Search NASA⌕ Search

Engineering topics

Drewry, Sean Michael

Publications and source records attributed to Drewry, Sean Michael.

Performance and properties evolution of near-term accident tolerant fuel: Cr-doped UO 2

Chromium-doped UO 2 fuel has received significant interest due to the ability for chromium to produce pellets with large average grain size (>30 μm), which has shown to increase fission gas retention during operation. Sintering of chromium-doped UO 2 pellets was pursued with oxygen potential and sintering atmosphere controlled to tailor the final microstructure of the material. Chromium additions in this study ranged from 750 to 7800 ppm. Cr concentrations were studied pre and post sintering using Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES). Effects of chromium content on lattice parameter and microstructure were examined with X-ray diffraction (XRD) and scanning electron microscopy (SEM). Contraction of the UO 2 lattice parameter was observed, as well as enlargement of grain size with increasing chromium content up to 4900 ppm Cr 2 O 3 . In addition, SEM indicated Cr incorporation within the matrix and the formation of chromium oxide precipitates throughout the microstructure at high Cr concentrations. Evaluation of thermophysical properties of Cr-doped UO 2 pellets were conducted up to 1200 °C to illustrate their evolution with increased dopant concentration and microstructural changes. The results show that grain size is maximized at 52 μm with Cr 2 O 3 concentration equal to 4900 ppm; however, grain size decreases at higher Cr 2 O 3 concentrations. No significant changes were observed in specific heat capacity, linear thermal expansion, and coefficient of thermal expansion compared to undoped UO 2 . The thermal conductivity also decreased through the incorporation of Cr 2 O 3 dopants above 750 ppm and is shown to be ~15 % lower than reported UO 2 values.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Accelerated radiation tolerance testing of Ti-based MAX phases

MAX phases have recently attracted significant attention for potential nuclear applications due to their novel properties such as unique hexagonal-compact nanolayered crystal structure, high-machinability due to lower hardness levels compared to conventional ceramics, and high-chemical inertness. In order for MAX phases to be used in nuclear reactors, two aspects deserve detailed investigations: (i) their phase stability at high-temperatures and (ii) microstructural defect formation and recovery induced by energetic particle irradiation. To date, degradation mechanisms of MAX phases at high-temperatures and following irradiation are largely unexplored fields of research. This work focuses on the evaluation of two Ti-based MAX phases – Ti 2 AlC and Ti 3 SiC 2 – within the context of extreme environments. To accomplish this, a one-of-a-kind comparison between neutron irradiations, performed over a decade of research at the High Flux Isotope Reactor (HFIR), and heavy-ion irradiations, carried out in situ in a Transmission Electron Microscope (TEM) at the MIAMI-2 facility, has been conducted. The results show Ti-based MAX phases are prone to accelerated decomposition under the conditions investigated. This questions the hypothesis that MAX phases exhibit high phase stability, especially when used in future nuclear energy systems where energetic particle irradiation is a dominating degradation mechanism.

36 MATERIALS SCIENCE↗