DOE OSTI2024

METHOD FOR EXPOSING IRRADIATED FUEL CLADDING TO RAPID THERMAL TRANSIENTS

Reactor core materials exposed to rapid thermal transients during accidents can experience significant changes in mechanical properties as irradiation hardness is recovered. Understanding material performance during transients using computer modeling requires accurate descriptions of mechanical property evolution with time and temperature. A simple experimental capability was developed to expose irradiated Zircaloy to a simulated thermal transient using immersion in molten tin (at 675°C) to rapidly heat and hold before rapidly cooling with a water quench. Multiple heating-cooling cycles using a nonirradiated tensile specimen showed simplicity and viability. Based on preliminary test results, a robust system was established for routine evaluation of simulated thermal accident scenarios in the Low Activation Materials Design and Analysis (LAMDA) laboratory at Oak Ridge National Laboratory (ORNL). This paper summarizes system development and nonirradiated Zircaloy commissioning test results. Future experiments will conduct tensile tests on irradiated Zircaloy after various rapid temperature profiles.

Byun, TS↗
DOE OSTI2023

Analysis of Deformation and Fracture Mechanisms in the Harvested Low-Dose Baffle Former Bolt via Advanced Mechanical Tests

This report details the production of tensile specimens from in-service irradiated baffle former bolts (BFBs) and presents the results of a pilot in-situ SEM/EBSD test conducted at Oak Ridge National Laboratory’s Low Activation Materials Development and Analysis (LAMDA) facility. The SEM/EDS results confirmed that the material is AISI 316L steel, not AISI 347, and that no Nb addition was detected in several analyzed locations. EBSD analysis of the microstructure revealed in-grain misorientation gradients indicative of cold work, likely caused by material processing, and no retained ferrite was identified. During straining, dislocation channel formation was the primary deformation mechanism, with twinning also observed in favorably oriented grains at local strains as small as ~1.5%. No strain-induced phase instability was observed, likely due to the fact that the Ni and Cr content reached the upper limits for the 316L steel specification. Multiple microfracture events were observed during the tensile test. Fine strain-induced pores formed at the channel-grain boundary intersection points, while coarser microcracks were associated with non-metallic inclusions. Data analysis is ongoing, and additional tests are planned in the near future to provide more statistics and details.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Sister Rod Destructive Examinations (FY2021) Appendix B: Segmentation, Defueling, Metallographic Data and Total Cladding Hydrogen

As a part of the DOE-NE High Burnup Spent Fuel Data Project, Oak Ridge National Laboratory (ORNL) is performing destructive examinations (DEs) of high burnup (HBU) (>45 GWd/MTU) spent nuclear fuel (SNF) rods from the North Anna Nuclear Power Station operated by Dominion Energy. The SNF rods, called sister rods or sibling rods are all HBU and include four different kinds of fuel rod cladding: standard Zircaloy-4 (Zirc-4), low-tin (LT) Zirc-4, ZIRLO®, and M5®. Appendix B provides detailed information regarding defueling activities, metallographic imaging and measurements, and total cladding hydrogen measurements.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Characterization of Fuel and Cladding In and Near the Pellet-Pellet Gap of a High-Burnup Pressurized Water Reactor Fuel Rod

Oak Ridge National Laboratory (ORNL) is performing extensive destructive examinations of 15 high-burnup (HBU) spent nuclear fuel (SNF) rods from the North Anna Power Station (NAPS), which is operated by Dominion Energy Virginia [1]. The examinations are being conducted to obtain a baseline condition of the HBU rods before dry storage and are focused on understanding overall SNF rod strength and durability [2,3]. The HBU rods, referred to as sister rods or sibling rods, are similar to rods placed into dry storage at NAPS that are planned to be examined after one decade. The sister rods include several ZIRLO®-clad rods manufactured by Westinghouse Electric Company. One of the ZIRLO®-clad rods examined includes a pellet-pellet gap of 1 mm that was identified during the nondestructive examinations (NDEs) [4]. The rod was sectioned axially at that elevation to reveal the pellet-pellet interfaces and the pellet-pellet gap. The section was mounted and polished to reveal the distribution of hydride precipitates in the cladding above, below, and within the gap [5]. Total cladding hydrogen measurements will be performed to quantify the total cladding hydrogen through the gap and any additional in-solution or precipitated hydrogen in the pellet-pellet gap region

Montgomery, Rose↗