Vinyl capped addition polyimides

Polyimide resins (PMR) are generally useful where high strength and temperature capabilities are required (at temperatures up to about 700 F). Polyimide resins are particularly useful in applications such as jet engine compressor components, for example, blades, vanes, air seals, air splitters, and engine casing parts. Aromatic vinyl capped addition polyimides are obtained by reacting a diamine, an ester of tetracarboxylic acid, and an aromatic vinyl compound. Low void materials with improved oxidative stability when exposed to 700 F air may be fabricated as fiber reinforced high molecular weight capped polyimide composites. The aromatic vinyl capped polyimides are provided with a more aromatic nature and are more thermally stable than highly aliphatic, norbornenyl-type end-capped polyimides employed in PMR resins. The substitution of aromatic vinyl end-caps for norbornenyl end-caps in addition polyimides results in polymers with improved oxidative stability.

Vannucci, Raymond D.↗

NASA NTRS1990

Vinyl capped addition polyimides

Polyimide resins having improved thermo-oxidative stability are provided having aromatic vinyl end-caps. The polyimides are prepared by the reaction of a mixture of monomers comprising (1) a diamine, (2) an ester of tetracarboxylic acid and (3) an aromatic vinyl compound in a molar ratio of 1:2:3 of n: (n + 1):2 when the aromatic vinyl compound contains nitrogen and in a ratio of (n + 1):n:2 when the aromatic vinyl compound does not contain nitrogen, wherein n ranges from about 5 to about 20.

Vannucci, Raymond D.↗

NASA NTRS1989

Graphite/polyimide composites with improved toughness

Studies were performed to determine the toughness characteristics of composites prepared from modified addition-type polyimides, using Celion 6000 graphite fiber as the reinforcement. The polyimides were prepared from aromatic diamines containing flexibilizing ether connecting groups. The composite flexural and short beam shear strengths were determined at room temperature and elevated temperatures. Composite toughness was evaluated using 10 deg off axis tensile tests and double cantilever beam fracture tests at room temperature. The effects of the flexibilized resin structure on composite mechanical properties, toughness characteristics, and thermo-oxidative stability are discussed.

Delvigs, Peter↗