Detsi, Eric

Publications and source records attributed to Detsi, Eric.

7 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Additive manufacturing of multiscale NiFeMn multi-principal element alloys with tailored composition

Nanostructured multi-principal element alloys (MPEAs) have been explored as next-generation engineering materials due to unique mechanical and functional properties which have significant advantages over traditional dilute alloys. However, the practical applications of nanostructured MPEAs are still limited due to the lack of scalable processing approaches to prepare a large quantity of nanostructured MPEAs, as well as lack of an efficient pathway for high-throughput discovery of better functional nanostructured MPEAs within their vast compositional space. Here we tackle these challenges by presenting an integrated approach by combining direct-ink-writing-based additive manufacturing, solid-state sintering, and chemical dealloying to manufacture hierarchically porous MPEAs. The hierarchical structure is comprised of macro- and micro-scale pores introduced via extrusion printing and polymer decomposition during sintering, as well as nanoscale pores formed via chemical dealloying. The macro- and micro-scale pores allow efficient dealloying of a large mass of material as the diffusion length that the corroding medium must penetrate remains at the scale of the ligaments formed after sintering (∼10 μm), despite the large volume of the 3D-printed samples. In addition, this integrated approach enables versatile control of the alloy composition via precisely tuning the ratio of elemental powders in the starting ink, thus offering a pathway for high-throughput discovery of novel functional MPEAs. As a case study, multiscale macro/micro/nanoporous NiFeMn MPEAs with three different compositions were investigated as catalysts to reduce the overpotential of oxygen evolution reaction (OER), where NiFeMn-based electrocatalysts display composition-dependent performance such that the overpotential measured at a current of 0.5 A g −1 for OER increases in the order of Ni 58 Fe 29 Mn 13 ⩽ Ni 64 Fe 26 Mn 10 < Ni 76 Fe 18 Mn 6 . This introduced manufacturing process offers new opportunities for scalable fabrication and rapid screening of nanostructured multi-component complex alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Morphology Evolution in Self-Healing Liquid-Gallium-Based Mg-Ion Battery Anode

Conventional solid battery anodes suffer from dendrite growth and volume changes, resulting in poor cycling performances. Self-healing electrodes made of liquid metals and alloys can overcome these issues by reversibly undergoing liquid–solid phase transformations during (dis)charging. Just recently, we achieved 1000 cycles in Mg-ion battery anodes using liquid Ga as the active material, which reversibly transformed into solid Mg 2 Ga 5 during (de)magnesiation. However, the fundamental mechanism behind this liquid–solid phase transformation remains unclear. In this follow-up work, cryogenic focused ion beam electron microscopy is used to elucidate the morphology evolution when liquid Ga embedded in a carbon-binder matrix transforms into solid Mg 2 Ga 5 during cycling. We found that liquid Ga gradually diffuses into the surrounding matrix, increasing the contact area between active material and electrolyte, facilitating the charge transfer process. These new insights will help understand the performance of alkali- and alkaline-earth-metal batteries based on liquid anodes.

25 ENERGY STORAGE↗
DOE OSTI2023

Sub-100 mA/cm 2 CO 2 -to-CO Reduction Current Densities in Hierarchical Porous Gold Electrocatalysts Made by Direct Ink Writing and Dealloying

While most research efforts on CO 2 -to-CO reduction electrocatalysts focus on boosting their selectivity, the reduction rate, directly proportional to the reduction current density, is another critical parameter to be considered in practical applications. This is because mass transport associated with the diffusion of reactant/product species becomes a major concern at a high reduction rate. Nanostructured Au is a promising CO 2 -to-CO reduction electrocatalyst for its very high selectivity. However, the CO 2 -to-CO reduction current density commonly achieved in conventional nanostructured Au electrocatalysts is relatively low (in the range of 1–10 mA/cm 2 ) for practical applications. In this work, we combine direct ink writing-based additive manufacturing and dealloying to design a robust hierarchical porous Au electrocatalyst to improve the mass transport and achieve high CO 2 -to-CO reduction current densities on the order of 64.9 mA/cm 2 with CO partial current density of 33.8 mA/cm 2 at 0.55 V overpotential using an H-cell configuration. Although the current density achieved in our robust hierarchical porous Au electrocatalyst is one order of magnitude higher than the one achieved in conventional nanostructured electrocatalysts, we found that the selectivity of our system is relatively low, namely 52%, which suggests that mass transport remains a critical issue despite the hierarchical porous architecture. We further show that the bulk dimension of our electrocatalyst is a critical parameter governing the interplay between selectivity and reduction rate. In conclusion, the insights gained in this work shed new light on the design of electrocatalysts toward scale-up CO 2 reduction and beyond.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Isolating intermediate Mg 11 Cu 6 Al 12 phase in ternary Mg-Cu-Al alloy by electrolytic dealloying

While dealloying is widely used to create nanoporous materials, it has rarely been employed to isolate difficult-to-synthesize intermediate phases. Here, in this work, we show how air-free, electrolytic dealloying at room temperature can be used to isolate the ternary intermetallic Mg 11 Cu 6 Al 12 phase. We create a ternary Mg-Cu-Al parent alloy containing the Mg 11 Cu 6 Al 12 compound and other phases, then subsequently remove these other phases via electrolytic dealloying to isolate the Mg 11 Cu 6 Al 12 phase. Isolated Mg 11 Cu 6 Al 12 phase exhibits ≈1 μm diameter rod-shaped microstructure. Phase and chemical analysis conducted using various techniques, including inductively coupled plasma and lab and synchrotron-based X-ray diffraction, show minimal impurities. This new approach to isolate the Mg 11 Cu 6 Al 12 phase can unlock its use in fundamental research and can be applied to other difficult-to-synthesize intermetallic compounds.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Mesoporous nickel-iron-manganese-alloy based metal/metal oxide composite thick film catalysts

Selective alloy corrosion is used to synthesize a robust and ultrafine mesoporous NiFeMn-based metal/metal oxide oxygen evolving catalyst with ligament and pore sizes in the range of 10 nm and a BET surface area of 43 m2/g. As an oxygen evolving catalyst, the mesoporous catalyst exhibits high stability (>264 hours) at a high current density (500 mA/cm2) with a low overpotential (360 mV) using a moderate electrolyte concentration (1 M KOH). The catalyst is made from non-precious metals and its fabrication is straight forward and directly applicable to large-scale synthesis.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Three-dimensional hierarchical nanoporous copper via direct ink writing and dealloying

Three-dimensional (3D) hierarchical nanoporous Cu (3DHNP-Cu) is synthesized using a combination of direct ink writing (DIW) based 3D printing, thermal sintering, and chemical dealloying of Mn–Cu alloys. Through tuning processing conditions such as ink composition and cooling rate (after sintering), with consideration of Mn loss during sintering, 3DHNP-Cu with fully bicontinuous nanostructures and negligible residual Mn can be produced after dealloying. The 3DHNP-Cu is comprised of structural features that span seven orders of magnitude, where DIW digitally controls macroscale porous features, thermal sintering and degradation of the binding polymer determines microscale porous features, and dealloying gives rise to nanoscale pores.

36 MATERIALS SCIENCE↗