NASA NTRS1984

Kinetics of crystal nucleation and growth in Pd(40)Ni(40)P(20) glass

Samples of Pd(40)Ni(40)P(20) glass, produced by cooling the melt at 1 or 800 K/s, are heated in a differential scanning calorimeter to determine the crystallization kinetics. Optical microscopy shows that eutectic crystallization proceeds both by growth from the surface of the samples and by the growth of spherical regions around preexisting nuclei in the interior. A modified Kissinger (1957) analysis is used to obtain the activation energy for crystal growth (3.49 eV). The steady state homogeneous nucleation frequency at 590 K is about 10 million/cu m per sec. This is estimated to be the maximum nucleation frequency: it is too low to account for the observed population of quenched-in nuclei, which are therefore presumed to be heterogeneous. The major practical obstacle to glass formation in this system is heterogeneous nucleation.

Drehman, A. J.↗

NASA NTRS1982

Bulk formation of a metallic glass - Pd40Ni40P20

Molten spheroids of Pd40Ni40P20, of up to 0.53-cm minor diameter, were slowly cooled (1.4 K/s) on a fused silica surface under 10 to the -6 torr vacuum to a form which was entirely glassy except for some superficial crystallinity comprising less than 0.5% of the volume. The occurrence of crystallization was eliminated by subjecting the specimens to surface etching followed by a succession of heating and cooling cycles. The absence of crystallization in bulk was confirmed by X-ray diffraction, transmission electron microscopy, and calorimetry. Using the last technique, the heat of crystallization of the glass was measured to be 5.3 + or - 0.3 kJ/g atom.

Drehman, A. J.↗

NASA NTRS1982

Crystal nucleation in Pd-Si alloys

A study of the crystal phase nucleation in undercooled droplets of Pd-Si alloys with composition near the Pd(84.5)Si(15.5) eutectic composition is reported. Molten droplets are released at the top of a drop tube and solidify (to either a crystalline or glassy state) during descent. This provides a containerless (and nearly gravity free) environment so that nucleation due to container walls or vibrations is eliminated. It is found that crystallization, due to homogeneous nucleation, is bypassed in droplets of 1 mm diameter when cooled at 760 K/sec. From this an upper limit of the homogeneous nucleation rate is estimated. Results are compared with a previously published study of nucleation in 0.06 mm to 0.33 mm diameter droplets, which indicated that nucleation results from heterogeneous surface nucleation and that the number of these nuclei is dependent on the atmosphere in the drop tube.

Drehman, A. J.↗