Engineering topics
Dubey, Pawan Kumar
Publications and source records attributed to Dubey, Pawan Kumar.
Hydroxide melt induced corrosion of Ni at elevated temperatures under steam electrolysis conditions
Molten alkali electrolyte based high temperature water electrolysis (HTWE) process offers an efficient pathway to integrate renewable energy resources for large scale and economic hydrogen production. Long term and stable operation of these systems require an in-depth understanding of materials stability under anodic and cathodic exposure conditions of the cell and cell stacks. In the present study, we report our findings on the corrosion of Ni in the presence and absence of (LieNa) hydroxide melt at 600 °C under oxidizing and reducing conditions representative of HTWE. While the Ni electrode was found to remain thermodynamically stable in metallic form under cathodic (reducing) exposure conditions, the corrosion rate in molten hydroxide under oxidizing conditions was found to be nonparabolic in nature. A cyclic voltammetry study provides the breakdown of the passive metal-oxide surface layer at the anodic overpotential region between 0.45 V and 2 V in molten hydroxide under oxidizing conditions. As a result, a thermochemical process for accelerated corrosion based on the oxide scale fluxing in hydroxide melt has been developed.
Sulfur Poisoning and Performance Recovery of SOFC Air Electrodes
The sulfur poisoning and performance recovery of the state-of-the-art SOFC cathodes (La 0 . 80 Sr 0 . 20 ) 0 . 95 MnO 3 ± δ (LSM) and (La 0 . 60 Sr 0 . 40 ) 0 . 95 Co 0 . 20 Fe 0 . 80 O 3 – δ (LSCF), have been studied. Electrochemical impedance spectroscopy measurements of LSCF|GDC and LSM|YSZ half-cells are carried out in alternating atmospheres of air and SO 2 –air at 700°C for hundreds of hours. In the presence of SO 2 , the electrochemical performance of both the cells decays with ohmic and non-ohmic losses, owing to the absorption and chemical interaction of SO 2 with the electrodes. In LSCF, the SrO segregated on the surface tends to absorb and react with SO 2 , forming SrSO 4 followed by the exsolution of Co-Fe. As for LSM, SO 2 is absorbed onto the Sr-rich areas of LSM, including the active reaction sites near the TPBs, leading to Sr exsolution and SrSO 4 formation, leaving a Sr-deficient LSM. During the subsequent exposure to air, the performance of the sulfur-contaminated LSM is almost restored. The LSM particles, exposed to alternating atmospheres of air and SO 2 -air during the electrochemical tests, show a relatively clean surface with sparsely distributed SrSO 4 particles, indicating a high stability against sulfur poisoning. It is suggested that the loosely adsorbed SO 2 at the TPBs is readily swept away by the SO 2 -free air flow, recovering its ORR activity, whereas the Sr-deficient LSM due to Sr-exsolution stays modified, contributing to the incomplete performance restoration. Unlike the case of LSM, the performance of the sulfur-poisoned LSCF partially recovers during the subsequent exposure to air. Correspondingly, the LSCF particles have a modified morphology covered with numerous nanoparticles, mostly SrSO 4 , showing the irreversible aspect of the sulfur poisoning. The morphology modification is not concentrated near the electrode/electrolyte interface but over the entire cathode, indicating that the degree of recovery from sulfur poisoning is closely related to the presence of SrO and chemical activity of Sr in the electrodes at the solid-gas interface. These results also show the potential application of LSM for a sulfur sensor available in high-temperature harsh conditions.
Corrosion of AISI 310 and 316 in Molten Hydroxide Under Steam Electrolysis Conditions
Steam electrolyzers, utilizing molten hydroxide electrolyte, offers potential for improvement in electrochemical efficiency, cost reduction, use of conventional materials of construction and process scale up for large scale hydrogen production. Stainless steels, used for the fabrication of cell components (current collector, gas separator, wet seals, and manifolds) experience accelerated corrosion in the presence of molten hydroxide electrolyte in both oxidizing (anodic) and reducing (cathodic) atmospheres. In this study, the corrosion behavior of AISI 310 and 316 in hydroxide melt has been studied at 600°C for 50 h. Melt immersion tests revealed formation of the porous lithium iron oxide at the melt-oxide interface for both AISI 310 and 316. Inductively coupled plasma optical emission spectrometry (ICP-OES) analysis showed the presence of Cr in the electrolyte melt obtained from samples exposed to oxidizing atmosphere. Thermochemical analysis was performed to validate the experimental results.
Stability of ceramic matrix materials in molten hydroxide under oxidizing and reducing conditions
The degradation mechanism of ceramic matrix materials used as molten hydroxide electrolyte support for steam electrolysis cells, is not well documented. In this study, we have investigated the structural and chemical stability of non-oxide and oxide ceramics (SiC, YSZ, Li 2 ZrO 3, LiAlO 2 , and SrZrO 3 ) in the presence of molten hydroxide under oxidizing and reducing conditions with humidity levels of 3 and 85% at 550 °C. SiC, YSZ, Li 2 ZrO 3 and LiAlO 2 showed structural and chemical changes due to dissolution of the ceramic particles in the hydroxide melt followed by precipitation. The SrZrO 3 powder, on the other hand, remained both chemically and structurally stable during 500 h test under both oxidizing and reducing atmospheres. The findings of a stable ceramic matrix in molten hydroxide contribute to the enhancement of the durability and performance of intermediate temperature water electrolysis system.