Spin Reorientation in Antiferromagnetic MnPd 5 Se with an Anti-CeCoIn 5 Structure Type
MnPd 5 Se, a derivative of the anti-CeCoIn 5 -type phase, was synthesized from a high-temperature solid-state reaction, structurally determined by X-ray diffraction, and magnetically characterized with a combined magnetic measurement and neutron powder diffraction (NPD). According to the X-ray diffraction results, MnPd 5 Se crystallizes in a layered tetragonal structure with the same space group as CeCoIn 5 , P4/mmm (No. 123). MnPd5Se shows antiferromagnetic ordering around 80 K on the basis of the magnetic property measurements. An A-type antiferromagnetic structure was revealed from the analysis of neutron powder diffraction results at 300, 50, and 6 K. Moreover, a spin orientation rotation was observed as the temperature decreased. Pd L 3 X-ray absorption near edge spectroscopy results for MnPd5Se semiqualitatively correlate with the calculated density of states supporting a nominal 0.2 electron transfer into the Pd d orbital from either Se or Mn in the compound. The discovery of MnPd 5 Se, along with our previously reported MnT 5 Pn (T = Pd or Pt; Pn = P or As), provides a tunable system for studying the magnetic ordering from ferromagnetism to antiferromagnetism with the strong spin–orbit coupling effect.
Spin Reorientation in Antiferromagnetic Layered FePt 5 P
FePt 5 P, a substitutional variant of the anti-CeCoIn 5 structure type in the space group P4/mmm, was synthesized by a high-temperature solid-state method and structurally characterized by X-ray diffraction. FePt 5 P contains layers of FePt 12 clusters formed by magnetically active Fe and heavy Pt with strong spin-orbit coupling (SOC); the layers are separated by P atoms. The various Fe–Pt distances in FePt 12 clusters generate complex magnetic orders in FePt 5 P. According to temperature-dependent magnetic and specific heat measurements, FePt 5 P shows a stripe-type antiferromagnetic order at T N ≈ 90 K, which is also confirmed by resistivity measurements. Furthermore, a spin reorientation occurs at ~74 and ~68 K in and out of the ab plane based on the specific heat measurements. The temperature-dependent neutron powder diffraction patterns demonstrate the antiferromagnetic order in FePt 5 P, and the spins orientate up to 58.4° with respect to the c axis at 10 K. First-principles calculations of FePt 5 P show the band splitting at the Fermi level by strong SOC and the s–d hybridization between P and Fe/Pt electrons enhances the structural stability and affects the magnetic ordering.