NASA NTRS1999

Particle Engulfment and Pushing by Solidifying Interfaces

The scientific objectives of the work on Particle Engulfment and Pushing by Solidifying Interfaces (PEP) include: (1) to enhance the fundamental understanding of the physics of interaction between inert particles and the solidification interface, and (2) to investigate aspects of melt processing of particulate metal matrix composites in the unique microgravity environment that will yield some vital information for terrestrial applications. The proposal itself calls for a long-term effort on the Space Station. This paper reports on ground experiments performed to date, as well as on the results obtained from two flight opportunities, the LMS mission (1996) and the USMP-4 mission (1997).

Stefanescu, Doru M.↗

NASA NTRS1998

Particle Engulfment and Pushing by Solidifying Interfaces LMS Mission Results

Results of the directional solidification experiments on Particle Engulfment and Pushing by Solidifying Interfaces (PEP) conducted on the space shuttle Columbia are reported. The experiment was manifested as part of The Life and Microgravity Science Mission. Two pure aluminum (99.999%) 9 mm cylindrical rods, loaded with about 2 vol.% 500 microns diameter zirconia particles were melted and directionally solidified in the microgravity (micro-g) environment of the shuttle. The particles were non-reactive with the matrices within the temperature range of interest. The experiments were conducted such as to insure a planar solid/liquid interface during solidification. Two different cartridge - crucible - sample designs were used: a spring-piston and expansion void. Both resulted in sound samples. Samples were evaluated post-flight for soundness by X-ray computer tomography (XCT).

Juretzko, Frank R.↗

NASA NTRS1998

Particle Engulfment and Pushing by Solidification Interfaces: Ground Experiments - Part 1

Directional solidification experiments have been carried out to determine the pushing/engulfment transition for two different metal/particle systems. The systems chosen were aluminum/zirconia particles and zinc/zirconia particles. Pure metals (99.999% Al and 99.95% Zn) and spherical particles (500 microns in diameter) were used. The particles were non-reactive with the matrices within the temperature range of interest. The experiments were conducted such as to insure a planar solid/liquid interface during solidification. Particle location before and after processing was evaluated by X-ray transmission microscopy for the Al/ZrO2 samples. All samples were characterized by optical metallography after processing. A clear methodology for the experiment evaluation was developed to unambiguously interpret the occurrence of the pushing/engulfment transition. It was found that the critical velocity for engulfment ranges from 1.9 to 2.4 micron/s for Al/ZrO2 and from 1.9 to 2.9 microns/s for Zn/ZrO2.

Juretzko, Frank R.↗

NASA NTRS1998

Particle Engulfment and Pushing by Solidifying Interfaces: Micro-Gravity Experiments and Theoretical Analysis - Pt. 2

Results of the directional solidification experiments on Particle Engulfment and Pushing by Solidifying Interfaces (PEP) conducted on the space shuttle Columbia during the Life and Microgravity Science Mission are reported. Two pure aluminum (99.999%) 9 mm cylindrical rods, loaded with about 2 vol.% 500 micrometers diameter zirconia particles were melted and resolidified in the microgravity (microg) environment of the shuttle. One sample was processed at step-wise increased solidification velocity, while the other at step-wise decreased velocity. It was found that a pushing-to-engulfment transition (PET) occurred in the velocity range of 0.5 to 1 micrometers. This is smaller than the ground PET velocity of 1.9 to 2.4 micrometers. This demonstrates that natural convection increases the critical velocity. A previously proposed analytical model for PEP was further developed. A major effort to identify and produce data for the surface energy of various interfaces required for calculation was undertaken. The predicted critical velocity for PET was of 0.775 micrometers/s.

Stefanescu, Doru M.↗

NASA NTRS1990

The influence of buoyant forces and volume fraction of particles on the particle pushing/entrapment transition during directional solidification of Al/SiC and Al/graphite composites

Directional solidification experiments in a Bridgman-type furnace were used to study particle behavior at the liquid/solid interface in aluminum metal matrix composites. Graphite or silicon-carbide particles were first dispersed in aluminum-base alloys via a mechanically stirred vortex. Then, 100-mm-diameter and 120-mm-long samples were cast in steel dies and used for directional solidification. The processing variables controlled were the direction and velocity of solidification and the temperature gradient at the interface. The material variables monitored were the interface energy, the liquid/particle density difference, the particle/liquid thermal conductivity ratio, and the volume fraction of particles. These properties were changed by selecting combinations of particles (graphite or silicon carbide) and alloys (Al-Cu, Al-Mg, Al-Ni). A model which consideres process thermodynamics, process kinetics (including the role of buoyant forces), and thermophysical properties was developed. Based on solidification direction and velocity, and on materials properties, four types of behavior were predicted. Sessile drop experiments were also used to determine some of the interface energies required in calculation with the proposed model. Experimental results compared favorably with model predictions.

Stefanescu, Doru M.↗