DOE OSTI2018

Effect of Initial Microstructure on Properties of Cryorolled Al 5052 Alloy Subjected to Different Annealing Treatment Temperatures

Al 5052 alloy sheets were subjected to different pre-annealing temperatures (150, 200, 250, 300, and 350 °C) prior to cryorolling. The process resulted in Al 5052 alloys with different initial microstructures. The pre-annealed alloy sheets were compared with a cryorolled sample not subjected to pre-annealing. The thicknesses of the alloy samples after cryorolling was reduced by 30%. The pre-annealed cryorolled samples exhibited low crystallite size, and high lattice strain. Among them, the cryorolled sample pre-annealed at 300 °C had the lowest crystallite size, and the highest lattice strain. Changes in initial microstructure of this sample resulted in a significant improvement in its hardness (88 Hv), tensile strength (333 MPa), and corrosion resistance. The sample had the highest corrosion resistance among the cryorolled samples.

36 MATERIALS SCIENCE↗

NASA NTRS2004

Evolution of In-Situ Generated Reinforcement Precipitates in Metal Matrix Composites

Due to certain inherent advantages, in-situ production of Metal Matrix Composites (MMCs) have received considerable attention in the recent past. ln-situ techniques typically involve a chemical reaction that results in precipitation of a ceramic reinforcement phase. The size and spatial distribution of these precipitates ultimately determine the mechanical properties of these MMCs. In this paper we will investigate the validity of using classical growth laws and analytical expressions to describe the interaction between a precipitate and a solid-liquid interface (SLI) to predict the size and spatial evolution of the in-situ generated precipitates. Measurements made on size and distribution of Tic precipitates in a Ni&I matrix will be presented to test the validity of such an approach.

Sen, S.↗

NASA NTRS2001

Particle Engulfment and Pushing (PEP): Past Micro-Gravity Experiments and Future Experimental Plan on the International Space Station (ISS)

The interaction of an insoluble particle with a growing solid-liquid interface (SLI) has been a subject of investigation for the four decades. For a metallurgist or a material scientist understanding the fundamental physics of such an interaction is relevant for applications that include distribution of reinforcement particles in metal matrix composites, inclusion management in castings, and distribution of Y2Ba1Cu1O5 (211) precipitates (flux pinning sites) in Y1Ba2Cu3O7 (123) superconducting crystals. The same physics is also applicable to other areas including geological applications (frost heaving in soils) and preservation of biological cells. Experimentally this interaction can be quantified in terms of a critical growth velocity, Vcr, of the SLI below which particles are pushed ahead of the advancing interface, and above which the particles are engulfed. Past experimental evidence suggests that this Vcr is an inverse function of the particle radius, R. In order to isolate the fundamental physics that governs such a relationship it is necessary to minimize natural convection at the SLI that is inherent in ground based experiments. Hence for the purpose of producing benchmark data (Vcr vs. R) PEP is a natural candidate for micro-gravity experimentation. Accordingly, experiments with pure Al containing a dispersion of ZrO2 particles and an organic analogue, succinonitrile (SCN) containing polystyrene particles have been performed on the LMS and USMP-4 mission respectively. In this paper we will summarize the experimental data that was obtained during these two micro-gravity missions and show that the results differ compared to terrestrial experiments. We will also discuss the basic elements of our analytical and numerical model and present a comparison of the predictions of these models against micro-gravity experimental data. Finally. we will discuss our future experimental plan that includes the ISS glovebox and MSRRl.

Sen, Subhayu↗

NASA NTRS1999

In-Situ Observations of Interaction Between Particulate Agglomerates and an Advancing Planar Solid/Liquid Interface: Microgravity Experiments

Results are reported of directional solidification experiments on particulate agglomerate pushing and engulfment by a planar solid/liquid (s/1) interface. These experiments were conducted on the Space Shuttle Columbia during the United States Microgravity Payload 4 (USMP-4) Mission. It was found that the pushing to engulfment transition velocity, V(sub ct),, for agglomerates depends not only on their effective size but also their orientation with respect to the s/l interface. The analytical model for predicting V(sub cr) of a single particle was subsequently enhanced to predict V(sub cr) of the agglomerates by considering their shape factor and orientation.

Sen, S.↗

NASA NTRS1999

In Situ Observations of Interaction Between Particulate Agglomerates and an Advancing Planar Solid/Liquid Interface: Microgravity Experiments

Results are reported of directional solidification experiments on particulate agglomerate pushing and engulfment by a planar solid/liquid (s/l) interface. These experiments were conducted on the Space Shuttle Columbia during the United States Microgravity Payload 4 (USMP-4) Mission. It was found that the pushing to engulfment transition velocity, V(sub cr) for agglomerates depends not only on their effective size but also their orientation with respect to the s,1 interface. The analytical model for predicting V(sub cr) of a single particle was subsequently enhanced to predict V(sub cr) of the agglomerates by considering their shape factor and orientation.

Sen, S.↗

NASA NTRS1998

Measurement of Interfacial Undercooling in a Dilute Pb-Sn Alloy Near the Regime of Morphological Instability

The solid/liquid (s/1) interfacial Seebeck technique was used to measure interfacial undercooling in a Pb-1 wt.% Sn alloy. For plane front solidification an undercooling in the range of 0.54-0.57C was recorded. However, for growth velocities between 6 to 15 micron/s the undercooling, increased with increase in velocity. 'Tbis is in contradiction to the theoretical predictions based on growth at the extremum condition. A modified analytical expression was developed based on the maro,,inal stability criterion to predict undercooling for growth velocities immediately over the limit of morphological stability. Between 6 to 15 microns/s the trend predicted by this modified expression is in qualitative agreement with the experimental results. This model is more consistent with the analysis of Venugopal and Kirkaldy which states that the extremum condition criterion is not applicable in the marginal stability regime. At higher growth velocities between 20 and 50 microns/s where stable cellular growth is expected the undercooling, decreased with increase in velocity. The predictions of Burden and Hunt based on extremum criterion agree reasonably well with the experimental results in this velocity range. Finally, the importance of non-equilibrium phase diagram parameters such as partition coefficient and liquidus slope were also evaluated using the experimental undercooling results obtained in this investigation.

Sen, S.↗

NASA NTRS1990

Directional Solidification Of Monotectic Alloys

Conditions promoting formation of aligned fibers sought. Report describes experiments in directional solidification of Cu/Pb and Bi/Ga monotectic alloys. Study motivated by need to understand physical mechanism governing formation of rodlike or fiberlike aligned structures in solidifying alloy and to determine process conditions favoring such structures.

Dhindaw, B. K.↗

NASA NTRS1988

Directional solidification of Cu-Pb and Bi-Ga monotectic alloys under normal gravity and during parabolic flight

Cu-Pb and Bi-Ga monotectic alloys of nominal hypermonotectic compositions were directionally solidified under various furnace translation rates, temperature gradients, and gravity levels. Gravity was varied by solidifying the alloys under ground conditions and in the furnace aboard NASA KC-135 aircraft, flying on parabolic trajectories. High translation rates, high gradients, high gravity levels, and higher density and lower thermal conductivity of the L2 phase favored the formation of fiber composite structure, while the opposite conditions resulted in structures consisting of L2 droplets in alpha matrix. A modified particle engulfment theory as originally enunciated by Ulhmann et al. (1964) is proposed to explain these observations.

Dhindaw, B. K.↗

NASA NTRS1988

Behavior of ceramic particles at the solid-liquid metal interface in metal matrix composites

Directional solidification results were obtained in order to investigate particle behavior at the solid-liquid interface in Al-2 pct Mg (cellular interface) and Al-6.1 pct Ni (eutectic interface) alloys. It is found that particles can be entrapped in the solid if adequate solidification rates and temperature gradients are used. Model results showed critical velocity values slightly higher than those obtained experimentally.

Stefanescu, D. M.↗

NASA NTRS1988

Directional solidification of Al-Ni/SiC composites during parabolic trajectories

Aluminum-6.1 wt. pct. nickel-silicon carbide composites containing varying volume fractions and particle sizes of SiC were directionally solidified at different translation rates and temperature gradients, under variable gravity levels. High-gravity, high-volume fractions of particles or high effective viscosity of liquid favored the engulfment of particles by the melt interface. Solidification under low gravity seemed to deflocculate the SiC particle agglomerates, while opposite results were obtained when solidifying under high gravity. Intercellular spacings were higher under low gravity solidfication.

Dhindaw, B. K.↗