Bonding to Bulk Metallic Glass using Aerospace-Grade Structural Adhesive
Bulk metallic glasses (BMGs) are non-crystalline metals with growing applications in aerospace. Due to their amorphous nature, BMGs generally exhibit stronger mechanical properties than most crystalline alloys and are more corrosion resistant. The limited reactivity of a corrosion resistant surface may explain the difficulty in establishing robust bonds to certain adhesives, especially commonly used structural adhesives for aerospace applications. Here, an amine cured aerospace adhesive was used for bonding an iron-nickel based BMG satellite component. Various types of processes were explored to avoid adhesive failure and increase bond strength. It was found that the BMG required specific chemical derivatization of the metal surface in order to achieve cohesive failure. Surface analysis was used to determine the mechanisms of adhesion enhancement. The process was optimized to maximize bond strength. This work helps explain the difficulties in bonding BMG materials and provides strategies for design of future bonded BMG components.
Determination of Trace Silicone Contamination on Composites by Quantitative XPS and LIBS
Surface treatment and surface characterization techniques are critical to ensure that adherends are chemically activated and free of contaminants prior to adhesive bonding. Silicone contamination from mold-release agents and other sources can interfere with interfacial bonding, decreasing the durability and performance of bonded composite structures. Tools and methods are needed that can be used in a production environment to reliably detect low levels of contaminants in a rapid, simple, and cost-effective manner to improve bond reliability. In this work, surface characterization of carbon fiber reinforced polymer (CFRP) composites was performed using laser induced breakdown spectroscopy (LIBS) and the results were compared with those obtained from X-ray photoelectron spectroscopy (XPS). The objective was to investigate the ability to quantify the surface species measured by LIBS since it offers many advantages over XPS in terms of ease of use, sample preparation, and real-time results. The as-processed CFRP panels had trace surface silicone contamination from the fabrication process, the source of which was not investigated. The composites were laser treated at select average laser power levels, resulting in varying levels of contamination reduction. The Si atomic percentage measurements using XPS were conducted both before and after laser ablation. The XPS results were compared with those obtained from LIBS to assess the reliability of each technique for surface contaminant characterization. The results showed an excellent correlation in Si atomic concentration between the two techniques.