Engineering topics
Publications and source records attributed to Dolan, Connor J..
Phase stability and the optoelectronic performance of the metastable CsPbI 3 host can be improved with triple-halide alloying, without excessive Br addition which widens the gap beyond that ideal for tandem-photovoltaics.
We present a design strategy for fabricating ultrastable phase-pure films of formamidinium lead iodide (FAPbI 3 ) by lattice templating using specific two-dimensional (2D) perovskites with FA as the cage cation. When a pure FAPbI 3 precursor solution is brought in contact with the 2D perovskite, the black phase forms preferentially at 100°C, much lower than the standard FAPbI 3 annealing temperature of 150°C. X-ray diffraction and optical spectroscopy suggest that the resulting FAPbI 3 film compresses slightly to acquire the (011) interplanar distances of the 2D perovskite seed. The 2D-templated bulk FAPbI 3 films exhibited an efficiency of 24.1% in a p-i-n architecture with 0.5–square centimeter active area and an exceptional durability, retaining 97% of their initial efficiency after 1000 hours under 85°C and maximum power point tracking.
The light-emitting diodes (LEDs) used in indoor testing of perovskite solar cells do not expose them to the levels of ultraviolet (UV) radiation that they would receive in actual outdoor use. We report degradation mechanisms of p-i-n-structured perovskite solar cells under unfiltered sunlight and with LEDs. Weak chemical bonding between perovskites and polymer hole-transporting materials (HTMs) and transparent conducting oxides (TCOs) dominate the accelerated A-site cation migration, rather than direct degradation of HTMs. An aromatic phosphonic acid, [2-(9-ethyl-9H-carbazol-3-yl)ethyl]phosphonic acid (EtCz3EPA), enhanced bonding at the perovskite/HTM/TCO region with a phosphonic acid group bonded to TCOs and a nitrogen group interacting with lead in perovskites. A hybrid HTM of EtCz3EPA with strong hole-extraction polymers retained high efficiency and improved the UV stability of perovskite devices, and a champion perovskite minimodule-independently measured by the Perovskite PV Accelerator for Commercializing Technologies (PACT) center-retained operational efficiency of >16% after 29 weeks of outdoor testing.
Metal halide perovskites (MHPs) have a strong potential for optoelectronic applications, especially photovoltaics. A significant advantage offered by MHPs is their bandgap tunability via chemical substitution and alloying, with lead–tin alloys producing the narrowest reported bandgaps of ~1.2 eV. Efforts to further narrow the bandgap of MHPs by alloying in other elements, such as bismuth, have largely been unsuccessful due to the introduction of defective electronic states, which severely diminish electronic quality. Here, in this study, we examine the effects of bismuth on a lead–tin alloyed MHP, motivated by the narrow bandgap of alloyed lead–tin MHPs. We find that the defect screening observed in lead–tin MHPs is not sufficient to screen the defect level introduced by bismuth, as evidenced by quenched photoluminescence, decreased mobility, and severely reduced performance in a photovoltaic device. Density functional theory calculations suggest that midgap states are introduced by bismuth addition over a range of chemical and compositional conditions. We further observe through wavelength-dependent photoconductivity that free carriers are generated out to ~0.9 eV in bismuth-containing samples, which could be of potential interest for NIR photodetection.