Fatigue Life of a NiCr-Coated Powder Metallurgy Disk Superalloy After Varied Processing and Exposures
No abstract available
Gabb, Tim P.↗
Engineering topics
Draper, S. L.
Publications and source records attributed to Draper, S. L..
Cyclic Oxidation and Hot Corrosion of NiCrY-Coated Disk Superalloy
Powder metallurgy disk superalloys have been designed for higher engine operating temperatures through improvement of their strength and creep resistance. Yet, increasing disk application temperatures to 704 C and higher could enhance oxidation and activate hot corrosion in harmful environments. Protective coatings could be necessary to mitigate such attack. Cylindrical coated specimens of disk superalloys LSHR and ME3 were subjected to thermal cycling to produce cyclic oxidation in air at a maximum temperature of 760 C. The effects of substrate roughness and coating thickness on coating integrity after cyclic oxidation were considered. Selected coated samples that had cyclic oxidation were then subjected to accelerated hot corrosion tests. The effects of this cyclic oxidation on resistance to subsequent hot corrosion attack were examined.
Hot corrosion↗
Effects of Long Term Exposures on PM Disk Superalloys
Turbine disks in some advanced engine applications may be exposed to temperatures above 700 C for extended periods of time, approaching 1,000 h. These exposures could affect the near-surface composition and microstructure through formation of damaged and often embrittled layers. The creation of such damaged layers could significantly affect local mechanical properties. Powder metal disk superalloys LSHR and ME3 were exposed at temperatures of 704, 760, and 815 C for times up to 2,020 h, and the types and depths of environmental attacked were measured. Fatigue tests were performed for selected cases at 704 and 760 C, to determine the impact of these exposures on fatigue life. Fatigue resistance was reduced up to 98% in both superalloys for some exposure conditions. Tensile tests were also performed to help understand fatigue responses, and showed corresponding reductions in ductility. The changes in surface composition and phases, depths of these changed layers, failure responses, and failure initiation modes were compared.
Heat resistant allos↗
Development and Evaluation of TiAl Sheet Structures for Hypersonic Applications
A cooperative program between the National Aeronautics and Space Administration (NASA), the Austrian Space Agency (ASA), Pratt & Whitney, Engineering Evaluation and Design, and Plansee AG was undertaken to determine the feasibility of achieving significant weight reduction of hypersonic propulsion system structures through the utilization of TiAl. A trade study defined the weight reduction potential of TiAl technologies as 25 to 35 percent compared to the baseline Ni-base superalloy for a stiffener structure in an inlet, combustor, and nozzle section of a hypersonic scramjet engine (ref. 1). A scramjet engine inlet cowl flap was designed, along with a representative subelement, using design practices unique to TiAl. A sub-element was fabricated and tested to assess fabricability and structural performance and validate the design system. The TiAl alloy selected was Plansee's third generation alloy Gamma Met PX (Plansee AG ), a high temperature, high strength gamma-TiAl alloy with high Nb content (refs. 2 and 3). Characterization of Gamma Met PX sheet, including tensile, creep, and fatigue testing was performed. Additionally, design-specific coupons were fabricated and tested in order to improve subelement test predictions. Based on the sheet characterization and results of the coupon tests, the subelement failure location and failure load were accurately predicted.
Draper, S. L.↗
Effect of Exposure on the Mechanical Properties of Gamma MET PX
The effect of a service environment exposure on the mechanical properties of a high Nb content TiAl alloy, Gamma MET PX , was assessed. Gamma MET PX, like other TiAl alloys, experiences a reduction of ductility following high temperature exposure. Exposure in Ar, air, and high-purity oxygen all resulted in a loss of ductility with the ductility reduction increasing with oxygen content in the exposure atmosphere. Embrittling mechanisms, including bulk microstructural changes, moisture induced environmental embrittlement, and near surface effects were investigated. The embrittlement has been shown to be a near-surface effect, most likely due to the diffusion of oxygen into the alloy.
Draper, S. L.↗
Microstructure and Mechanical Properties of Extruded Gamma Met PX
A gamma TiAl alloy with a high Nb content is being assessed as a compressor blade material. The microstructure and mechanical properties of extruded Ti-45Al-X(Nb,B,C) (at %) were evaluated in both an as-extruded condition and after a lamellar heat treatment. Tensile behavior of both as-extruded and lamellar heat treated specimens was studied in the temperature range of RT to 926 C. In general, the yield stress and ultimate tensile strength reached relatively high values at room temperature and decreased with increasing deformation temperature. The fatigue strength of both microstructures was characterized at 650 C and compared to a baseline TiAl alloy and to a Ni-base superalloy. Tensile and fatigue specimens were also exposed to 800 C for 200 h in air to evaluate the alloy's environmental resistance. A decrease in ductility was observed at room temperature due to the 800 C exposure but the 650 C fatigue properties were unaffected. Compressive and tensile creep testing between 727 and 1027 C revealed that the creep deformation was reproducible and predictable. Creep strengths reached superalloy-like levels at fast strain rates and lower temperatures but deformation at slower strain rates and/or higher temperature indicated significant weakening for the as-extruded condition. At high temperatures and low stresses, the lamellar microstructure had improved creep properties when compared to the as-extruded material. Microstructural evolution during heat treatment, identification of various phases, and the effect of microstructure on the tensile, fatigue, and creep behaviors is discussed.
Draper, S. L.↗
Microstructure and Mechanical Properties of Extruded Gamma Microstructure Met PX
A gamma TiAl alloy with a high Nb content is being assessed as a compressor blade material. The microstructure and mechanical properties of extruded Ti-45Al-X(Nb,B,C) (at.%) were evaluated in both an as-extruded condition and after a lamellar heat treatment. Tensile behavior of both as-extruded and lamellar heat treated specimens was studied in the temperature range of RT to 926 C. In general, the yield stress and ultimate tensile strength reached relatively high values at room temperature and decreased with increasing deformation temperature. The fatigue strength of both microstructures was characterized at 650 C and compared to a baseline TiAl alloy and to a Ni-base superalloy. Tensile and fatigue specimens were also exposed to 800 C for 200 h in air to evaluate the alloy's environmental resistance. A decrease in ductility was observed at room temperature due to the 800 C. exposure but the 650 C fatigue properties were unaffected. Compressive and tensile creep testing between 727 and 1027 C revealed that the creep deformation was reproducible and predictable. Creep strengths reached superalloy-like levels at fast strain rates and lower temperatures but deformation at slower strain rates and/or higher temperature indicated significant weakening for the as-extruded condition. At high temperatures and low stresses, the lamellar microstructure had improved creep properties when compared to the as-extruded material. Microstructural evolution during heat treatment, identification of various phases, and the effect of microstructure on the tensile, fatigue, and creep behaviors is discussed.
Draper, S. L.↗
Effect of Impact Damage on the Fatigue Response of TiAl Alloy-ABB-2
The ability of gamma-TiAl to withstand potential foreign or domestic object damage is a technical risk to the implementation of gamma-TiAl in low pressure turbine (LPT) blade applications. In the present study, the impact resistance of TiAl alloy ABB-2 was determined and compared to the impact resistance of Ti(48)Al(2)Nb(2)Cr. Specimens were impacted with four different impact conditions with impact energies ranging from 0.22 to 6.09 J. After impacting, the impact damage was characterized by crack lengths on both the front and backside of the impact. Due to the flat nature of gamma-TiAl's S-N (stress vs. cycles to failure) curve, step fatigue tests were used to determine the fatigue strength after impacting. Impact damage increased with increasing impact energy and led to a reduction in the fatigue strength of the alloy. For similar crack lengths, the fatigue strength of impacted ABB-2 was similar to the fatigue strength of impacted Ti(48)Al(2)Nb(2)Cr, even though the tensile properties of the two alloys are significantly different. Similar to Ti(48)Al(2)Nb(2)Cr, ABB-2 showed a classical mean stress dependence on fatigue strength. The fatigue strength of impacted ABB-2 could be accurately predicted using a threshold analysis.
Draper, S. L.↗
The Effect of Ballistic Impacts on the High Cycle Fatigue Properties of Ti-48Al-2Nb-2Cr (at.%)
The ability of gamma - TiAl to withstand potential foreign and/or domestic object damage is a technical risk to the implementation of gamma - TiAl in low pressure turbine (LPT) blade applications. The overall purpose of the present study was to determine the influence of ballistic impact damage on the high cycle fatigue strength of gamma - TiAl simulated LPT blades. Impact and specimen variables included ballistic impact energy, projectile hardness, impact temperature, impact location, and leading edge thickness. The level of damage induced by the ballistic impacting was studied and quantified on both the impact (front) and backside of the specimens. Multiple linear regression was used to model the cracking and fatigue response as a function of the impact variables. Of the impact variables studied, impact energy had the largest influence on the response of gamma - TiAl to ballistic impacting. Backside crack length was the best predictor of remnant fatigue strength for low energy impacts (<0.74J) whereas Hertzian crack length (impact side damage) was the best predictor for higher energy impacts. The impacted gamma - TiAl samples displayed a classical mean stress dependence on the fatigue strength. For the fatigue design stresses of a 6th stage LPT blade in a GE90 engine, a Ti-48Al-2Nb-2Cr LPT blade would survive an impact of normal service conditions.
Draper, S. L.↗
Tensile Behavior of Al2o3/feal + B and Al2o3/fecraly Composites
The feasibility of Al2O3/FeAl + B and Al2O3/FeCrAlY composites for high-temperature applications was assessed. The major emphasis was on tensile behavior of both the monolithics and composites from 298 to 1100 K. However, the study also included determining the chemical compatibility of the composites, measuring the interfacial shear strengths, and investigating the effect of processing on the strength of the single-crystal Al2O3 fibers. The interfacial shear strengths were low for Al203/FeAl + B and moderate to high for Al203/FeCrAlY. The difference in interfacial bond strengths between the two systems affected the tensile behavior of the composites. The strength of the Al203 fiber was significantly degraded after composite processing for both composite systems and resulted in poor composite tensile properties. The ultimate tensile strength (UTS) values of the composites could generally be predicted with either rule of mixtures (ROM) calculations or existing models when using the strength of the etched-out fiber. The Al2O3/FeAl + B composite system was determined to be unfeasible due to poor interfacial shear strengths and a large mismatch in coefficient of thermal expansion (CTE). Development of the Al2O3/FeCrAlY system would require an effective diffusion barrier to minimize the fiber strength degradation during processing and elevated temperature service.
Draper, S. L.↗
Al2O3 fiber strength degradation in metal and intermetallic matrix composites
The mechanisms for fiber damage in single crystal Al2O3 fiber-reinforced composites were investigated. Both fiber fragmentation and fiber strength degradation were observed in composites with a variety of matrix compositions. Four mechanisms that may be contributing to the fiber strength loss have been proposed and include matrix reaction, reaction with binders, residual stress-induced damage, and pressure from hot pressing. The effect of matrix reaction was separated from the other three effects by sputter-coating the matrices on cleaned fibers and annealing with a temperature profile that simulates processing conditions. These experiments revealed that Y and Cr in FeCrAlY base alloys and Zr in NiAl alloys reacted with the fiber, and grooves and adherent particles were formed on the fiber surface which were responsible for the strength loss. The effects of the matrix reaction appeared to dominate over the other possible mechanisms, although evidence for reaction with binders was also found. Ridges on the fiber surface, which reflected the grain boundaries of the matrix, were also observed. In order for single-crystal Al2O3 to be used as a fiber in MMC's and IMC's, a matrix or protective coating which minimizes matrix reaction during processing will be necessary. Of the matrices investigated, the Thermo-span(sup TM) alloy was the least damaging to fiber properties.
ALUMINA/IRON CHROMIUM ALUMINUM↗
The effect of temperature on the deformation and fracture of SiC/Ti-24Al-11Nb
The effect of temperature on the stress-strain behavior in air and the failure mechanisms of Ti-24Al-11Nb alloy and of a SiC/Ti-24Al-11Nb composite with continuous SiC fibers oriented parallel to the loading direction was investigated over temperature range 23-815 C. It was found that the tensile failure process of SiC/Ti-24Al-11Nb was controlled at all temperatures by fiber fracture. Composite failure occurred at 0.8 percent strain at all temperatures. Debond and frictional stresses at the fiber-matrix interface decreased with increased temperature.
Brindley, P. K.↗
Effect of Fiber Strength on the Room Temperature Tensile Properties of Sic/Ti-24Al-11Nb
SCA-6 SiC fibers of known strength were incorporated into SiC/Ti-24Al-11Nb (at. percent) composites and the effect of fiber strength variability on room temperature composite strength was investigated. Fiber was etched out of a composite fabricated by the powder cloth technique and the effect of the fabrication process on fiber strength was assessed. The strength of the composite was directly correlated with the strength of the as-received fiber. The strength of composite plates containing mixed fiber strengths was dominated by the lower strength fiber. Fabrication by the powder cloth technique resulted in only a slight degradation of fiber strength. The strength of the composite was found to be overestimated by the rule of mixtures strength calculation. Examination of failed tensile specimens revealed periodic fiber cracks and the failure mode was concluded to be cumulative. With the variation in fiber strength eliminated, the composite UTS was found to have a positive correlation with volume fraction of fiber.
Draper, S. L.↗
Compatibility of Fe-40Al with various fibers
Chemical reaction can occur at the fiber/matrix interface of intermetallic matrix composites, leading to a degradation of mechanical properties. Fe-40Al matrix composites were fabricated using SiC, B, W, Mo-base, and Al2O3 fibers. Composite samples were heat treated up to 1500 K to study the reaction kinetics, and reaction rates were determined from reaction zone thickness measurements. The Al2O3 and W fibers were found to be compatible with the Fe-40Al matrix, while the Mo-based fibers reacted moderately and the B and SiC fibers reacted severely. Experimental results are compared to theoretical thermodynamic predictions.
Draper, S. L.↗
Factors which influence tensile strength of a SiC/Ti-24Al-11Nb (at. pct) composite
Tensile and fiber pullout tests were used in conjunction with SEM to investigate structural and processing effects on SiC fiber, a neat Ti-24Al-11Nb matrix alloy, and a composite fabricated from the two. The effects of oxygen content, fiber spacing, fiber volume fraction, fiber-matrix reaction thickness, Teflon content, and matrix powder size, appear to be smaller than the effects of variability in fiber strength. Fiber spacing did not influence radial crack formation, interfacial bond shear strength, or stress-strain behavior in the composite. The temperature dependence of composite properties was investigated over the 23-815 C range.
Brindley, P. K.↗
Microstructure and tensile properties of Fe-40 at. pct Al alloys with C, Zr, Hf, and B additions
The influence of small additions of C, Zr, and Hf, alone or in combination with B, on the microstructure and tensile behavior of substoichiometric FeAl was investigated. Tensile properties were determined from 300 to 1100 K on powder which was consolidated by hot extrusion. All materials possessed some ductility at room temperature, although ternary additions generally reduced ductility compared to the binary alloy. Adding B to the C- and Zr-containing alloys changed the fracture mode from intergranular to transgranular and restored the ductility to approximately 5 percent elongation. Additions of Zr and Hf increased strength up to about 900 K. Fe6Al6Zr and Fe6Al6Hf precipitates, both with identical body-centered tetragonal structures, were identified as the principal second phase in these alloys. Strength decreased steadily as temperature increased above 700 K, as diffusion-assisted mechanisms became operative. Although all alloys had similar strengths at 1100 K, Hf additions significantly improved high-temperature ductility by suppressing cavitation.
Gaydosh, D. J.↗
The role of interfacial dislocation networks in high temperature creep of superalloys
The dislocation networks generated during high-temperature creep of several single-crystal nickel-based superalloys are analyzed. The networks continually evolve during creep at relatively low temperatures or eventually reach a more stable configuration at high temperatures. Specifically, the role of these networks in directional coarsening processes are studied, along with their formation kinetics, characteristics, and stability during creep. The results of this study combined with previous findings suggest that the directional coarsening process is strongly influenced by elastic strain energy. The dislocation networks formed during primary creep are found to be stable during all subsequent creep stages. Aspects of these dislocation networks are determined to be a product of both the applied creep stress and coherency strains.
Gabb, T. P.↗
Effect of Ga and P dopants on the thermoelectric properties of n-type SiGe
The purpose of this study was to hot-press improved n-type Si80Ge20/GaP samples directly (without any heat treatment) and to confirm that a Ga/P ratio less than one increases the solubility of P and, hence, improves the power factor and Z. One of the three samples (Ga/P = 0.43) had an improvement in Z of about 20 percent between 400 and 1000 C over that for standard SiGe. This demonstrates that improved samples can be pressed directly and that a Ga/P ratio less than one is necessary. The other two samples (Ga/P = 0.33 and 0.50) had Z's equal to or less than that of standard SiGe but had a lower hot-pressing temperature than the improved sample.
Draper, S. L.↗