Engineering topics
Publications and source records attributed to Drennan, D. N..
Addition of silica fibers greatly reduces shrinkage and cracking during casting of ceramics. Fiber-reinforced slip-cast silica ceramics are also tougher and have lower dielectric loss. Silica fibers are hyperpure material containing only 1 part per million total metal-ion impurities. Hyperpure fibers ensure high reflectance and allow casting to be fired at temperature greater than 2,200 degrees F without loss of strength from devitrification.
High purity three dimensionally woven silica-silica materials were evaluated for use as a tough reflective heat shield for planetary entry probes. A special weave design was selected to minimize light piping effects through the heat shield thickness. Various weave spacings were evaluated for densification efficiency with an 0.7 micron particle size high purity silica. Spectral hemispherical reflectance was measured from 0.2 to 2.5 microns at room temperature. Reflectance increases due to densification and purity of material were measured. Reflectance of 3D hyperpure silica was higher than 3D astroquartz silica for all wavelengths. Mechanical properties were measured in beam flexure and beam shear tests. Results indicated strengths lower than reported for slip cast fused silica. Low strengths were attributed to low densities achieved through vacuum impregnation.
A highly reflective hyperpure ( 25 ppm ion impurities) slip cast fused silica heat shield material developed for planetary entry probes was successfully scaled up. Process development activities for slip casting large parts included green strength improvements, casting slip preparation, aggregate casting, strength, reflectance, and subscale fabrication. Successful fabrication of a one-half scale Saturn probe (shape and size) heat shield was accomplished while maintaining the silica high purity and reflectance through the scale-up process. However, stress analysis of this original aggregate slip cast material indicated a small margin of safety (MS. = +4%) using a factor of safety of 1.25. An alternate hyperpure material formulation to increase the strength and toughness for a greater safety margin was evaluated. The alternate material incorporates short hyperpure silica fibers into the casting slip. The best formulation evaluated has a 50% by weight fiber addition resulting in an 80% increase in flexural strength and a 170% increase in toughness over the original aggregate slip cast materials with comparable reflectance.
A high purity slip cast silica material has been developed for use as a reflective heat shield for entries into the atmospheres of the outer planets. The several stages leading to the development of this material are described and details of raw material selection, preparation of the slip material and casting techniques are discussed. Optical (reflectance and transmittance), physical and chemical properties measurements were performed as a function of the important material and processing variables. Performance analysis of a reflective heat shield fabricated from the high purity silica slip shows that approximately 90 percent of the radiant bow shock energy incident on the heat shield during entry into the atmosphere of Jupiter will be reflected.
Measurements were made of reflectance in the vacuum ultraviolet down to 0.15 micron. Scattering coefficients (S) and absorption coefficients (K) were also measured. These coefficients express the optical properties and are used directly in a thermodynamic analysis for sizing a heat shield. The effect of the thin silica melt layer formed during entry was also studied from the standpoint of trapped radiant energy.