Engineering Scale Drying of Aluminum-Clad Spent Nuclear Fuel: Experiment Report
Engineering-scale tests were performed to evaluate the relative effectiveness of forced gas and vacuum-drying processes on aluminum-clad spent nuclear fuel (ASNF) in preparation for extended dry storage. Drying models were developed to improve confidence in the likely range of conditions at the start of dry storage and to understand the factors most significant to each process. Testing was performed at the Holtec International Forced Helium Dehydration training facility in Camden, New Jersey, by students from the University of South Carolina in collaboration with Idaho National Laboratory. A full-size Type 1a basket, with a full-diameter vessel configuration (based on the Department of Energy standardized canister design), was used in combination with a 10 assembly surrogate ASNF arrangement to provide a proxy for geometry. A resistance heater incorporated in one assembly simulated the influence of 100 W decay heat. This instrumented chamber allowed testing of the removal of bulk water, physisorbed water, and chemisorbed water over a range of operating parameters with either drying process. Thick oxide films were grown on aluminum test plates to mimic the ASNF surface chemistry. These one-use test plates were housed within select assemblies during drying. Post-test analysis of these plates gave a measure of the moisture removed during each test, which was compared to a control. Instrumentation provided detailed thermal, humidity, and gas or pressure data relevant to each test. Model simulations generally compared favorably to instrument data for the tests. While both processes were able to remove bulk water, removal of chemisorbed water was shown to depend heavily on local temperature. To the disadvantage of vacuum drying, operations approaching or exceeding 220°C achieved consistently more dehydroxylation.