Detchprohm, Theeradetch

Publications and source records attributed to Detchprohm, Theeradetch.

10 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Breakdown characteristics analysis of kV-class vertical GaN PIN rectifiers by wafer-level sub-bandgap photoluminescence mapping

This work reports analysis of the reverse-bias breakdown characteristics of homojunction gallium nitride (GaN) p–i–n (PIN) rectifiers fabricated on bulk GaN substrates. Sub-bandgap photoluminescence mapping at room temperature as a contactless, non-destructive wafer inspection method was performed to analyze the impact of material properties on grown GaN PIN diodes and to study the correlation between defect types and breakdown characteristics of vertical GaN PIN rectifiers. Under the sub-bandgap excitation, yellow luminescence is dominant. The premature breakdown characteristics of the fabricated kV-class vertical GaN PIN rectifiers with nitrogen-implanted floating guard rings are found to be associated with material defects and deep level complexes. Photoluminescence mapping has demonstrated its effectiveness in quantitative analysis of dislocations and other types of defects.

42 ENGINEERING↗
DOE OSTI2023

1.2-kV Vertical GaN PIN Rectifier With Ion-Implanted Floating Guard Rings

Here, this work reports on the fabrication and properties of a homojunction gallium nitride (GaN) p-i-n (PIN) rectifier fabricated on a free-standing GaN substrate. Uniform device performance is achieved with breakdown voltage (BV) >1.2 kV and low ON-resistance × area ( R ON A ). The statistics of the BV measurements show 58.5% of devices achieve BV >1.3 kV, and 71.1% of devices achieve BV >1.2 kV, as attributed to high quality and control in both epitaxial growth and device process. At room temperature, R ON A is 0.23 mΩ∙ cm 2 at a current density ( J ) of 6.9 kA/cm2. The corresponding Baliga’s figure of merit is >5.97 GW/cm 2 . Temperature-dependent reverse I – V measurements were performed and show a positive temperature coefficient of 0.42 V/K, indicating the avalanche capability of reverse breakdown. Further analysis with the Poole-Frenkel model on the temperature-dependent measurement suggested that a trap-assisted tunneling process contributed to the reverse leakage current. Floating guard rings (FGRs) formed by nitrogen implantation serve as an effective edge termination technique in these GaN PIN rectifiers, resulting in uniform performance in both forward and reverse bias.

42 ENGINEERING↗
DOE OSTI2023

Non-planar growth of high Al-mole-fraction AlGaN on patterned GaN platforms for mitigating strain-induced cracks beyond the critical layer thickness

Non-planar growth of Al x Ga 1-x N epitaxial layers with an average alloy composition up to Al-mole-fraction of x ~ 0.21 was performed on patterned c-plane GaN on (0001) sapphire substrates with stripe-shaped mesa structures. This approach successfully realized the growth of crack-free AlGaN layers on the top of mesas with layer thicknesses greater than the expected critical layer thickness by relaxing the in-plane stress on the top of the mesa. The effectiveness of the relaxation strongly depends on the width and depth of the stripe mesa. In conclusion, the relaxation of in-plane stress and resultant suppression of cracks in AlGaN layer are qualitatively discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Carbon and silicon background impurity control in undoped GaN layers grown with trimethylgallium and triethylgallium via metalorganic chemical vapor deposition

The unintentional impurity incorporation in GaN epitaxial layers impacts the electrical conductivity and optical properties of the films grown by metalorganic chemical vapor deposition (MOCVD). It is critical to control impurity-related states for device structure development. The aim of this work is to contribute to the understanding of the reasons for the presence of certain background impurities. In this paper, the unintentional impurity incorporation of carbon, hydrogen, oxygen, and silicon in undoped (u-) GaN films grown by low-pressure MOCVD were studied. Background impurity concentrations were evaluated by secondary ion mass spectroscopy (SIMS) to optimize growth parameters including V/III ratio, growth temperature (T g ), growth pressure (P g ), and gallium (Ga) precursors of trimethylgallium (TMG) or triethylgallium (TEG). Unintentional [C] and [Si] incorporations are found to be highly dependent on the growth parameters. Further, for the same growth conditions, u-GaN films grown with a TEG precursor exhibited a lower background concentration of C compared to that of GaN grown with TMG. However, the lowest background [C] achieved was grown with TMG using optimized conditions and exhibited [C]<4×10 15 cm -3 which was at the detection limit of the SIMS measurement. These results were measured for a u-GaN layer grown with TMG at 200 Torr, 1030°C, and a V/III of 3700. The lowest background [Si] of 4×10 15 cm -3 was achieved by growing with TMG at 200 Torr, 1000°C, and V/III of 650.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Breakdown characteristics of deep-ultraviolet Al 0.6 Ga 0.4 N p-i-n avalanche photodiodes

A top-illuminated deep-ultraviolet Al 0.6 Ga 0.4 N p-i-n avalanche photodiode (APD) structure was designed and grown by metalorganic chemical vapor deposition on an AlN bulk substrate and on two different quality AlN/sapphire templates, and APDs were fabricated and tested. The APD devices with a circular diameter of 20 μm have demonstrated a distinctive reverse-bias breakdown behavior. The reverse breakdown voltage of the APDs is approximately -140 V, which corresponds to a breakdown electric field of 6–6.2 MV/cm for the Al 0.6 Ga 0.4 N material as estimated by Silvaco TCAD simulation. The APDs grown on the AlN bulk substrate show the lowest leakage current density of < 1 × 10 -8 A/cm 2 (at low reverse bias) compared to that of the devices grown on the AlN templates. From the photocurrent measurement, a maximum gain (current limited) of 1.2 × 10 4 is calculated. The average temperature coefficients of the breakdown voltage are negative for APD devices fabricated from both the AlN bulk substrate and the AlN templates, but these data show that the coefficient is the least negative for the APD devices grown on the low-dislocation-density AlN bulk substrate.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗
DOE OSTI2022

Realizing crack-free high-aluminum-mole-fraction AlGaN on patterned GaN beyond the critical layer thickness

Wide-bandgap III-nitride heterostructures are required for a variety of device applications. However, this alloy system has a large lattice constant and thermal expansion coefficient mismatch that limits the alloy composition and layer thickness for many heteroepitaxial device structures. Consequently, various methods have been devised to allow the heteroepitaxial growth of AlInGaN heterostructures to accommodate this inherent strain. In this work, we describe a non-planar-growth approach that enables the deposition of crack-free high-Al-mole-fraction Al x Ga 1-x N on patterned GaN/sapphire templates and bulk GaN substrates with large-area mesas. We have studied the effects of the patterned mesa width, the mesa etch depth, and the gap between the mesas on the heteroepitaxy of Al x Ga 1-x N superlattices with an average Al molar fraction 0.11 < x¯ < 0.21 and non-planar overgrowth growth thicknesses up to 3.5 μm. Similar to the planar growth approach, increasing the thickness and Al mole fraction of the Al x Ga 1-x N superlattices leads to surface cracking when exceeding the critical layer thickness. However, limiting the mesa dimension in one direction enables strain mitigation and drastically increases the critical layer thickness. Additionally, larger etch depths of the mesas increase the Al alloy composition and thickness for crack-free AlGaN heteroepitaxy whereas the gap in between the mesas seems to have no crucial influence. We demonstrate that the Al alloy composition and layer thicknesses of such heterostructures can be increased far beyond the critical layer thickness for planar growth and demonstrate the growth of a crack-free full AlxGa 1-x N/GaN quantum-well laser heterostructure designed for operation at ~370 nm.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗