Structure–Transport Properties Governing the Interplay in Humidity-Dependent Mixed Ionic and Electronic Conduction of Conjugated Polyelectrolytes

Polymeric mixed ionic-electronic conductors (MIECs) are of broad interest in the field of energy storage and conversion, opto-electronics, and bioelectronics. A class of polymeric MIECs are conjugated polyelectrolytes (CPEs), which possess a p-conjugated backbone imparting electronic transport characteristics along with side chains comprised of a pendant ionic group to allow for ionic transport. Here, our study focuses on the humidity-dependent structure-transport properties of poly[3-(potassium-n-alkanoate) thiophene-2,5-diyl] (P3KnT) CPEs with varied side-chain lengths of n = 4, 5, 6, and 7. UV-Vis spectroscopy along with electronic paramagnetic resonance (EPR) spectroscopy reveal the infiltration of water leads to a hydrated, self-doped state that allows for electronic transport. The resulting humidity-dependent ionic conductivity (σ i ) of the thin films shows a monotonic increase with relative humidity (RH) while electronic conductivity (σ e ) follows a nonmonotonic profile. The values of σ e continue to rise with increasing RH reaching a local maximum after which σ e begins to decrease. P3KnTs with higher n values demonstrate greater resiliency to increasing RH before suffering decrease in σ e . This drop in σ e is attributed to two factors. First, disruption of the locally-ordered π-stacked domains observed through in situ humidity-dependent grazing incidence wide angle X-ray scattering (GIWAXS) experiments can account for some of the decrease in σ e . A second and more dominant factor is attributed to the swelling of the amorphous domains where electronic transport pathways connecting ordered domains are impeded. P3K7T is most resilient to swelling (based on ellipsometry and water uptake measurements) where sufficient hydration allows for high σ i (1.0 × 10 -1 S/cm at 95% RH) while not substantially disrupting σ e (1.7 × 10 -2 S/cm at 85% RH and 8.0 × 10 -3 S/cm at 95% RH). Overall, our study highlights the complexity of balancing electronic and ionic transport in hydrated CPEs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Correlating conductivity and Seebeck coefficient to doping within crystalline and amorphous domains in poly(3-(methoxyethoxyethoxy)thiophene)

Molecular doping of conjugated polymers (CPs) plays a vital role in optimizing organic electronic and energy applications. For the case of organic thermoelectrics, it is commonly believed that doping CPs with a strong dopant could result in higher conductivity (σ) and thus better power factor (PF). Herein, by investigating thermoelectric performance of a polar side-chain bearing CP, poly(3- (methoxyethoxyethoxy)thiophene) (P3MEET), vapor doped with fluorinatedderivative of tetracyanoquinodimethane FnTCNQ (n = 1, 2, 4), we show that using strong dopants can in fact have detrimental effects on the thermoelectric performance of CPs. Despite possessing higher electron affinity, doping P3MEET with F4TCNQ only results in a σ (27.0 S/cm) comparable to samples doped with other two weaker dopants F2TCNQ and F1TCNQ (26.4 and 20.1 S/cm). Interestingly, F4TCNQ-doped samples display a marked reduction in the Seebeck coefficient (α) compared to F1TCNQ- and F2TCNQ-doped samples from 42 to 13 μV/ K, leading to an undesirable suppression of the PF. Additionally, structural characterizations coupled with Kang-Snyder modeling of the α–σ relation show that the reduction of α in F4TCNQ-doped P3MEET samples originates from the generation of low mobility carrier within P3MEET's amorphous domain. Our results demonstrate that factors such as dopant distribution and doping efficiency within the crystalline and amorphous domains of CPs should play a crucial role in advancing rational design for organic thermoelectrics.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Ionic Dopant-Induced Ordering Enhances the Thermoelectric Properties of a Polythiophene-Based Block Copolymer

Conjugated polymer-based block copolymers (CP-BCPs) are an unexplored class of materials for organic thermoelectrics. In this study, the authors report on the electronic conductivity (σ) and Seebeck coefficient (α) of a newly synthesized CP-BCP, poly(3-hexylthiophene)-block-poly (oligo-oxyethylene methacrylate) (P3HT-b-POEM), upon solution co-processing with lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), and subsequently vapor-doping with a molecular dopant, 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ). It is found that the addition of the hydrophilic block POEM greatly enhances the processability of P3HT, enabling homogeneous solution-mixing with LiTFSI. Notably, interactions between P3HT-b-POEM with ionic species significantly improve molecular order and unexpectedly cause electrical oxidizing doping of P3HT block both in solution and solid-states, a phenomenon that has not been previously observed in Li-salt containing P3HT. Vapor doping of P3HT-b-POEM-LiTFSI thin films with F4TCNQ further enhances σ and yields a thermoelectric power factor PF = α 2 σ of 13.0 μW m -1 K -2 , which is more than 20 times higher than salt-free P3HT-b-POEM sample. Through modeling thermoelectric behaviors of P3HT-b-POEM with the Kang-Snyder transport model, the improvement in PF is attributed to higher electronic charge mobility originating from the enhanced molecular ordering of P3HT. The results demonstrate that solution co-processing CP-BCPs with a salt is a powerful method to control structure and performance of organic thermoelectric materials.