Engineering topics

Demasi, J. T.

Publications and source records attributed to Demasi, J. T..

6 records

NASA NTRS1987

Thermal barrier coating life prediction model development

The objectives of this program are to increase understanding of thermal barrier coating (TBC) degradation and failure modes, to generate quantitative ceramic failure life data under cyclic thermal conditions which simulate those encountered in gas turbine engine service, and to develop an analytical methodology for prediction of coating life in the engine. Observations of degradation and failure modes in plasma deposited ceramic indicate that spallation failure results from progressive cracking of the ceramic parallel to and adjacent to, but not coincident with the metal-ceramic interface.

Demasi, J. T.↗

NASA NTRS1986

Thermal barrier coating life prediction model development

A methodology is established to predict thermal barrier coating life in a environment similar to that experienced by gas turbine airfoils. Experiments were conducted to determine failure modes of the thermal barrier coating. Analytical studies were employed to derive a life prediction model. A review of experimental and flight service components as well as laboratory post evaluations indicates that the predominant mode of TBC failure involves thermomechanical spallation of the ceramic coating layer. This ceramic spallation involves the formation of a dominant crack in the ceramic coating parallel to and closely adjacent to the topologically complex metal ceramic interface. This mechanical failure mode clearly is influenced by thermal exposure effects as shown in experiments conducted to study thermal pre-exposure and thermal cycle-rate effects. The preliminary life prediction model developed focuses on the two major damage modes identified in the critical experiments tasks. The first of these involves a mechanical driving force, resulting from cyclic strains and stresses caused by thermally induced and externally imposed mechanical loads. The second is an environmental driving force based on experimental results, and is believed to be related to bond coat oxidation. It is also believed that the growth of this oxide scale influences the intensity of the mechanical driving force.

Demasi, J. T.↗

NASA NTRS1986

Thermal barrier coating life prediction model development

The objective of this program is to establish a methodology to predict Thermal Barrier Coating (TBC) life on gas turbine engine components. The approach involves experimental life measurement coupled with analytical modeling of relevant degradation modes. The coating being studied is a flight qualified two layer system, designated PWA 264, consisting of a nominal ten mil layer of seven percent yttria partially stabilized zirconia plasma deposited over a nominal five mil layer of low pressure plasma deposited NiCoCrAlY. Thermal barrier coating degradation modes being investigated include: thermomechanical fatigue, oxidation, erosion, hot corrosion, and foreign object damage.

Demasi, J. T.↗

NASA NTRS1985

Thermal barrier coating life prediction model development

A methodology was established to predict thermal barrier coating life in an environment simulative of that experienced by gas turbine airfoils. Specifically, work is being conducted to determine failure modes of thermal barrier coatings in the aircraft engine environment. Analytical studies coupled with appropriate physical and mechanical property determinations are being employed to derive coating life prediction model(s) on the important failure mode(s). An initial review of experimental and flight service components indicates that the predominant mode of TBC failure involves thermomechanical spallation of the ceramic coating layer. This ceramic spallation involves the formation of a dominant crack in the ceramic coating parallel to and closely adjacent to the metal-ceramic interface. Initial results from a laboratory test program designed to study the influence of various driving forces such as temperature, thermal cycle frequency, environment, and coating thickness, on ceramic coating spalling life suggest that bond coat oxidation damage at the metal-ceramic interface contributes significantly to thermomechanical cracking in the ceramic layer. Low cycle rate furnace testing in air and in argon clearly shows a dramatic increase of spalling life in the non-oxidizing environments.

Sheffler, K. D.↗

NASA NTRS1985

Thermal barrier coating life prediction model development

The objective is to develop an integrated life prediction model accounting for all potential life-limiting thermal barrier coating (TBC) degradation and failure modes, including spallation resulting from cyclic thermal stress, oxidation degradation, hot corrosion, erosion and foreign object damage.

Demasi, J. T.↗

NASA NTRS1985

Mechanisms of thermal barrier coating degradation and failure

The objectives and initial results of a Thermal Barrier Coating (TBC) Life Prediction Model Development Program are described. The goals of this program are to: identify and understand TBC failure modes; generate quantitative TBC life data; and develop and verify a TBC life prediction model. The coating being studied is a two layer thermal barrier system incorporating a nominal ten mil outer layer of seven percent yttria partially stabilized zirconia plasma deposited over an inner layer of highly oxidation resistant low pressure plasma sprayed NiCrAlY bond coating. This coating currently is in flight service on turbine vane platforms in the JT-9D and PW2037 engines and is bill-of- material on turbine vane airfoils in the advanced PW4000 and IAE V2500 engines. Effort currently is in progress on the first task, which involves the identification and understanding of TBC failures. Five modes of coating damage were considered: thermomechanical ceramic failure; oxidative bond coat failure; hot corrosion; foreign object damage (FOD); and erosion.

Demasi, J. T.↗