Investigation of hot-spots due to trapped flux in niobium superconducting radiofrequency cavities

One of the significant sources of residual losses in superconducting radio-frequency cavities is magnetic flux trapped during the cool-down due to the incomplete Messier effect. If the trapped vortices are non-uniformly distributed on the cavity surface, the temperature mapping revealed the “hotspots” at the location of high density of pinned vortices. Here, we performed a rf test on 1.3 GHz single cell cavity with the combination of the temperature mapping system. The temperature mapping reveled the development of the hot spots with the increase in rf field inside the cavity. When magnetic field is trapped locally on the surface of cavity, the hot-spots strength increase rapidly, showing the direct correlation of vortex induced hot spot and corresponding rf loss.

Accelerator Physics↗

DOE OSTI2024

IMPACT OF MEDIUM TEMPERATURE HEAT TREATMENT ON FLUX TRAPPING SENSITIVITY IN SRF CAVITIES

The effect of mid-T heat treatment on flux trapping sensitivity was measured on several 1.3 GHz single cell cavities subjected to medium temperature vacuum annealing at temperature of 150 - 400 ?C for a duration of 3 hours. The cavity was cooldown with residual magnetic field ?0 and ?20 mG in Dewar with cooldown condition of full flux trapped. The quality factor as a function of accelerating gradient was measured. The results show the correlation between the treatment temperature, quality factor, and sensitivity to flux trapping. Sensitivity increases with increasing heat treatment temperatures within the range of (200 - 325 ?C/3h).Moreover, variations in the effective penetration depth ofthe magnetic field and the density of quasi-particles can occur,influencing alterations in the cavity?s electromagneticresponse and resonance frequency.

Dhakal, P.↗

DOE OSTI2024

DEVELOPMENT OF PLASMA SIMULATION TOOL FOR THE ACCEL-ERATING CAVITIES

Plasma processing of superconducting radio frequency (SRF) cavities has shown an improvement in accelerating gradient by reducing the radiation due to field emission and multipacting. Plasma processing is a common tech-nique where the free oxygen produced by the plasma breaks down and removes hydrocarbons from surfaces. This increases the work function and reduces the second-ary emission coefficient. The hydrocarbon fragments of H2, CO, CO2, and H2O are removed from the system with the process gas which is flowing through the system. Here, we present COMSOL for the first time to simulate the plasma processing of an SRF cavity. In this work, we use Jefferson Lab's C75 SRF cavities design as our case study. Using simulation, we predict the condition of plasma ignition inside the SRF cavity. The simulation provides information about the optimal rf coupling to the cavity, mode for plasma ignition, choice of gas concen-tration, power, and pressure.

Senevirathne, I.↗

DOE OSTI2023

Microstructure development in a cold worked SRF Nb sheet undergoing 700°C-900°C/3h heat treatments.

Bulk Nb for TESLA shaped SRF cavities is a mature technology, with high gradient (>35 MV/m) and high Q cavities (>1010, ~2K) routinely fabricated. Significant advances are in order to push Q?s to 1011 (~2K), and involve modifications to the sub-surface Nb layers by impurity doping (N, O). In order to achieve the lowest surface resistance any trapped flux needs to be expelled for cavities to reach high Q?s. There is clear evidence that cavities fabricated from polycrystalline sheets meeting current specifications require higher temperatures beyond 800oC leads to better flux expulsion, and hence improves Q. Recently, cavities fabricated with a non-traditional Nb sheet with initial cold work due to cold rolling expelled flux better after 800°C/3h heat treatment than cavities fabricated using fine-grain polycrystalline Nb sheets. Here, we analyze the microstructure development in Nb from the vendor supplied cold work non-annealed sheet that was fabricated into an SRF cavity as a function of heat treatment building upon the methodology development to analyze microstructure being developed by the FSU-MSU-UT-Austin- JLAB collaboration. The results indicate correlation between full recrystallization and better flux expulsion.

Balachandran, S.↗

DOE OSTI2023

Temperature, rf field, and frequency dependence performance evaluation of superconducting niobium half-wave coaxial cavity

Recent advancement in superconducting radio frequency cavity processing techniques, with diffusion of impurities within the RF penetration depth, resulted in high quality factor with increase in quality factor with increasing accelerating gradient. The increase in quality factor is the result of a decrease in the surface resistance as a result of nonmagnetic impurities doping and change in electronic density of states. The fundamental understanding of the dependence of surface resistance on frequency and surface preparation is still an active area of research. Here, we present the result of RF measurements of the TEM modes in a coaxial half-wave niobium cavity resonating at frequencies between 0.3 ? 1.3 GHz. The temperature dependence of the surface resistance was measured between 4.2 K and 1.6 K. The field dependence of the surface resistance was measured at 2.0 K. The baseline measurements were made after standard surface preparation by buffered chemical polishing.

Dhakal, P.↗

DOE OSTI2023

Medium grain niobium SRF cavity production technology for science frontiers and accelerator applications

Herein we present the cost-effective production of superconducting radio frequency (SRF) cavities made of medium grain (MG) niobium (Nb) discs directly sliced from forged and annealed billet. This production method provides clean surface conditions and reliable mechanical characteristics with sub-millimeter average grain size resulting in stable SRF cavity production. We propose to apply this material to particle accelerator in the science and industrial applications. The science applications require high field gradients(≥ 30 MV/m) particularly in pulsed mode. The industrial applications require high $Q_0$ values with moderate gradients (~ 20 MV/m) in CW mode operation. This paper describes the MG Nb disc production recently demonstrated and discusses future prospects for application in advanced particle accelerators in the science and industrial applications.

47 OTHER INSTRUMENTATION↗

DOE OSTI2023

Effect of Strain on the Resistivity and Thermal Conductivity of High Purity Niobium

High purity niobium (Nb) is a technologically important material for large-scale accelerator and nano-scale quantum computing applications in microwave frequency range. The high thermal conductivity and low resistivity of Nb are critical to the high performance at temperature range of 0.01–4.0 K. The presence of interstitials such as O, N, H, and C act as scattering centers and alter the mean free path, reducing resistivity and thermal conductivity, and contributing significantly to Nb's thermal performance for temperatures of 2.0 K and above. The residual resistivity ratio (RRR), defined as the ratio of the normal state resistivity at 300 K to that at 4.2 K (Nb, T c = 9.2 K), is an accepted direct estimate of the impurity content of fully recrystallized Nb. Complete re-crystallization of Nb is challenging unless very high temperatures are employed, which is often impractical, hence, in practice, dislocation and dislocation structures impact the thermal performance of Nb due to strong phonon scattering contributions. Furthermore, this paper reports on the degradation of thermal conductivity and RRR of high purity Nb large grain, single crystal with fixed impurity, varying strain, and dislocation content levels. Experimental thermal conductivity data fits the Boltzmann transport equation incorporating dislocation density.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Residual loss due to magnetic flux trapping in niobium superconducting microwave cavities

One of the significant source of radio frequency loss in superconducting microwave cavities is the trapped residual magnetic field during the cooldown due to the incomplete Messier effect. The sensitivity of flux trapping depends on the distribution of impurities, network of dislocations and defects which pin vortices. Recent advancement in cavity processing techniques resulted in very high quality factors with impurity doping, however the rf loss related to the flux trapping increases. High quality factor in SRF cavities is not only limited to particle accelerators but also emerging as an application to quantum computing and quantum information science. In this presentation, we present the results of measurements of flux trapping sensitivity on several 1.3 GHz elliptical accelerating cavities with different grain size, impurity content and surface preparations.

Dhakal, P.↗

DOE OSTI2022

Evaluation of Single-Cell Cavities Made of Forged Ingot Niobium at Jefferson Lab

Currently, fine grain niobium (Nb) (grain size ~ 50 um) and large grain Nb (grain size of a few cm) are being used for the fabrication of superconducting radio frequency (SRF) cavities. Medium grain forged ingot with grain size of a few hundred um may be beneficial for cost-effectiveness as well as providing better performance for future SRF-based accelerators. Forged ingot Nb with medium grain size is a novel production method to obtain Nb discs used for the fabrication of superconducting radio frequency cavities. We have fabricated two 1.5 GHz single cell cavities made from forged Nb ingot with a residual resistivity ratio of ~100. The cavities were chemically and mechanically polished and heat-treated in the temperature range of 650-1000 C before the rf test. One of the cavities reached an accelerating gradient of 34 MV/m with a quality factor Q > 1e10, while the second cavity was limited at 14 MV/m, likely due to a weld defect at the equator.

Dhakal, P.↗

DOE OSTI2022

Cavity Qualification and Production Update for SNS-PPU Cryomodules at Jefferson Lab

The Proton Power Upgrade (PPU) project at Oak Ridge National Lab’s Spallation Neutron Source (SNS) currently being constructed will double the proton beam power capability from 1.4 to 2.8 MW by adding seven cryomodules, each containing four six-cell high-beta (β = 0.81) superconducting radio frequency cavities. Research Instruments, located in Germany, built and processed the cavities at the vendor site, including electropolishing as the final active chemistry step. Twenty-eight cavities for seven cryomodules and an additional four cavities for a spare cryomodules were delivered to Jefferson Lab and first qualification tests were completed on all cavities as received from the vendor. The performance largely exceeded the requirements on quality factor and accelerating gradient. Here we present the status of initial cavity qualification tests, rework on unqualified cavities and final cavity qualification with helium vessel prior to installation in cryomodules. In addition, an update on cryomodule production is presented.

Dhakal, P.↗

DOE OSTI2022

MAGNETIC FLUX EXPULSION IN SUPERCONDUCTING RADIO-FREQUENCY NIOBIUM CAVITIES MADE FROM COLD WORKED NIOBIUM

Trapped residual magnetic field during the cool down of superconducting radio frequency (SRF) cavities is one of the primary sources of RF residual losses leading to lower quality factor. Historically, SRF cavities have been fabricated from high purity fine grain niobium with grain size ~50 to 100 µm as well as large grain with grain size of the order of few centimeters. Non-uniform recrystallization of fine-grain Nb cavities after the post fabrication heat treatment leads to higher flux trapping during the cool down, and hence the lower quality factor. We fabricated two 1.3 GHz single cell cavities from cold-worked niobium from different vendors and processed along with cavities made from SRF grade Nb. The flux expulsion and flux trapping sensitivity were measured after successive heat treatments in the range 800 to 1000°C. The flux expulsion from cold-worked fine-grain Nb cavities improves after 800°C/3h heat treatments and it becomes similar to that of standard fine-grain Nb cavities when the heat treatment temperature is higher than 900°C.

Khanal, B. D.↗

DOE OSTI2022

Effect of duration of 120 oC baking on the performance on superconducting radio frequency niobium cavities

Over the last decade much attention was given in increasing the quality factor of superconducting radio frequency (SRF) cavities by impurity doping. Prior to the era of doping, the final cavity processing technique to achieve the high accelerating gradient includes the ?in situ? low temperature baking of SRF cavities at temperature ~ 120 oC for several hours. Here, we present the results of a series of measurements on 1.3 GHz TESLA shape single-cell cavities with successive low temperature baking at 120 oC up to 96 hours. The experimental data were analyzed with available theory of superconductivity to elucidate the effect of the duration of low temperature baking on the superconducting properties of cavity materials as well as the rf performance. In addition, the rf loss related to the trapping of residual magnetic field refereed as flux trapping sensitivity was measured with respect to the duration of 120 oC bake.

Khanal, B. D.↗

DOE OSTI2022

MAGNETIC FLUX EXPULSION IN SUPERCONDUCTING RADIO-FREQUENCY NIOBIUM CAVITIES MADE FROM COLD WORKED NIOBIUM

Trapped residual magnetic field during the cool down of superconducting radio frequency (SRF) cavities is one of the primary sources of RF residual losses leading to lower quality factor. Historically, SRF cavities have been fabricated from high purity fine grain niobium with grain size ~50 to 100 µm as well as large grain with grain size of the order of few centimeters. Non-uniform recrystallization of fine-grain Nb cavities after the post fabrication heat treatment leads to higher flux trapping during the cool down, and hence the lower quality factor. We fabricated two 1.3 GHz single cell cavities from cold-worked niobium from different vendors and processed along with cavities made from SRF grade Nb. The flux expulsion and flux trapping sensitivity were measured after successive heat treatments in the range 800 to 1000°C. The flux expulsion from cold-worked fine-grain Nb cavities improves after 800°C/3h heat treatments and it becomes similar to that of standard fine-grain Nb cavities when the heat treatment temperature is higher than 900°C.

Khanal, B. D.↗

DOE OSTI2022

SRF Levitation and Trapping of Nanoparticles

A proposal has been conceived to levitate and trap mesoscopic particles using radio frequency (RF) fields in a superconducting RF(SRF) cavity. Exploiting the intrinsic characteristics of an SRF cavity, this proposal aims at overcoming a major limit faced by state-of-the-art laser trapping techniques. The goal of the proposal is to establish a foundation to enable observation of quantum phenomena of an isolated mechanical oscillator interacting with microwave fields. An experiment supported by LDRD funding at JLab has started to address R&D issues relevant to these new research directions using existing SRF facilities at JLab. The success of this experiment would establish its groundbreaking relevance to quantum information science and technology, which may lead to applications in precision force measurement sensors, quantum memories, and alternative quantum computing implementations with promises for superior coherence characteristics and scalability well beyond the start-of-the-art. In this contribution, we will introduce the proposal and basic consideration of the experiment.

Geng, R. L.↗

DOE OSTI2022

Status of SNS Proton Power Upgrade SRF Cavities Production Qualification

The Proton Power Upgrade project at Oak Ridge National Lab’s Spallation Neutron Source (SNS PPU) currently being constructed will double the proton beam power from 1.4 to 2.8 MW by adding 7 additional cryomodules, each contains four six-cell high beta (\beta = 0.81) superconducting radio frequency cavities. The cavities were built by Research Instruments, Germany, with all the cavity processing done at the vendor site, including electropolishing as the final active chemistry step. All 28 cavities needed for 7 cryomodules were delivered to Jefferson Lab, ready to be tested. The cryogenic RF qualifications and helium vessel welding were done at Jefferson Lab. The performance largely exceed the requirements, and greatly exceeded the performance of the original SNS cavity production series. Here, we present the summary of RF test on production cavities to this date.

Dhakal, P.↗

DOE OSTI2022

Thermal Conductivity of Electroplated Copper Onto Bulk Niobium at Cryogenic Temperatures

Superconducting radio-frequency (SRF) cavities made of high-purity bulk niobium are widely used in modern particle accelerators. The development of metallic outer coatings with high thermal conductivity would have a beneficial impact in terms of improved thermal stability, reduced material cost and for the development of conduction-cooled, cryogen-free SRF cavities. Several high-purity, fine-grain Nb samples have been coated with 2-4 mm thick copper by electroplating. Measurements of the thermal conductivity of the bimetallic Nb/Cu samples in the range 2 ? 7 K showed values of the order of 1 kW/(m K) at 4.3 K. Very good adhesion between copper and niobium was achieved by depositing a thin Cu layer by cold spray on the niobium, prior to electroplating the bulk Cu layer.

Dhakal, P.↗

DOE OSTI2021

Development of Helium Vessel Welding Process for SNS PPU Cavities

The Spallation Neutron Source Proton Power Upgrade cavities are produced by Research Instrument with all the cavity processing done at vendor sites with final chemistry applied to the cavity to be electropolishing. Cavities are delivered to Jefferson Lab, ready to be tested. One of the tasks to be completed before the arrival of production-ready PPU cavities is to develop a robust helium vessel welding protocol. We have successfully developed the process and applied it to three six-cell high beta cavities. Here, we present the summary of RF results, welding process development, and post helium vessel RF results.

Dhakal, P.↗

DOE OSTI2021

Status of SNS Proton Power Upgrade SRF Cavities Production Qualification

The Proton Power Upgrade project at Oak Ridge National Lab’s Spallation Neutron Source (SNS PPU) currently being constructed will double the proton beam power from 1.4 to 2.8 MW by adding 7 additional cryomodules, each contains four six-cell high beta (\beta = 0.81) superconducting radio frequency cavities. The cavities were built by Research Instruments, Germany, with all the cavity processing done at the vendor site, including electropolishing as the final active chemistry step. All 28 cavities needed for 7 cryomodules were delivered to Jefferson Lab, ready to be tested. The cryogenic RF qualifications and helium vessel welding were done at Jefferson Lab. The performance largely exceed the requirements, and greatly exceeded the performance of the original SNS cavity production series. Here, we present the summary of RF test on production cavities to this date.

Dhakal, P.↗