Publications and source records attributed to Ding, Hongtao.

4 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Enhancing corrosion resistance of lightweight metal alloys through laser shock peening

In this study, we investigated the effects of laser shock peening (LSP) on the corrosion resistance of lightweight metal alloys, specifically AA6061 and AZ31. LSP was performed underwater, using a nanosecond pulse laser and without using a protective coating or layer on the workpiece. The corrosion behaviors of these alloys were analyzed through electrochemical tests, including open circuit potential, electrochemical impedance spectroscopy, and potentiodynamic polarization measurements. The results demonstrated that LSP significantly improved the polarization resistance, and higher laser power intensities led to increased corrosion resistance and reduced corrosion rates. This enhancement in anti-corrosion performance is attributed to the formation of a protective oxide layer on the surface, acting as a barrier against corrosion. In conclusion, the findings underscore the potential of laser surface treatment as a viable technique for enhancing the corrosion resistance of lightweight metal alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Role of surface wetting on tribological behavior for laser nanotextured steel using ionic liquid lubricants

Here, this research evaluates the effect of surface wettability on the tribological performance through ball-on-flat tribology testing. The substrate material, M2 tool steel, is laser processed and then functionalized with fluorocarbon and nitrile chemistry to achieve distinct oleophobicity and oleophilicity, respectively, but with a similar nanoscale surface texture. The baseline lubricant is poly-alpha-olefin (PAO) oil, and ionic liquids (ILs) are used as additives for this study. The interaction between the nanoscale textured steel surface and ionic liquid-based oils is investigated. A set of reciprocating wear tests are performed to investigate the tribological behavior of the tribo-system consisting of the surface-engineered, flat M2 tool steel specimen and a standard, surface-polished steel ball. Results show that the oleophobic flat surface results in a lower friction, while the oleophilic surface modification leads to a better wear protection to the flat surface. Ammonium-based IL provides the highest friction reduction, while the phosphonium-based ILs provide an improved wear protection.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Microstructural basis for improved corrosion resistance of laser surface processed AZ31 Mg alloy

Despite their excellent strength to weight ratio, wider use of Mg alloys for light weighting applications is limited by their poor corrosion resistance, especially in chloride ion-containing environments. The present study shows improved corrosion resistance imparted by laser surface processing (LSP) of a commercial AZ31 (Mg-3Al-1Zn) alloy. Nanosecond laser processing at three different power settings was carried out on the surface of a 1 mm thick rolled AZ31 sheet. Corrosion testing based on ASTM B117 method and several other electrochemical tests indicates substantial enhancement of corrosion resistance in LSP-treated AZ31. The underlying reason behind improved corrosion resistance of LSP-AZ31 surface has been identified using a variety of characterization tools (SEM, TEM, XPS). Formation of a ~0.5 µm thick mixed metal (Mg, Al) oxide surface film together with refinement in the size and number density of Al-Mn intermetallic particles appear to be playing a major role towards improved corrosion resistance after LSP treatment of AZ31 alloy.

Jana, Saumyadeep↗