NASA NTRS1981

Optically induced bistable states in metal/tunnel-oxide/semiconductor /MTOS/ junctions

A new switching phenomenon in metal-oxide semiconductor tunnel junction has been discovered. With a sufficiently large negative bias applied to the electrode, incident visible light of intensity greater than about 1 microW/sq cm causes the reverse-biased junction to switch from a low-current to a high-current state. It is believed that hot-electron-induced impact ionization provides the positive feedback necessary for switching, and causes the junction to remain in its high-current state after the optical excitation is removed. The junction may be switched back to the low-current state electrically. The basic junction characteristics have been measured, and a simple model for the switching phenomenon has been developed.

Lai, S. K.↗

NASA NTRS1980

Photoemission measurements of interface barrier energies for tunnel oxides on silicon

Internal photoemission measurements of the Si/SiO2 and Al/SiO2 barrier heights on oxides of tunneling thickness (43-56 A) are compared with measurements on thick oxides (310 A and greater) and the barrier heights are found to be the same. The results suggest that substantially thinner oxides, grown by the same method, can be characterized by the same barrier heights. Limits to the experimental technique posed by photovoltaic and displacement currents, and transport of hot carriers in the tunnel oxide are discussed.

Dressendorfer, P. V.↗

NASA NTRS1980

Processing dependence of metal/tunnel-oxide/silicon junctions

The effects of process variations on the fixed-charge density, interface-state density, and tunneling properties of tunnel oxides on (100) silicon are discussed. Annealing the oxide in nitrogen reduces the fixed-charge and interface-state densities substantially, but also causes a marked increase in oxide capacitance. Anneals in forming gas before metallization alter the interface-state distribution and decrease the insulating qualities of the tunneling oxides. Postmetallization anneals in forming gas reduce the interface-state density to 1 x 10 to the 11th e/sq cm V or below, and appear not to affect the current through the oxide. No evidence for metal-induced interface states is observed.

Dressendorfer, P. V.↗